ZrO2-nucleated calcium aluminate glass-ceramics with mid-infrared transparency

Published online by Cambridge University Press:  01 February 2006

Jiin-Jyh Shyu  and
Hung-Chuan Mai
Jiin-Jyh Shyu*
Affiliation:
Department of Materials Engineering, Tatung University, Taipei 104, Taiwan, Republic of China
Hung-Chuan Mai
Affiliation:
Department of Materials Engineering, Tatung University, Taipei 104, Taiwan, Republic of China
*
a)Address all correspondence to this author. e-mail: [email protected]
Get access

Abstract

A silica-free MgO–CaO–BaO–Al2O3–ZrO2 glass was converted into glass-ceramic by adding zirconia as a nucleating agent. The crystallization and properties of the glass-ceramics were investigated. It was found that ZrO2 is an efficient nucleating agent for the present calcium aluminate glass. Addition of an appropriate amount of ZrO2 changed the crystallization behavior from surface nucleation to internal nucleation. The primary crystalline phase was Ca3Al2O6, which exhibited bulk nucleation. When the crystallizing time was increased, BaAl2O4 formed as a surface layer that grew from the surface into the interior of the sample. The hardness was increased when the parent glass was converted into glass-ceramics. The glass-ceramics without BaAl2O4 surface layer have visible-to-infrared transparency comparable with the parent glass. The transparency was substantially reduced after the development of the surface layer.

Keywords

Nucleation & growthSi
Type
Articles
Information
Journal of Materials Research , Volume 21 , Issue 2 , February 2006 , pp. 465 - 472
Copyright
Copyright © Materials Research Society 2006

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1.Line, M.E., MacChesney, J.B., Lyons, K.B., Bruce, A.J., Miller, A.E. and Nassau, K.: Calcium aluminate glasses as potential ultralow-loss optical materials at 1.5–1.9 μm. J. Non-Cryst. Solids 107, 251 (1989).Google Scholar
2.Line, M.E.: A possible non-halide route to ultralow loss glasses. J. Non-Cryst. Solids 103, 279 (1988).CrossRefGoogle Scholar
3.Hosono, H., Yamazaki, K. and Abe, Y.: Dopant-free ultraviolet-sensitive calcium aluminate glasses. J. Am. Ceram. Soc. 68, C-304 (1985).Google Scholar
4.Hosono, H., Yamazaki, K. and Abe, Y.: Photosensitive characteristics of dopant-free, ultraviolet-sensitive calcium aluminate glasses. J. Am. Ceram. Soc. 70, 867 (1987).CrossRefGoogle Scholar
5.Davy, J.R.: Development of calcium aluminate glasses for use in the infrared spectrum to 5 μm. Glass Technol. 19, 32 (1978).Google Scholar
6.Hafner, H.C., Kreidl, N.J. and Weidel, R.A.: Optical and physical properties of some calcium aluminate glasses. J. Am. Ceram. Soc. 41, 315 (1958).CrossRefGoogle Scholar
7.Higby, P.L., Ginther, R.J., Aggarwal, I.D. and Friebele, E.J.: Glass formation and thermal properties of low-silica calcium aluminosilicate glasses. J. Non-Cryst. Solids 126, 209 (1990).Google Scholar
8.Pye, L.D. Aluminate glasses—A review, in Infrared Optical Materials VI, edited by Musikant, S. (SPIE Proc. 929 The International Soc. for Opt. Eng., Bellingham, WA, 1988), p. 149.CrossRefGoogle Scholar
9.Saggese, S.J. and Harrington, J.A.: Calcium-aluminate glass for use as n < 1 hollow waveguides in the delivery of CO2 laser energy. Opt. Mater. 2, 119 (1993).Google Scholar
10.Wallenberger, F.T., Weston, N.E. and Dunn, S.A.: Melt spun calcium aluminate fibers: Infrared transmission. J. Non-Cryst. Solids 124, 116 (1990).CrossRefGoogle Scholar
11.Chung, W.J. and Heo, J.: Energy transfer process for the blue up-conversion in calcium aluminate glasses doped with Tm3+ and Nd3+. J. Am. Ceram. Soc. 84, 348 (2001).Google Scholar
12.Tanabe, S., Ohyagi, T., Hanada, T. and Soga, N.: Upconversion and local structure of Er3+-doped aluminate glasses. J. Ceram. Soc. Jpn. 101, 78 (1993).CrossRefGoogle Scholar
13.Li, W. and Mitchell, B.S.: Nucleation and crystallization in calcium aluminate glasses. J. Non-Cryst. Solids 255, 199 (1999).CrossRefGoogle Scholar
14.Sung, Y.M. and Sung, J.H.: Crystallization behavior of calcium aluminate glass fibers. Part I. Differential thermal analysis study. J. Mater. Sci. 33, 4733 (1998).Google Scholar
15.Mitchell, B.S., Yon, K.Y., Dunn, S.A. and Koutsky, J.A.: Phase identification in calcia-alumina fibers crystallized from amorphous precursors. J. Non-Cryst. Solids 152, 143 (1993).CrossRefGoogle Scholar
16.Höland, W. and Beall, G.H.: Glass-Ceramic Technology (The American Ceramic Society, Westerville, OH, 2002), p. 48.Google Scholar
17.Marotta, A., Buri, A., Branda, F. and Saiello, S. Nucleation and crystallization of Li2O · 2SiO2 glass—A DTA study, in Advances in Ceramics, Vol. 4: Nucleation and Crystallization in Glasses, edited by Simmons, J.H., Uhlmann, D.R., and Beall, G.H. (American Ceramic Society, Columbus, OH, 1982), p. 146.Google Scholar
18.Ray, C.S. and Day, D.E.: Determining the nucleation rate curve for lithium disilicate glass by differential thermal analysis. J. Am. Ceram. Soc. 73, 439 (1990).CrossRefGoogle Scholar
19.Beall, G.H. and Pinckney, L.R.: Nanophase glass-ceramics. J. Am. Ceram. Soc. 82, 5 (1999).CrossRefGoogle Scholar