Rheology of aqueous boehmite-coated silicon nitride suspensions and gels

Published online by Cambridge University Press:  03 March 2011

Wei-Heng Shih  and
Leh-Lii Pwu
Wei-Heng Shih
Affiliation:
Department of Materials Engineering, Drexel University, Philadelphia, Pennsylvania 19104
Leh-Lii Pwu
Affiliation:
Department of Materials Engineering, Drexel University, Philadelphia, Pennsylvania 19104
Get access

Abstract

The rheological properties of boehmite-coated silicon nitride aqueous suspensions and gels are reported. In unidirectional rheological tests, it was found that the boehmite coating reduces the viscosity of the suspensions over a wide range of shear rates and volume fractions of particles. The suspension shear stress as a function of shear rate can be described by the Bingham model, and the Bingham yield stresses of boehmite-coated silicon nitride suspensions are lower than those of the uncoated suspensions. The reduction in the viscosity and the Bingham yield stress is attributed to a shallower secondary minimum in the Derjaguin-Landau-Verwey-Overbeek (DLVO) potential between coated particles than that for uncoated silicon nitride particles. Moreover, at low values of pH, the coated silicon nitride suspensions gelled over time, and the viscoelastic behavior of the gels was studied by dynamic oscillatory tests. It was found that the shear modulus (G′) and loss modulus (G″) remain constant up to a certain strain amplitude, γ°, beyond which G′ and G″ begin to vary. The value of G′ in the linear region increases exponentially, whereas γ° decreases exponentially with the volume fraction of coated silicon nitride particles. The exponential behavior of the shear modulus G′ of the gels is similar to the exponential pressure-density relationship found in the previous pressure filtration study, indicating that particulate rearrangement occurs as volume fraction of particles is increased.

Type
Articles
Information
Journal of Materials Research , Volume 10 , Issue 11 , November 1995 , pp. 2808 - 2816
Copyright
Copyright © Materials Research Society 1995

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1Yamada, T., Am. Ceram. Soc. Bull. 72 (5) (1993).Google Scholar
2Mah, T-I., Mazdiyasni, K. S., and Run, R., Am. Ceram. Soc. Bull. 58 (9), 840 (1979).Google Scholar
3Shaw, T. M. and Pethica, R. A., J. Am. Ceram. Soc. 69 (2), 88 (1986).CrossRefGoogle Scholar
4Garg, A. K. and De Jonghe, L.C., J. Mater. Res. 5, 136–142 (1990).CrossRefGoogle Scholar
5Malghan, S.G., Pei, P.T., and Wang, P. S., Ceram. Eng. & Sci. Proc. 12 (9–10), 2115–2123 (1991).CrossRefGoogle Scholar
6Liden, E., Persson, M., Carlstrom, E., and Carlsson, R., J. Am. Ceram. Soc. 74 (6), 1335 (1991).CrossRefGoogle Scholar
7Shih, W-H., Pwu, L-L., and Tseng, A. A., J. Am. Ceram. Soc. 78 (5), 1252–1260 (1995).CrossRefGoogle Scholar
8Shih, W-H., Kim, S.I., Shih, W.Y., Liu, J., and Aksay, I. A., Phys. Rev. A 42, 4772 (1990).CrossRefGoogle Scholar
9Pierre, A. C. and Uhlmann, D. R. in Better Ceramics Through Chemistry II, edited by Brinker, C. J., Clark, D. E., and Ulrich, D. R., Mater. Res. Soc. Symp. Proc. 73, Pittsburgh, PA, 1986), p. 481.Google Scholar
10van Olphen, H., Introduction to Clay Colloidal Chemistry (John Wiley, New York, 1980).Google Scholar
11See for example, Void, R. D. and Void, M. J., Colloid and Interface Chemistry (Addison-Wesley, Reading, MA, 1983).Google Scholar
12Weltmann, R.N. and Green, H., J. Appl. Phys. 14, 569 (1943).CrossRefGoogle Scholar
13Buscall, R., McGowan, I. J., and Mumme-Young, C.A., Faraday Discuss. Chem. Soc. 90, 1 (1990).CrossRefGoogle Scholar
14Yoldas, B.E., Am. Ceram. Soc. Bull. 54, 289 (1975).Google Scholar
15Krieger, I.M. and Dougherty, T.J., Trans Soc. Rheol. III, 137 (1959).CrossRefGoogle Scholar
16Green, T.M. and Akinc, M., Am. Ceram. Soc. Bull. 70 (7), 1162 (1991).Google Scholar
17Bingham, E. C., Fluidity and Plasticity (McGraw-Hill, New York, 1922), or see, for example, Bird, R. B., Armstrong, R. C., and Hassager, O., Dynamics of Polymeric Liquids (1977).Google Scholar
18Bergstrom, L., Surface Characterization of Silicon Nitride and Consolidation of Flocculated Suspensions, Ph.D. Thesis, The Royal Institute of Technology in Sweden (1992).Google Scholar
19Prieve, D.C. and Russel, W.B., J. Colloid Interf. Sci. 125, 1 (1988).CrossRefGoogle Scholar
20Shih, W-H., Liu, J., Shih, W. Y., Kim, S. I., Sarikaya, M., and Aksay, I. A., in Processing Science of Advanced Ceramics, edited by Aksay, I. A., McVay, G.L., and Ulrich, D.R. (Mater. Res. Soc. Symp. Proc. 155, Pittsburgh, PA, 1989), p. 83.Google Scholar
21Sonntag, R.C. and Russel, W.B., J. Colloid Interf. Sci. 116, 485 (1987).CrossRefGoogle Scholar
22Dietler, G., Aubert, C., Cannell, D. S., and Wiltzius, P., Phys. Rev. Lett. 57, 3117 (1986).CrossRefGoogle Scholar
23Shih, W. Y., Liu, J., Shih, W-H., and Aksay, I. A., J. Stat. Phys. 62, 961 (1991).CrossRefGoogle Scholar
24Shih, W. Y., Shih, W-H., and Aksay, A., in Physical Phenomena in Granular Materials, edited by Cody, G. D., Geballe, T. N., and Sheng, P. (Mater. Res. Soc. Symp. Proc. 195, Pittsburgh, PA, 1990), p. 477.Google Scholar
25Goodwin, J.W., Am. Ceram. Soc. Bull. 69 (10), 1694 (1990).Google Scholar
26Russel, W.B., J. Rheo. 24 (3), 287 (1980).CrossRefGoogle Scholar