Dry Process for Fabricating Low Cost and High Performance Electrode for Energy Storage Devices

Published online by Cambridge University Press:  16 January 2019

Qiang Wu ,
Jim P. Zheng ,
Mary Hendrickson  and
Edward J. Plichta
Qiang Wu*
Affiliation:
Department of Electrical and Computer Engineering, Florida A&M University and Florida State University, Tallahassee, FL32310, USA
Jim P. Zheng
Affiliation:
Department of Electrical and Computer Engineering, Florida A&M University and Florida State University, Tallahassee, FL32310, USA
Mary Hendrickson
Affiliation:
Army Power Division, RDER-CCA, 5100 Magazine Road, Aberdeen Proving Ground, MD21005, USA
Edward J. Plichta
Affiliation:
Army Power Division, RDER-CCA, 5100 Magazine Road, Aberdeen Proving Ground, MD21005, USA
*
*(Email: [email protected])
Get access

Abstract

We report a roll-to-roll dry processing for making low cost and high performance electrodes for lithium-ion batteries (LIBs). Currently, the electrodes for LIBs are made with a slurry casting procedure (wet method). The dry electrode fabrication is a three-step process including: step 1 of uniformly mixing electrode materials powders comprising an active material, a carbonaceous conductor and the soft polymer binder; step 2 of forming a free-standing, continuous electrode film by pressing the mixed powders together through the gap between two rolls of a roll-mill; and step 3 of roll-to-roll laminating the electrode film onto a substrate such as a current collector. Compared with the conventional wet slurry electrode manufacturing method, the dry manufactural procedure and infrastructure are simpler, the production cost is lower, and the process eliminates volatile organic compound emission and is more environmentally friendly, and the ability of making thick (>120µm) electrodes with high tap density results in high energy density of final energy storage device. A prototype LIBs of LiNi0.6Mn0.2Co0.2O2 (NMC622)/graphite also has 230 Wh/ kg energy density.

Keywords

energy storage
Type
Articles
Information
MRS Advances , Volume 4 , Issue 15: Energy-Transfer, Storage and Conversion , 2019 , pp. 857 - 863
Copyright
Copyright © Materials Research Society 2019 

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

Reference:

Simon, P., Gogotsi, Y., Nat. Mater. 7, 845 (2008).CrossRefGoogle Scholar
Obrovac, M., Chevrier, V., Chem. Rev. 114, 11444 (2014).CrossRefGoogle Scholar
Khomenko, V., Raymundo-Pinero, E., and Beguin, F., J. Power Sources 177, 643 (2008).CrossRefGoogle Scholar
Du, Z., Wood, D. L., Daniel, C., Kalnaus, S. and Li, J., J. Appl. Electrochem. 47, 405 (2017)CrossRefGoogle Scholar
Wood, D.L., Li, J., and Daniel, C., J. Power Sources, 275, 234 (2015).CrossRefGoogle Scholar
Duong, H. M., Feigenbaum, H., and Hong, J., US 20150303481 A1.Google Scholar
Al-Shroofy, M., Zhang, Q.L., Xu, J.G., Chen, T., Kaur, A.P., Cheng, Y. T., J. Power Sources 352, 187 (2017).CrossRefGoogle Scholar
Ludwig, B., Zheng, Z., Shou, W., Wang, Y., Pan, H., Sci. Rep. 6 (2016)Google Scholar
Yoshio, M., Brodd, R. J. and Kozawa, A. (eds.): Lithium-Ion Batteries - Science and Technologies. Springer Science & Business Media, LLC. 157 (2009).Google Scholar
Zheng, P. J., and Wu, Q., WO 2016210419 A1.Google Scholar
Supplementary material: File

Wu et al. supplementary material

Wu et al. supplementary material 1

Download Wu et al. supplementary material(File)
File 2 MB