Processing tetramethylammonium-carbonate-coprecipitated slurries to obtain small-particle-size YBa2Cu3O7

Published online by Cambridge University Press:  31 January 2011

Nicholas D. Spencer ,
Thorvald S. Peders  and
Matthew B. Baer
Nicholas D. Spencer
Affiliation:
W.R. Grace & Co.-Conn. Research Division, 7379 Route 32, Columbia, Maryland 21044
Thorvald S. Peders
Affiliation:
W.R. Grace & Co.-Conn. Research Division, 7379 Route 32, Columbia, Maryland 21044
Matthew B. Baer
Affiliation:
W.R. Grace & Co.-Conn. Research Division, 7379 Route 32, Columbia, Maryland 21044
Get access

Abstract

The effect of different drying and calcination methods on the ultimate particle size of YBa2Cu3O7 (Y-123) has been investigated. The starting material was a tetramethylammonium (TMA) carbonate-precipitated slurry. Spray-drying the slurry after filtering and reslurrying (to remove residual TMA) was most effective in the ultimate formation of finely divided Y-123. The morphology of the spray-dried powder could be preserved by calcining in very low total pressures of flowing oxygen. When a slurry with 0.16% solids content was spray dried, and this powder calcined at 750 °C in 2 Torr of flowing oxygen, a Y-123 powder of mean particle size 0.74 μm (66% submicron) was obtained.

Type
Articles
Information
Journal of Materials Research , Volume 6 , Issue 2 , February 1991 , pp. 220 - 226
Copyright
Copyright © Materials Research Society 1991

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1Ginley, D. S., Mitchell, M. A., Kwak, J. F., Venturini, E. L., Baughman, R. J., and Fu, W., J. Mater. Res. 4, 501 (1989).CrossRefGoogle Scholar
2Kwak, J. F., Ginley, D. S., Venturini, E. L., Morosin, B., Baughman, R. J., Barbour, J. C., and Eatough, M. O., in Studies of High-Temperature Superconductors, edited by Narlikar, A. V. (Nova Science Publishers, Commack, New York, in press).Google Scholar
3Spencer, N. D., Pan, W. H., and Rudesill, J. A., Eur. Patent Applic. 0306973, 1988.Google Scholar
4Bunker, B. C., Lamppa, D. L., and Voigt, J. A., Patent, U. S. 4 839 339, 1989.Google Scholar
5Bunker, B. C., Voight, J. A., Lamppa, D. L., Doughty, D., Venturini, E. L., Kwak, F. J., Ginley, D. S., Headley, T. J., Harrington, M. S., Eatough, M. O., Tissot, R. G., and Hammetter, W. F., in Better Ceramics Through Chemistry III, edited by Brinker, C. J., Clark, D. E., and Ulrich, D. R. (Mater. Res. Soc. Symp. Proc. 121, Pittsburgh, PA, 1988), pp. 373–384.Google Scholar
6Spencer, N. D., Chemistry of Materials (in press).Google Scholar
7Balachandran, U., Poeppel, R. B., Emerson, J. E., Johnson, S. A., Lanagan, M. T., Youngdahl, C. A., Shi, D., Goretta, K. C., and Eror, N. G., Mater. Lett. 8, 454 (1989).CrossRefGoogle Scholar
8Dolhert, L. E., Grace, W. R. & Co.-Conn., Research Division, personal communication, 1989.Google Scholar