Characterization and Radiation Resistance of a Mixed-Alkali Borosilicate Glass for High-Level Waste Vitrification

Published online by Cambridge University Press:  10 February 2011

J.M. Roderick ,
D. Holland  and
C.R. Scales
J.M. Roderick
Affiliation:
Physics Department, Warwick University, Coventry, CV4 7AL, UK, [email protected]
D. Holland
Affiliation:
Physics Department, Warwick University, Coventry, CV4 7AL, UK, [email protected]
C.R. Scales
Affiliation:
British Nuclear Fuels Ltd, Sellafield, Seascale, Cumbria, UK
Get access

Abstract

Glasses related to those used for the vitrification of high-level waste (HLW) have been produced from the sodium-lithium borosilicate system. Their thermal and structural characteristics have been measured for a wide range of boron oxide contents (NBS series) and for a range of alkali oxide to boron oxide ratios, R, for several fixed silica to boron oxide ratios, K (ABS series). The NBS series of glasses was seen to exhibit a maximum in the glass transition temperature, Tg, and a minimum in the fraction of 4-coordinated borons, N4, at 22 mol% and 29 mol% boron oxide, respectively. With variation of K and R, initial results indicate an increase in Tg to a maximum before a gradual decrease. Density measurements show a general increase before remaining within experimental error at larger R. Initial α-particle irradiation tests have been carried out on several base glass samples and show evidence of B(α,n) reactions, the occurrence of which could have important consequences for the future viability of wasteforms designed for reprocessing of higher burn-up fuel.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 608: Symposium QQ – Scientific Basis for Nuclear Waste Management XXIII , 1999 , 721
Copyright
Copyright © Materials Research Society 2000

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1 &, G.J.H. Jacobs Liskien, H., Ann. Nuci. Energy 10 No.10 (1983), 541.Google Scholar
2 Snyder, W.S. and Neufeld, J., Physical Review 97 No.6 (1955), 1636.Google Scholar
3 Ewing, R.C. and Weber, W.J., J. Mater. Res. 12 No.8 (1997), 1946.Google Scholar
4 Boekenhauer, R. et al. , J. Non-Cryst. Solids 175 (1994), 137.Google Scholar
5 Dell, W.J. & Bray, P.J., J. Non-Cryst. Solids 58 (1983) 1.Google Scholar
6 Brungs, M.P. and McCartney, E.R., Phys. Chem. Glasses 16 (1975), 48.Google Scholar
7 Xhong, J. and Wu, X., J. Non-Cryst. Solids 107 (1988), 81.Google Scholar
8 Roderick, J.M., Holland, D. and Scales, C.R., Proceedings of the Third Conference on Borate Glasses, Crystals and Melts, Phys. Chem. Glasses, in press.Google Scholar
9 Tang, Y. & Jiang, Z., J. Non-Cryst Solids 189 (1995), 251.Google Scholar
10 Budhwani, K. & Feller, S., Phys. Chem. Glasses 36 No.4 (1975), 183.Google Scholar
11 Mazurin, O.V., Streltsina, M.V. & Totesh, A.S., Phys. Chem. Glasses 10 No.2 (1969), 63.Google Scholar