Preparation of barium titanate ceramics from amorphous fine particles of the Ba–Ti–O system and its dielectric properties

Published online by Cambridge University Press:  03 March 2011

S. Wada
Affiliation:
Department of Applied Chemistry, Tokyo University of Agriculture and Technology, 24–16, Nakamachi 2-chome, Koganei, Tokyo 184, Japan
T. Suzuki
Affiliation:
Department of Applied Chemistry, Tokyo University of Agriculture and Technology, 24–16, Nakamachi 2-chome, Koganei, Tokyo 184, Japan
T. Noma
Affiliation:
Department of Applied Chemistry, Tokyo University of Agriculture and Technology, 24–16, Nakamachi 2-chome, Koganei, Tokyo 184, Japan
Get access

Abstract

Using titanium nitrate solution stabilized by chelation, amorphous fine particles of the Ba-Ti-O system were prepared by the mist decomposition method in air. After calcination of these particles, barium titanate ceramics were prepared using the hot uniaxial pressing method, and various properties were investigated. As a result, the grain sizes could be controlled over the range from 58 nm to 187 nm by the sintering temperatures and/or the calcination temperatures, keeping the density almost constant. Moreover, the dielectric properties of the samples showed that the relative permittivity decreased with decreasing grain size, and Curie temperature also shifted to lower temperatures in the same way. In this study, we first found that Curie temperature existed in the barium titanate ceramics with grain sizes from 58 to 147 nm.

Type
Articles
Copyright
Copyright © Materials Research Society 1995

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1Kinoshita, K. and Yamaji, A., J. Appl. Phys. 47, 371 (1976).Google Scholar
2Arlt, G., Hennings, D., and de With, G., J. Appl. Phys. 58, 1619 (1985).CrossRefGoogle Scholar
3Fang, T-T., Hsieh, H-L., and Shiau, F-S., J. Am. Ceram. Soc. 76, 1205 (1993).Google Scholar
4Uchino, K., Sadanaga, E., and Hirose, T., J. Am. Ceram. Soc. 72, 1555 (1989).Google Scholar
5Uchino, K., Sadanaga, E., Oonishi, K., Morohashi, T., and Yamamura, H., in Ceramic Dielectrics–Ceramic Transactions (American Ceramic Society, Westerville, OH, 1990), Vol. 8, p. 107.Google Scholar
6Samara, G. A., Phys. Rev. 151, 378 (1966).CrossRefGoogle Scholar
7Wada, S., Suzuki, T., and Noma, T., J. Mater. Sci. Lett. 13, 190 (1994).Google Scholar
8Imai, H., Takami, K., and Naito, M., Mater. Res. Bull. XIX, 1293 (1984).CrossRefGoogle Scholar
9Ishizawa, H., Sakurai, O., Mizutani, N., and Kato, M., Am. Ceram. Soc. Bull. 65, 1399 (1986).Google Scholar
10Papet, P., Dougherty, J. P., and Shrout, T. R., J. Mater. Res. 5, 2902 (1990).Google Scholar
11Vivekanandan, R., Philip, S., and Kutty, T. R. N., Mater. Res. Bull. XXII, 99 (1986).Google Scholar
12Hennings, D. and Schreinemacher, S., J. Euro. Ceram. Soc. 9, 41 (1992).CrossRefGoogle Scholar
13Oonishi, K., Morohashi, T., and Uchino, K., J. Jpn. Ceram. Soc. 97, 473 (1989).CrossRefGoogle Scholar
14Arlt, G., Ferroelectrics 76, 451 (1987).CrossRefGoogle Scholar