Structural characterization of sputter-deposited LaNiO3 thin films on Si substrate by x-ray reflectivity and diffraction

Published online by Cambridge University Press:  31 January 2011

Hsin-Yi Lee  and
Tai-Bor Wu
Hsin-Yi Lee
Affiliation:
Department of Materials Science and Engineering, National Tsing Hua University, and Research Division, Synchrotron Radiation Research Center, Hsinchu 30077, Taiwan, Republic of China
Tai-Bor Wu
Affiliation:
Department of Materials Science and Engineering, National Tsing Hua University, Hsinchu 30043, Taiwan, Republic of China
Get access

Abstract

X-ray reflectivity and diffraction were applied to characterize the highly (100)-textured thin films of LaNiO3, which were deposited on Si substrate via radio frequency magnetron sputtering at temperatures ranging from 250 to 450 °C. Two interference fringes of different period were observed from the reflectivity curves, and the fitting result indicates that in addition to the normal lanthanum-nickel oxide layer, a transition layer, which has a larger mass density than the previous one, exists in the sputter-deposited films. A comparison of the measured x-ray diffraction intensity with that calculated from layer thickness and mass density obtained from reflectivity data indicates that the transition layer is noncrystalline. The x-ray diffraction result also shows that there is a significant decrease of (100) diffraction intensity relative to that of (200) as increasing the deposition temperature. Using the reflectivity and diffraction data along with results of electron diffraction and film composition analysis from our other studies, such a change of relative intensity between the two diffraction peaks is attributed to the increasing content of two also highly textured La-rich phases, i.e., (110)-textured La4Ni3O10 and (100)-textured La2NiO4, in addition to the LaNiO3.

Type
Articles
Information
Journal of Materials Research , Volume 12 , Issue 11 , November 1997 , pp. 3165 - 3173
Copyright
Copyright © Materials Research Society 1997

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1.Bruchhaus, R., Pitzer, D., Eibl, O., Scheithauer, V., and Hoesler, W., in Ferroelectric Thin Films II, edited by Kingon, A. I., Myers, E. R., and , B. (Mater. Res. Soc. Symp. Proc. 243, Pittsburgh, PA, 1992), p. 123.Google Scholar
2.Jiang, M. C. and Wu, T. B., J. Mater. Res. 9, 1879 (1994).CrossRefGoogle Scholar
3.Scott, J. F. and Paz de Araujo, C. A., Science 246, 1400 (1989).CrossRefGoogle Scholar
4.Eom, C. B., van Dover, R. B., Phillips, J. M., Fleming, R. M., Cava, R. J., Marshall, J. H., Werder, D. J., Chen, C. H., and Fork, D. K., in Ferroelectric Thin Films III, edited by Tuttle, B. A., Myers, E. R., Desu, S. B., and Larsen, P. K. (Mater. Res. Soc. Symp. Proc. 310, Pittsburgh, PA, 1993), p. 145.Google Scholar
5.Vijat, D. P. and Desu, S. B., J. Electrochem. Soc. 140, 2640 (1993).Google Scholar
6.Nakamuna, T., Nakao, Y., Kamisawa, A., and Takasu, H., Jpn. J. Appl. Phys. 33, 5207 (1994).Google Scholar
7.Ramesh, R., Chan, W. K., Wilkens, B., Gilchrist, H., Sands, T., Tarascon, J. M., Keramidas, V. G., Fork, D. K., Lee, J., and Safari, A., Appl. Phys. Lett. 61, 1537 (1992).CrossRefGoogle Scholar
8.Wold, A., Post, B., and Banks, E., J. Am. Chem. Soc. 70, 4911 (1957).CrossRefGoogle Scholar
9.Obayashi, H. and Kudo, T., Jpn. J. Appl. Phys. 14, 330 (1957).CrossRefGoogle Scholar
10.Rajeez, K. P., Shivakuma, G. V., and Raychaudhmi, A. K., Solid State Commun. 79, 591 (1991).Google Scholar
11.Yang, C. C., Chen, M. S., Hong, T. J., Wu, C. M., Wu, J.M., and Wu, T. B., Appl. Phys. Lett. 66, 2643 (1995).CrossRefGoogle Scholar
12.Shyu, M. J., Hong, T. J., and Wu, T. B., Jpn. J. Appl. Phys. 34, 3647 (1995).CrossRefGoogle Scholar
13.Shyu, M. J., Hong, T. J., and Wu, T. B., Mater. Lett. 23, 221 (1995).CrossRefGoogle Scholar
14.Chen, M. S., Wu, J. M., and Wu, T. B., Jpn. J. Appl. Phys. 34, 4870 (1995).CrossRefGoogle Scholar
15.Chen, M. S., Wu, T. B., and Wu, J. M., Appl. Phys. Lett. (in press).Google Scholar
16.Kiessig, H., Ann. Physik. 10, 715 (1931).CrossRefGoogle Scholar
17.Cowley, R. A. and Ryan, T. W., J. Phys. D. 20, 61 (1987).CrossRefGoogle Scholar
18.Parratt, L. G., Phys. Rev. 95, 359 (1954).CrossRefGoogle Scholar
19.Braslau, A., Pershan, P. S., Swislow, G., Ocko, B. M., and Als-Nielsen, J., Phys. Rev. A 38, 2457 (1988).CrossRefGoogle Scholar
20.Heald, S. M., Chen, H., and Tranquada, J. M., Phys. Rev. B 38, 1016 (1988).CrossRefGoogle Scholar
21.Lucas, C. A., Hatton, P. D., Bates, S., Ryan, W., Miles, S., and Tanner, B. K., J. Appl. Phys. 63, 1936 (1988).CrossRefGoogle Scholar
22.Chen, H. and Heald, S. M., J. Appl. Phys. 66, 1793 (1989).CrossRefGoogle Scholar
23.Tidswell, I. M., Ocko, B. M., Pershan, P. S., Wasserman, S. R., Whitesides, G. M., and Axe, J. D., Phys. Rev. B 41, 1111 (1990).CrossRefGoogle Scholar
24.Bowen, D. K., Loxley, N., Tanner, B. K., Cooke, M. L., and Capano, M. A., in Advances in Surfaces and Thin Film Diffraction, edited by Huang, T. C., Cohen, P. I., and Eaglesham, D. J. (Mater. Res. Soc. Symp. Proc. 208, Pittsburgh, PA, 1991), p. 113.Google Scholar
25.Wu, T. B., Hong, T. J., and Jiang, M. C., Mater. Chem. Phys. 36, 337 (1994).CrossRefGoogle Scholar
26.Sinha, S. K., Sirota, E. B., Garoff, S., and Stanley, H. B., Phys. Rev. B 38, 2297 (1988).CrossRefGoogle Scholar
27.Sinha, S. K., Physica B 173, 25 (1991).CrossRefGoogle Scholar
28.Yoneda, Y., Phys. Rev. 131, 2010 (1963).CrossRefGoogle Scholar
29.Tseng, S. Y. and Lee, C. H., J. Vac. Soc. ROC. 6, 4 (1993).Google Scholar
30.Lee, H. Y., Wu, T. B., and Lee, J. F., J. Appl. Phys. 80, 2175 (1996).CrossRefGoogle Scholar
31.Hong, T. J., Ph.D. Thesis (in Chinese), National Tsing Hua University, 1995.Google Scholar
32. JCPDS 34–314 and 33–710, Wustenberg, H., Hahn, Inst. für Kristallogr., Techische Hochschule, Aachen, Germany, JCPDS Grant-in-Report, 1981.Google Scholar
33. JCPDS 35–1242, Brisi, C., Vallino, M. and Abbattistra, F., J. Less-Comm. Met. 79, 215 (1981).CrossRefGoogle Scholar
34.Cullity, B. D., Elements of X-ray Diffraction, 2nd ed., edited by Cohen, M. (Addison-Wesley Publishing Company, Inc., Reading, MA, 1978), pp. 134 and 292.Google Scholar
35.Liu, Y. W., M.S. Thesis (in Chinese), National Tsing Hua University, 1996.Google Scholar