Segregation of Vanadium at the WC/Co Interface in VC-doped WC-Co

Published online by Cambridge University Press:  31 January 2011

A. Jaroenworaluck
Affiliation:
Department of Materials Science, Faculty of Engineering, The University of Tokyo, 7-3-1, Bunkyo-ku, Tokyo 113–8656, Japan
T. Yamamoto
Affiliation:
Department of Materials Science, Faculty of Engineering, The University of Tokyo, 7-3-1, Bunkyo-ku, Tokyo 113–8656, Japan
Y. Ikuhara
Affiliation:
Department of Materials Science, Faculty of Engineering, The University of Tokyo, 7-3-1, Bunkyo-ku, Tokyo 113–8656, Japan
T. Sakuma
Affiliation:
Department of Materials Science, Faculty of Engineering, The University of Tokyo, 7-3-1, Bunkyo-ku, Tokyo 113–8656, Japan
T. Taniuchi
Affiliation:
Tsukuba Plant, Mitsubishi Materials Corp., 1511 Furumagi, Ishige-machi, Yuuki-gun, Ibaraki 300–2795, Japan
K. Okada
Affiliation:
Tsukuba Plant, Mitsubishi Materials Corp., 1511 Furumagi, Ishige-machi, Yuuki-gun, Ibaraki 300–2795, Japan
T. Tanase
Affiliation:
Tsukuba Plant, Mitsubishi Materials Corp., 1511 Furumagi, Ishige-machi, Yuuki-gun, Ibaraki 300–2795, Japan
Get access

Abstract

Morphology of carbide grain in WC–12 wt.% Co–0.5 wt.% VC was examined by HREM and EDS with a special interest in the segregation of V at the WC/Co interfaces. A small addition of VC in WC-Co is effective to suppress the grain growth of carbide grains. HREM observation revealed that the WC/Co interfaces are faceted and consist of mainly two kinds of habit planes, (1010) and (0001), respectively. EDS analyses clearly showed the segregation of doped V along the interfaces. In addition, the concentration of segregated V is higher at the (0001) type habit plane than (1010) one. The retardation of the grain growth of carbide grains in the VC-doped WC-Co is closely related to the formation of the faceted WC/Co interface.

Type
Articles
Copyright
Copyright © Materials Research Society 1998

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1.Exner, H. E., Int. Metals Rev. 4, 149 (1979).Google Scholar
2.Egami, A., Ehira, M., Machida, M., Proceedings of 13th Int. Plansee Seminar, edited by Bildstein, H., and Eck, R., Metallwerk Plansee, Reutte (1993), Vol. 3, p. 693.Google Scholar
3.Taniuchi, T., Okada, K., and Tanase, T., Proceedings of 14th Int. Plansee Seminar (1997).Google Scholar
4.Mohan, K. and Strutt, P. R., NanoStructured Mater. 7 (5), 547 (1996).CrossRefGoogle Scholar
5.Mohan, K. and Strutt, P. R., Mater. Sci. Eng. A209 (1–2), 237 (1996).CrossRefGoogle Scholar
6.Suzuki, H., Fuke, Y., and Hayashi, K., J. Jpn. Osc. Powder & Powder Metall. 19 (3), 106 (1972).CrossRefGoogle Scholar
7.Terade, O. and Suzuki, H., Funtai-Oyabi-Fummatsu-Yakin-Journal of the Japan Society of Powder and Powder Metallurgy, 44 (1), 102 (1997).CrossRefGoogle Scholar