One of the newer tendencies in materials science has been to tailor-make classical products (long associated with old applications) with controlled properties for special uses, especially in high technology. Preparing dispersed systems in which all particles have nearly uniform size (monodisperse solids) is a typical example. This goal can be achieved in some cases through cleverly controlled particle growth from a liquid medium. Examples of such preparations include gold colloids prepared by Zsigmondy and later by Turkevich et al., sulfur sols obtained by LaMer, metal oxides and hydrous oxides prepared by Matijević et al., silica, etc. These dispersions have been used either to check theories of colloid science, or to a lesser extent, for industrial purposes. In the case of fine metal particles, a uniform size distribution associated with a low degree of agglomeration, and sometimes the spherical shape, appear as particularly convenient characteristics for certain applications. The production of conductive inks or pastes for electronic materials and for the preparation of conductive paints are particularly good examples.

In so-called thick film technology, conductive inks and pastes are screen printed on a ceramic substrate in order to form, after firing, a conductive film with a thickness less than 10 μm. This technique is, for instance, used to form the network in hybrid integrated circuits or the internal electrodes of multilayer ceramic capacitors.

Metallic powders in thick film compositions are usually precious metals (Au, Ag, Pt, Pd), their mixtures, or alloys. Cheaper metals such as copper or nickel are tested and may be potential substitutes for precious metals in different specific applications. Powders for thick film composition are mainly obtained through chemical precipitation from aqueous or organic solutions, which yield high purity powders. Modification of precipitation parameters (such as the nature and the concentration of the starting metallic compound and of the reducing agent, reaction temperature, viscosity of the medium) and the addition of additives and surfactants, can often be used to control particle size and agglomeration.

Over the past few years, we have developed a new process for preparing finely divided metal powders of easily reducible metals (such as precious metals and copper) or less reducible metals (such as cobalt, nickel, cadmium, or lead) by precipitation in liquid polyols. This reaction will be used as an example in order to discuss the mechanism of formation of uniform micrometer and submicrometer size metal particles by precipitation reactions.

Type
Fine Particles Part I
Copyright
Copyright © Materials Research Society 1989

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1.Zsigmondy, R., Z. Phyis. Chem. 56 (1906) p. 65.CrossRefGoogle Scholar
2.Zsigmondy, R. and Thiessen, P.A., Das Kolloide Gold, (Akad. Verlagsges, Leipzig, 1925).Google Scholar
3.Turkevich, J., Gold Bull. 18 (3) (1985) p. 86.CrossRefGoogle Scholar
4.LaMer, V.K. and Barnes, M.D., J. Colloid Sci. 1 (1946) p. 71.CrossRefGoogle Scholar
5.Demchak, R. and Matijević, E., J. Colloid Interface Sci. 31 (1969) p. 257.CrossRefGoogle Scholar
6.Brace, R. and Matijević, E., J. Inorg. Nucl. Chem. 35 (1973) p. 3691.CrossRefGoogle Scholar
7.Sugimoto, T. and Matijević, E., J. Colloid Interface Sci. 74 (1980) p. 227.CrossRefGoogle Scholar
8.Matijević, E., Langmir 2 (1986) p. 12.CrossRefGoogle Scholar
9.Van Helden, A.K., Jansen, J.W., and Vrig, A., J. Colloid Interface Sci. 81 (1981) p. 354.CrossRefGoogle Scholar
10.Overbeek, J.T.G., Adv. Colloid Interface Sci. 15 (1982) p. 251.CrossRefGoogle Scholar
11.Ferrier, G.G., Berzins, A.R., and Davey, N.M., Platinum Metals Rev., 29 (1985) p. 175.Google Scholar
12.Demopoulos, G.P. and Pouskouleli, G., J. of Metals 40 (1988) p. 46.Google Scholar
13.Zeniya, Y., Precious Metals 1986, edited by Rao, U.V., (IPMI, Allentown, PA, 1986) p. 409.Google Scholar
14.Walton, B., Radio Electron. Eng. 45 (1975) p. 139.CrossRefGoogle Scholar
15.Lemon, T.H., Platinum Metals Rev. 19 (1975) p. 146.Google Scholar
16.Larry, J.R., Rosenberg, R.M., and Uhler, R.O., IEEE Trans., Components, Hybrids Manuf. Technol. 3 (1980) p. 211.CrossRefGoogle Scholar
17.Figlarz, M., Fievet, F., and Lagier, J.P., French patent no. 82 21483 (December 21, 1982); Europe Patent No. 011 3281; U.S. Patent No. 45 39041; Finland Patent No. 74416; Japan Application No. 24 303783.Google Scholar
18.Blin, B., Thèse de Docteur Ingénieur, Université Paris 7, 1987.Google Scholar
19.Figlarz, M., Fievet, F., and Lagier, J.P., in Powder Preparation/Rapid Quenching, Proc. Int. Meeting on Advanced Materials, Tokyo 1988 (Mater. Res. Soc. Conf. Proc. 3, Pittsburgh, PA, 1989) p. 125.Google Scholar
20.Tekaia-Ehlsissen, K., Delahaye-Vidal, A., Nowogrocki, G., and Figlarz, M., C.R. Acad. Sci., Paris 309-II (1989) p. 349.Google Scholar
21.Fievet, F., Lagier, J.P., Blin, B., Beaudoin, B., and Figlarz, M., Solid State Ionics 32/33 (1989) p. 198.CrossRefGoogle Scholar
22.Blin, B., Fievet, F., Beaupère, D., and Figlarz, M., Nouv. J. Chim. 13 (1989) p. 67.Google Scholar
23.Sugimoto, T., Adv. Colloid Interface Sci. 28 (1987) p. 65.CrossRefGoogle Scholar
24.LaMer, V.K. and Dinegar, R.H., J. Am. Chem. Soc. 72 (1950) p. 4847.CrossRefGoogle Scholar
25.LaMer, V.K., Ind. Eng. Chem. 44 (1952) p. 1270.Google Scholar