Room-temperature gelcasting of alumina with a water-soluble copolymer

Published online by Cambridge University Press:  22 May 2013

Yan Yang
Affiliation:
R&D Center for Structural Ceramics and Composites, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai, People’s Republic of China, 200050
Shunzo Shimai
Affiliation:
R&D Center for Structural Ceramics and Composites, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai, People’s Republic of China, 200050
Shiwei Wang*
Affiliation:
R&D Center for Structural Ceramics and Composites, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai, People’s Republic of China, 200050
*
a)Address all correspondence to this author. e-mail: [email protected]
Get access

Abstract

A novel and simple method for gelcasting of alumina was developed using a nontoxic and water-soluble copolymer of isobutylene and maleic anhydride (commercially called Isobam). In this method, there is requirement of only a small amount of Isobam (0.3 wt%) and neither initiators nor dispersants are needed for preparation and gelation of a 50 vol% solids loaded alumina slurry. The gelation rate increased with increasing solids loading but decreased with increasing Isobam content. A typical gelation time was 38 min for the slurry containing 50 vol% solids loading and 0.3 wt% Isobam. The resultant wet gel was strong enough to allow reversible bending and twisting. This simple gelling system is attractive for wet forming of ceramics because only a single additive, which acts as both dispersant and gelling agent at room temperature in air, is used.

Type
Articles
Copyright
Copyright © Materials Research Society 2013 

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

Omatete, O.O., Janney, M.A., and Strehlow, R.A.: Gelcasting - a new ceramic forming process. Am. Ceram. Soc. Bull. 70(10), 1641 (1991).Google Scholar
Takeshita, M. and Kurita, S.: Development of self-hardening slip casting. J. Eur. Ceram. Soc. 17(2–3), 415 (1997).CrossRefGoogle Scholar
Mao, X.J., Shimai, S., Dong, M.J., and Wang, S.W.: Gelcasting of alumina using epoxy resin as gelling agent. J. Am. Ceram. Soc. 90(3), 986 (2007).CrossRefGoogle Scholar
Mao, X.J., Shimai, S., Dong, M.J., and Wang, S.W.: Gelcasting and pressureless sintering of translucent alumina ceramics. J. Am. Ceram. Soc. 91(5), 1700 (2008).CrossRefGoogle Scholar
Park, J.K., Lee, J.S., and Lee, S.I.: Preparation of porous cordierite using gelcasting method and its feasibility as a filter. J. Porous Mater. 9(3), 203 (2002).CrossRefGoogle Scholar
Mao, X.J., Shimai, S., and Wang, S.W.: Gelcasting of alumina foams consolidated by epoxy resin. J. Eur. Ceram. Soc. 28(1), 217 (2008).CrossRefGoogle Scholar
Morissette, S.L. and Lewis, J.A.: Chemorheoloy of aqueous-based alumina-poly(vinyl alcohol) gelcasting suspensions. J. Am. Ceram. Soc. 82(3), 521 (1999).CrossRefGoogle Scholar
Chabert, F., Dunstan, D.E., and Franks, G.V.: Cross-linked polyvinyl alcohol as a binder for gelcasting and green machining. J. Am. Ceram. Soc. 91(10), 3138 (2008).CrossRefGoogle Scholar
Hansen, E.W., Holm, K.H., Jahr, D.M., Olafsen, K., and Stori, A.: Reaction of poly(vinyl alcohol) and dialdehydes during gel formation probed by 1H n.m.r. - a kinetic study. Polymer 38(19), 4863 (1997).CrossRefGoogle Scholar
Johnson, S.B., Franks, G.V., and Dunstan, D.E.: A novel thermally activated crosslinking agent for chitosan in aqueous solution: A rheological investigation. Colloid Polym. Sci. 282(6), 602 (2004).CrossRefGoogle Scholar
Tallon, C., Jach, D., Moreno, R., Nieto, M.I., Rokicki, G., and Szafran, M.: Gelcasting of alumina suspensions containing nanoparticles with glycerol monoacrylate. J. Am. Ceram. Soc. 29, 875 (2009).CrossRefGoogle Scholar
Bednarek, P., Szafran, M., Sakka, Y., and Mizerski, T.: Gelcasting of alumina with a new monomer synthesized from glucose. J. Eur. Ceram. Soc. 30, 1795 (2010).CrossRefGoogle Scholar
Fanelli, A.J., Silvers, R.D., Frei, W.S., Burlew, J.V., and Marsh, G.B.: New aqueous injection moulding process for ceramic powder. J. Am. Ceram. Soc. 72(10), 1833 (1989).CrossRefGoogle Scholar
Jia, Y., Kanno, Y., and Xie, Z.P.: Fabrication of alumina green body through gelcasting process using alginate. Mater. Lett. 57(16–17), 2530 (2003).CrossRefGoogle Scholar
Lyckfeldt, O., Brandt, J. and Lesca, S.: Protein forming – a novel shaping technique for ceramics. J. Eur. Ceram. Soc. 20(14–15), 2551 (2000).CrossRefGoogle Scholar
Adolfsson, E.: Gelcasting of zirconia using agarose. J. Am. Ceram. Soc. 89(6), 1897 (2006).CrossRefGoogle Scholar
Chen, Y.L., Xie, Z.P., and Huang, Y.: Alumina casting based on gelation of gelatine. J. Eur. Ceram. Soc. 19(2), 271 (1999).CrossRefGoogle Scholar
Mao, X.J., Wang, S.W., and Shimai, S.: Porous ceramics with tri-modal pores prepared by foaming and starch consolidation. Ceram. Int. 34(1), 217 (2008).CrossRefGoogle Scholar
Israelachvili, J.N.: Intermolecular and Surface Forces, 2nd ed. (Academic Press Ltd., London, 1992), pp 280.Google Scholar
Tallon, C. and Franks, G.V.: Recent trends in shape forming from colloidal processing: A review. J. Ceram. Soc. Jpn. 119(3), 147 (2011).CrossRefGoogle Scholar