Phase relation and thermoelectric property of Ca1-xBixMn1-yNiyO3 (0 ≤ x, y ≤ 0.1)

Published online by Cambridge University Press:  03 March 2016

Kenjiro Fujimoto ,
Minoru Gibu ,
Yuki Yamaguchi  and
Keishi Nishio
Kenjiro Fujimoto*
Affiliation:
Faculty of Science and Technology, Tokyo University of Science, Yamazaki 2641, Noda, Chiba, 278-8510 Japan Research Institute for Science and Technology, Tokyo University of Science, Yamazaki 2641, Noda, Chiba, 278-8510Japan
Minoru Gibu
Affiliation:
Faculty of Science and Technology, Tokyo University of Science, Yamazaki 2641, Noda, Chiba, 278-8510 Japan
Yuki Yamaguchi
Affiliation:
Faculty of Science and Technology, Tokyo University of Science, Yamazaki 2641, Noda, Chiba, 278-8510 Japan Research Institute for Science and Technology, Tokyo University of Science, Yamazaki 2641, Noda, Chiba, 278-8510Japan
Keishi Nishio
Affiliation:
Faculty of Industrial Science and Technology, Tokyo University of Science, Niijuku 6-3-1, Katsushika, Tokyo 125-8585, Japan Research Institute for Science and Technology, Tokyo University of Science, Yamazaki 2641, Noda, Chiba, 278-8510Japan
*
*(Email: [email protected])
Get access

Abstract

We established a Ca1-xBixMn1-yNiyO3 (0 ≤ x, y ≤ 0.1) powder library using a combinatorial system based on the electrostatic spray deposition method. Single phase perovskite-type structures were identified in all of the powders. To measure electrical conductivity, the powder library was subjected to high-pressure (200 MPa) and heat-treated at 950°C for 1 hour in an oxygen atmosphere. As a representative example, the electrical conductivity of 5%-Bi-substituted CaMnO3-δ showed a higher value (63 S·cm-1) than an unsubstituted powder (13 S·cm-1). The improved electrical conductivity, on the other hand, was still very far from the ideal result (167 S·cm-1).

Keywords

combinatorial synthesiscold isostatic pressing (CIP)thermoelectric
Type
Articles
Information
MRS Advances , Volume 1 , Issue 26: Theory, Characterization, and Modeling , 2016 , pp. 1941 - 1946
Copyright
Copyright © Materials Research Society 2016 

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

Merrifield, R. B., J. Am. Chem. Soc., 85 (1963) 2149 Google Scholar
Hanak, J. J. et al. , Physica, 55 (1971) 555 CrossRefGoogle Scholar
Koinuma, H. et al. , Jpn. J. Appl. Phys., 27 (1988) L1887Google Scholar
Koinuma, H. et al. , Nature Materials, 3(7) (2004) 429–438 CrossRefGoogle Scholar
Xiang, X. D. et al. , Science, 268 (1995) 1738 CrossRefGoogle Scholar
Fujimoto, K. et al. , Applied Surface Science, 223 (2004) 49.Google Scholar
Fujimoto, K. et al. , Measurement Science and Technology, 16 (2005) 41–45 Google Scholar
Fujimoto, K. et al. , Solid State Ionics, 177 (2006) 26–39 Google Scholar
Fujimoto, K. et al. , ACS Combinatorial Science, 16(2) (2014) 66–70 CrossRefGoogle Scholar
Fujimoto, K. et al. , ACS Combinatorial Science, 15 (2013) 622–625 Google Scholar
Ohtaki, M. et al. , Journal of Solid State Chemistry, 120 (1995) 105–111 Google Scholar
Bocher, L. et al. , Inorg. Chem., 47 (2008) 8077–8085 Google Scholar
Huang, X.Y. et al. , Solid State Communications, 145 (2008) 132–136 Google Scholar
Zhang, X.H. et al. , Journal of Alloys and Compounds, 634 (2015) 1–5 Google Scholar
Kabir, R. et al. , Journal of Alloy and Compounds, 628 (2015) 347–351 CrossRefGoogle Scholar
Fujimoto, K. et al. , Key Engineering Materials, 617 (2014) 256–259 Google Scholar
Poeppelmeier, K.R. et al. , Journal of Solid State Chemistry, 45(1) (1982) 71–9.Google Scholar
Poeppelmeier, K.R. et al. , Journal of Solid State Chemistry, 44(1) (1982) 89–98.Google Scholar