Effects of Si on Phase Stability and Precipitation Behavior of C14 Laves Phase (Fe,Cr)2(Nb,Mo) in High Cr αFe-base Alloys

Published online by Cambridge University Press:  12 February 2019

Yoshisato Kimura ,
Ko Kato  and
Yaw Wang Chai
Yoshisato Kimura*
Affiliation:
Department of Materials Science and Engineering, Tokyo Institute of Technology, Yokohama226-8502, Japan.
Ko Kato
Affiliation:
Department of Materials Science and Engineering, Tokyo Institute of Technology, Yokohama226-8502, Japan.
Yaw Wang Chai
Affiliation:
Department of Materials Science and Engineering, Tokyo Institute of Technology, Yokohama226-8502, Japan.
*
*(Email: [email protected])
Get access

Abstract

The growth mechanism of C14 Laves phase in the bcc αFe matrix was determined as the ledge mechanism on the (110)α//(0001)C14 habit plane in Fe-20Cr-0.5Nb-1Mo (at%) alloys annealed at 1073 K for 24 hours, using conventional and scanning transmission electron microscopy. Terrace planes are the basal plane of hcp-based C14 structure. Precipitation particles tend to grow in plate shape depending on the anisotropic difference of lattice mismatch. The addition of Si with Mo remarkably enhances C14 Laves phase precipitation. The area fraction of Laves phase increases from 5.9% to 12.1% by the 2Si addition on Fe-20Cr-0.5Nb-2Mo alloys. Contrary to this, the addition of Si is not effective to increase Laves phase precipitation. It is indicated that Si improves the phase stability of C14 Laves phase while the partitioning of Mo into C14 Laves phase would be promoted due to the attractive interaction between Mo and Si.

Keywords

microstructuretransmission electron microscopy (TEM)crystallographic structure
Type
Articles
Information
MRS Advances , Volume 4 , Issue 25-26: Processing and Manufacturing , 2019 , pp. 1477 - 1483
Check for updates
Copyright
Copyright © Materials Research Society 2019 

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

Fujita, N., Ohmura, K., Kikuchi, M., Suzuki, T., Funaki, S., and Hiroshige, I., Scr Mater. 35, 705–710 (1996).CrossRefGoogle Scholar
Yamamoto, K., Kimura, Y., Wei, F.G., Mishima, Y., Mat. Sci. Eng. A329–331, 249-254 (2002).CrossRefGoogle Scholar
Yamamoto, K., Kimura, Y., Mishima, Y., ISIJ Int. 43, 1253–1259 (2003).CrossRefGoogle Scholar
Fujita, N., Bhadeshia, H. K. D. H., Kikuchi, M., Simul, M., Mater. Sci. Eng. 12, 273–284 (2004).Google Scholar
Isik, M. I., Kostka, A., and Eggeler, G., Acta Mater. 81, 230-240 (2014).CrossRefGoogle Scholar
Okamoto, H., ed., Desk Handbook Phase Diagrams for Binary Alloys 2nd edition, (ASM Intl., Materials Park OH, 2010), p.278, 284, 285, 382, 383.Google Scholar
Villars, P., Prince, A. and Okamoto, H., Handbook of Ternary Alloy Phase Diagrams, Vol. 7 (ASM Intl. Materials Park, OH, 1995), pp. 8789-8817.Google Scholar
Villars, P., Prince, A. and Okamoto, H., Handbook of Ternary Alloy Phase Diagrams, Vol. 7 (ASM Intl. Materials Park, OH, 1995), pp. 8828-8833.Google Scholar
Westbrook, J. H., Interemetallic Compounds (Wiley, New York, (1977).Google Scholar
Iseda, A., Teranishi, H., and Yoshida, K., Testu-to-Hagane 76, 2190-2197 (1990). (in Japanese)CrossRefGoogle Scholar