Stress development and relaxation during reactive film formation of Ni2Si

Published online by Cambridge University Press:  03 March 2011

K.P. Liew ,
R.A. Bernstein  and
C.V. Thompson
K.P. Liew
Affiliation:
Singapore-MIT Alliance, 4 Engineering Drive 3, Singapore 117576
R.A. Bernstein
Affiliation:
Department of Materials Science and Engineering, Massachusetts Institute of Technology, Cambridge, Massachusetts 02139
C.V. Thompson
Affiliation:
Singapore-MIT Alliance, 4 Engineering Drive 3, Singapore 117576; and Department of Materials Science and Engineering, Massachusetts Institute of Technology, Cambridge, Massachusetts 02139
Get access

Abstract

Using continuous wafer-curvature measurements, stress generation was monitored as nickel thin films reacted with silicon substrates to form Ni2Si during isothermal anneals. A large compressive force developed during the reaction, but gradually relaxed after the reaction was complete. From a model for reactive film formation, a lower limit for the instantaneous stress associated with compound formation was found to be −2.00 ± 0.75 GPa. This instantaneous stress can be explained by a volumetric strain of 1.65 ± 0.62%, which is much smaller than the theoretical volume expansion of 62% in this system. These results suggest that significant inelastic deformation occurs during silicide formation. It was also found that diffusive creep relaxes the growth stress after the reaction. The observed instantaneous stress indicates that the energy of deformation associated with the reaction is of the same order as the energy that drives it, suggesting that stress generation and stress relaxation can play a significant role in the kinetics of reactive film formation.

Keywords

DiffusionSputteringMetal
Type
Articles
Information
Journal of Materials Research , Volume 19 , Issue 2 , February 2004 , pp. 676 - 680
Copyright
Copyright © Materials Research Society 2004

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1Einspruch, N.G.: VLSI Electronics: Microstructure Science 6 355 (1983).Google Scholar
2Steegen, A. and Maex, K.: Mater. Sci. Eng. R 38 1 (2002).Google Scholar
3Tsai, C. and Hu, K.: Thin Solids Films 350 91 (1999).CrossRefGoogle Scholar
4Chen, L.J., Cheng, S.L., Luo, H.M., Huang, H.Y., Peng, Y.C., Tsui, B.Y., Tsai, C.J. and Guo, S.S. The influences of stress on the growth of Ti and Ni silicides on (001)si, 5th International Conference on Solid-State and Integrated Circuit Technology: Proceedings 256, (1998).Google Scholar
5Marcus, R.B. and Sheng, T.T.: J. Electrochem. Soc. 129 1278 (1982).Google Scholar
6Kao, D.B., McVittie, J.P., Nix, W.D. and Saraswat, K.C.IEEE International Electron Devices Meeting Technical Digest p. 388 (1985).Google Scholar
7Sutardja, P.Modeling of stress effects and in silicon oxidation, Trans. Electron Devices 36, Gainesville, FL 2415 (1989).Google Scholar
8Cea, S. Ph.D. Thesis, University of Florida (1996).Google Scholar
9Xu, D.X., Das, S.R., Peters, C.J. and Erickson, L.E.: Thin Solid Films 326 143 (1998).CrossRefGoogle Scholar
10Maillard-Schaller, E., Boyanov, B.I., English, S. and Nemanich, R.J.: J. Appl. Phys. 85 3614 (1999).CrossRefGoogle Scholar
11d’Heurle, F.M. and Thomas, O.Defect and Diffusion Forum 129–130, 137 (1996).Google Scholar
12Zhang, S.L. and d’Heurle, F.M.Thin Solid Films 213 34 (1992).CrossRefGoogle Scholar
13Liew, K.P., Bernstein, R.A. and Thompson, C.V. (Unpublished).Google Scholar
14Lavoie, C., Coia, C., Purtell, R., Desjardins, P., Jordan-Sweet, J.L.Cabral, C. Jr.d’Heurle, F.M. and Harper, J.M.E.Electrochemical Society Symposium Proceedings 455 2001 (2002).Google Scholar
15Gambino, J.P. and Colgan, E.G.: Mater. Chem. Phys. 52 99 (1998).Google Scholar
16Nix, W.D.: Metall. Trans. 20A 2217 (1989).Google Scholar
17Stoney, G.G.: Proc. R. Soc. (London) A 82 172 (1909).Google Scholar
18Thompson, C.V. and Carel, R.: J. Mech. Phys. Solids 44 657 (1996).Google Scholar
19Knauth, P., Charai, A. and Gas, P.: Scr. Metall. Mater. 28 325 (1993).Google Scholar
20Liew, K.P., Thesis, M.S. National University of Singapore Singapore (2003).Google Scholar
21Press, W.H., Flannery, B.P., Teukolsky, S.A. and Vetterling, W.T.Numerical Recipe in C: The Art of Scientific Computing 2nd ed. (Cambridge University Press, New York, NY 1992, p. 410).Google Scholar
22Ciccariello, J-C., Poize, S. and Gas, P.: J. Appl. Phys. 67 3315 (1990).Google Scholar
23Properties of Metal Silicides, edited by Maex, K. and van Rossum, M. (Inspec, London, 1995), p. 15.Google Scholar
24Gas, P. and d’Heurle, F.M. in Silicide Thin Films—Fabrication, Properties, and Applications, edited by Tung, R.T., Maex, K., Pellegrini, P.W., and Allen, L.H. (Mater. Res. Soc. Symp. Proc. 402, Pittsburgh, PA 1996) p. 39.Google Scholar