Zn doping in YBCO single crystal by the solute-rich liquid-crystal pulling method

Published online by Cambridge University Press:  31 January 2011

X. Yao
Affiliation:
Superconductivity Research Laboratory, ISTEC, 1–10–13 Shinonome Koto-ku, Tokyo 135, Japan
K. Ohtsu
Affiliation:
Superconductivity Research Laboratory, ISTEC, 1–10–13 Shinonome Koto-ku, Tokyo 135, Japan
S. Tajima
Affiliation:
Superconductivity Research Laboratory, ISTEC, 1–10–13 Shinonome Koto-ku, Tokyo 135, Japan
H. Zama
Affiliation:
Superconductivity Research Laboratory, ISTEC, 1–10–13 Shinonome Koto-ku, Tokyo 135, Japan
F. Wang
Affiliation:
Superconductivity Research Laboratory, ISTEC, 1–10–13 Shinonome Koto-ku, Tokyo 135, Japan
Y. Shiohara
Affiliation:
Superconductivity Research Laboratory, ISTEC, 1–10–13 Shinonome Koto-ku, Tokyo 135, Japan
Get access

Abstract

Zn-doped YBa2Cu3O6+δ (YBCO) single crystals were fabricated by the solute-rich liquid-crystal pulling (SRL-CP) method. The Zn content of x ranged from 0.0035–0.029 and almost uniformly distributed in YBa2(Cu1−xZnx)3O6+δ. There is a nearly linear relationship between the added Zn content in the liquid and the analyzed Zn content in the liquid/in the crystal. When the added Zn content Cl was 1.086 at. %, decreasing of growth temperature led to increasing growth rate. However, growth temperature had no obvious effect on the doped Zn content in the crystal Cs, the Zn content in the flux Cl, and the effective distribution ratio of k′. In addition, growth spirals on the grown crystal surface were observed by atomic force microscopy (AFM). X-ray Laue pattern and RBS measurements are indicative of good crystallinity of YBa2(Cu1−xZnx)3O6+δ. Critical temperatures of Tc changed from 89 to 57 K when the Zn content x ranged 0.0035 to 0.029 after appropriate oxygenation.

Type
Articles
Copyright
Copyright © Materials Research Society 1996

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1.Markert, J. T., Dunlap, B.D., and Maple, M.B., MRS Bull. 14, 37 (1989).Google Scholar
2.Semba, K., Ishii, T., and Matsuda, A., unpublished.Google Scholar
3.Maeda, H., Koizumi, A., Bamba, N., Takayama-Muromachi, E., Izumi, F., Asano, H., Shimizu, K., Moriwaki, H., Maruyama, H., Kuroda, Y., and Yamazaki, H., Physica C 157, 483 (1989).CrossRefGoogle Scholar
4.Chien, T. R., Wang, Z.Z., and Ong, N.P., Phys. Rev. Lett. 67, 2088 (1991).Google Scholar
5.Tarascon, J. M., Barboux, P., Miceli, P. F., Greene, L.H., Hull, G. W., Eibschutz, M., and Sunshine, S. A., Phys. Rev. B 37, 7458 (1988).CrossRefGoogle Scholar
6.Yamada, Y. and Shiohara, Y., Physica C 217, 182 (1993).Google Scholar
7.Liang, R., Dosanjh, P., and Bonn, D. A., Physica C 195, 51 (1992).CrossRefGoogle Scholar
8.Scheel, H. J., Klemenz, C., Reinhart, F-K., Lang, H. P., and Güntherodt, H-J., Appl. Phys. Lett. 65, 901 (1994).Google Scholar
9.Flemings, M.C., Solidification Processing (McGraw-Hill Book Company, New York, 1974).CrossRefGoogle Scholar
10.Burton, J. A., Prim, R. C., and Slichter, W. P., J. Chem. Phys. 21, 1987 (1953).CrossRefGoogle Scholar
11.Yamada, Y., Nakamura, M., Shiohara, Y., and Tanaka, S., Cryst. Growth 148, 241 (1995).Google Scholar