Analyse des plaques composites fissurées et vieillies en conditions hygrothermiques

Published online by Cambridge University Press:  04 November 2011

Tahar Rezoug ,
Amina Benkhedda ,
Mohamed Khodjet-kesba  and
El Abbès Bedia Adda
Tahar Rezoug*
Affiliation:
Laboratoire des Sciences Aéronautiques, Département d’aéronautique de Blida, Université Saad Dahlab de Blida, 09130 Blida, Algérie
Amina Benkhedda
Affiliation:
Laboratoire des Sciences Aéronautiques, Département d’aéronautique de Blida, Université Saad Dahlab de Blida, 09130 Blida, Algérie
Mohamed Khodjet-kesba
Affiliation:
Laboratoire des Sciences Aéronautiques, Département d’aéronautique de Blida, Université Saad Dahlab de Blida, 09130 Blida, Algérie
El Abbès Bedia Adda
Affiliation:
Laboratoire de Matériaux et Hydrologie, Université de Sidi Bel Abbés, Algérie
*
aAuteur pour correspondance : [email protected]
Get access

Abstract

Cet article concerne les composites stratifiés croisés constitués de plis unidirectionnels. Ces stratifiés ont été vieillis en conditions hygrothermiques par des conditions d’environnement variables. En effet les propriétés mécaniques des stratifiés sont affectées par les variations de la température et de l’humidité. Lorsque des stratifiés croisés sont soumis à des sollicitations de traction quasi-statiques, le premier type d’endommagement qui apparaît est la fissuration transversale des couches orientées à 90°. La présence de ce type de fissures entraîne une diminution de la rigidité des stratifiés. Dans cet article, un modèle analytique fondé sur la diffusion du cisaillement a été modifié pour évaluer la perte de rigidité des stratifiés engendrée par le vieillissement hygrothermique avec la variation transitoire de la concentration en fonction de la densité de fissures. Les résultats de cet article démontrent clairement la dépendance de la dégradation des propriétés élastiques en fonction de la densité de fissuration et des conditions environnementales.

Keywords

MicrofissurationsrigiditévieillissementhygrothermieMicrofissuringrigidityageinghydrothermal
Type
Research Article
Information
Mechanics & Industry , Volume 12 , Issue 5 , 2011 , pp. 395 - 398
Copyright
© AFM, EDP Sciences 2011

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

Références

Kim, H.S., Wang, X.M., Nik Abbdulah, N.A.H, Effect of temperature on fatigue crack growth in the polymer ABS, J. Fatigue Fract. Eng. Mater. Struct. 17 (1994) 361–367 CrossRefGoogle Scholar
Kim, R.Y., Effect of temperature and moisture on pin bearing strength of composite laminates, J. Compos. Mater. 10 (1976) 149–155 CrossRefGoogle Scholar
Naitali, B., Hugot, F., El Ganaoui, M., Numerical study of a regularization technique of thermomechanical constraints in depots found in plasma projection, Mécanique & Industries 11 (2010) 75–80 CrossRefGoogle Scholar
Mckague, E.L., Halkias, J.R., J.E., Reynolds, Moisture in composites : The effect of supersonic service on diffusion, J. Compos. Mater. 9 (1975) 2–9 CrossRefGoogle Scholar
Shen, C.H., Springer, G., Moisture absorption and desorption of composite materials, J. Compos. Mater. 10 (1976) 2–20 CrossRefGoogle Scholar
K. Amara, A. Tounsi, A. Megueni, E. Adda Bedia, Evolution de la fissuration transverse dans les stratifiés croisés vieillis, Laboratoire des matériaux et hydrologie, Sidi bel Abbés, 2003
Ogi, K., Takao, Y., Evolution of transverse cracking in CF/Epoxy cross-ply laminates under creep loading, J. Reinf. Plast. Compos. 18 (1999) 1546–1556 CrossRefGoogle Scholar
Tounsi, A., Amara, K.H., Adda-dedia, E.A., Analysis of transverse cracking and stiffness loss in cross-ply laminates with hygrothermal conditions, Comput. Mater. Sci. 32 (2005) 167–174 CrossRefGoogle Scholar
Tounsi, A., Amara, K., Benzair, A., Megueni, A., On the transverse cracking and stiffness degradation of aged angle-ply laminates, Mater. Lett. 60 (2006) 2561–2564 CrossRefGoogle Scholar
Bouazza, M., Tounsi, A., Benzair, A., Adda-dedia, E.A., Effect of transverse cracking on stiffness reduction of hygrothermal aged cross-ply laminates, Materials and Design 28 (2007) 1116–1123 CrossRefGoogle Scholar
S.W. Tsai, Composite design, Think composite, 4th edition, Dayton, 1988
J.G. Bauzin, N. Laraqi, A. Baïri, Estimation of thermal contact parameters at the interface of two sliding bodies, J. Phys.: Conference Series 135 (2008) 022015, DOI: 10.1088/1742-6596/135/1/012015 CrossRef
Bauzin, J.G., Laraqi, N., Simultaneous estimation of frictional heat flux and two thermal contact parameters for sliding contacts, Numer. Heat Transf. A Appl. 45 (2004) 313–328 CrossRefGoogle Scholar