Structures and magnetic properties of Sm-Fe-N bulk magnets produced by the spark plasma sintering method

Published online by Cambridge University Press:  31 January 2011

Tetsuji Saito
Tetsuji Saito*
Affiliation:
Department of Mechanical Science and Engineering, Chiba Institute of Technology, Narashino, Chiba 275-0016, Japan
*
a)Address all correspondence to this author. e-mail: [email protected]
Get access

Abstract

Sm-Fe-N powders were successfully consolidated at 873 K and below by the spark plasma sintering (SPS) method. Although the decomposition temperature of the hard magnetic Sm2Fe17N3 phase has been reported to be 873 K, partial decomposition of the Sm2Fe17N3 phase was noted in the bulk materials obtained by sintering at below that temperature. The resultant bulk materials showed a coercivity of around 0.24 MAm−1, significantly lower than that of the original Sm-Fe-N powder. It was found that decomposition of the Sm2Fe17N3 phase in the SPS method was significantly lowered by the addition of a small amount of Zn powder to the Sm-Fe-N powder. The bulk material obtained by sintering a mixture of Sm-Fe-N and Zn powder (10%Zn) at 723 K exhibited high coercivity, comparable with that of the original Sm-Fe-N powder.

Keywords

Magnetic propertiesSinteringNitride
Type
Articles
Information
Journal of Materials Research , Volume 22 , Issue 11 , November 2007 , pp. 3130 - 3136
Copyright
Copyright © Materials Research Society 2007

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1Croat, J.J., Herbst, J.F., Lee, R.W.Pinkerton, F.E.: Pr-Fe and Nd-Fe-based materials: A new class of high-performance permanent magnets. J. Appl. Phys. 55, 2078 1984CrossRefGoogle Scholar
2Sagawa, M., Fujimura, S., Togawa, N., Yamamoto, H.Matsuura, Y.: New materials for permanent magnets on a base of Nd and Fe. J. Appl. Phys. 55, 2083 1984CrossRefGoogle Scholar
3Coehoorn, R., de Mooij, D.B., Duchateau, J.P.W.B.Buschow, K.H.J.: Novel permanent magnetic materials made by rapid quenching. J. Phys. E 49, 669 1988Google Scholar
4Coey, J.M.D.Sun, H.: Improved magnetic properties by treatment of iron-based rare earth intermetallic compounds in anmonia. J. Magn. Magn. Mater. 87, L251 1990CrossRefGoogle Scholar
5Buschow, K.H.J.: Structure and properties of some novel ternary Fe-rich rare-earth intermetallics. J. Appl. Phys. 63, 3130 1988CrossRefGoogle Scholar
6Cadgan, J.M., Li, H.S., Margarian, A., Dunlop, J.B., Ryan, R.H., Collocott, S.J.Davis, R.L.: New rare-earth intermetallic phase R3(Fe,M)29Xn; (R = Ce, Pr, Nd, Sm, Gd; M = Ti, V, Cr, Mn; and X = H, N, C. J. Appl. Phys. 76, 6138 1994CrossRefGoogle Scholar
7Sakurada, S., Tsutai, A., Hirai, T., Yanagida, Y.Sahashi, M.: Structural and magnetic properties of rapidly quenched (R,Zr)(Fe, Co)10Nx (R=Nd, Sm). J. Appl. Phys. 79, 4611 1996CrossRefGoogle Scholar
8Leonowicz, M., Kaszuwara, W., Jezierska, E., Januszewski, D., Mendoza, G., Davies, H.A.Paszula, J.: Application of the shock compaction technique for consolidation of hard magnetic powders. J. Appl. Phys. 83, 6634 1998CrossRefGoogle Scholar
9Mashimo, T., Huang, X., Hirosawa, S., Makita, K., Kato, Y., Mitsudo, S.Motokawa, M.: Magnetic properties of fully dense Sm2Fe17Nx magnets prepared by shock compression. J. Magn. Magn. Mater. 210, 109 2000CrossRefGoogle Scholar
10Saito, T., Fukui, M.Takeishi, H.: Sm-Fe-N bulk magnets produced by compression shearing method. Scripta Mater. 53, 1117 2005CrossRefGoogle Scholar
11Tokita, M.: Trends in advanced SPS spark plasma sintering system and technology. J. Soc. Powder Technol. Jpn. 30, 790 1993CrossRefGoogle Scholar
12Ono, H., Waki, N., Shimada, M., Sugiyama, T., Fujiki, A., Yamamoto, H.Tani, M.: Isotropic bulk exchange-spring magnets with 134 kJ/m3 prepared by spark plasma sintering method. IEEE Trans. Mag. 37, 2552 2001CrossRefGoogle Scholar
13Saito, T., Tomonari, T.Kageyama, H.: Production of bulk amorphous and nanocomposite materials of an Nd4Fe77.5B18.5 alloys by spark plasma sintering method. IEEE Trans. Mag. 40, 2880 2004CrossRefGoogle Scholar
14Otani, Y., Moukarita, A., Sun, H.Coey, J.M.D.: Metal bonded Sm2Fe17N3−δ magnets. J. Appl. Phys. 69, 6735 1991Google Scholar
15Huang, M.Q., Zhang, L.Y., Ma, B.M., Zheng, Y., Elibicki, J.M., Wallace, W.E.Sanker, S.G.: Magnetism of (Sm,R)2Fe17Ny (R=Y, Tb or mischmetal). J. Appl. Phys. 70, 6027 1991CrossRefGoogle Scholar
16Wendhausen, P.A.P., Eckert, D., Handstein, A., Müller, K-H., Leitner, G.Skomski, R.: On the role of Zn in Sm2Fe17Nx permanent magnets. J. Appl. Phys. 73, 6044 1993CrossRefGoogle Scholar