The use of polymeric milling media in the reduction of contamination during mechanical attrition

Published online by Cambridge University Press:  31 January 2011

Claudio L. De Castro  and
Brian S. Mitchell
Claudio L. De Castro
Affiliation:
Department of Chemical Engineering, Tulane University, New Orleans, Louisiana 70118
Brian S. Mitchell*
Affiliation:
Department of Chemical Engineering, Tulane Institute for Macromolecular Engineering and Science, Tulane University, New Orleans, Louisiana 70118
*
a)Address all correspondence to this author.
Get access

Abstract

Aluminum samples were milled in a high-energy ball mill at times ranging from 10 to 500 min in stainless vial/media and nylon vial/media. The crystallite size of aluminum milled in the stainless steel setup reached a plateau at 25 nm around 100 min, whereas the crystallite size of aluminum milled in the nylon setup reached the same plateau at 500 min. Contamination studies were conducted using x-ray fluorescence, hydrogen–carbon–nitrogen analysis, and thermogravimetric analysis. Although organic contamination due to the nylon milling media was high at 12 wt% when milled for 500 min, it is shown that the contaminant could be easily removed by thermal treatment.

Type
Rapid Communications
Information
Journal of Materials Research , Volume 17 , Issue 12 , December 2002 , pp. 2997 - 2999
Copyright
Copyright © Materials Research Society 2002

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1.Castro, C.L. De and Mitchell, B.S., in Synthesis, Functionalization and Surface Treatment of Nanoparticles, edited by Baraton, M.I. (American Scientific Publishers, Los Angeles, CA, 2002), p. 1.Google Scholar
2.Koch, C.C., Nanostruct. Mater. 2, 109–129 (1993).CrossRefGoogle Scholar
3.Kuhn, E., in Powder Metallurgy (ASM, Materials Park, OH, 1984), p. 56–70.Google Scholar
4.Kim, Y.D., Chung, J.Y., Kim, J., and Jeon, H., Mater. Sci. Eng. A 291, 17 (2002).CrossRefGoogle Scholar