Nanomechanical properties of sub-10 nm carbon film overcoats using the nanoindentation technique

Published online by Cambridge University Press:  03 March 2011

Chang-Dong Yeo ,
Andreas A. Polycarpou ,
James D. Kiely  and
Yiao-Tee Hsia
Chang-Dong Yeo
Affiliation:
Department of Mechanical Science and Engineering, University of Illinois at Urbana-Champaign, Urbana, Illinois 61801
Andreas A. Polycarpou*
Affiliation:
Department of Mechanical Science and Engineering, University of Illinois at Urbana-Champaign, Urbana, Illinois 61801
James D. Kiely
Affiliation:
Seagate Research, Pittsburgh, Pennsylvania 15222
Yiao-Tee Hsia
Affiliation:
Seagate Research, Pittsburgh, Pennsylvania 15222
*
a) Address all correspondence to this author. e-mail: [email protected]
Get access

Abstract

The hardness and elastic modulus of ultra thin amorphous carbon overcoat (COC) films were measured using a recently developed sub-nm nanoindentation system. The carbon overcoat film thickness was varied to be 2.5 nm, 5 nm, and 10 nm on a glass substrate with a 2 nm titanium interlayer. A very sharp indenting tip, which was a cube corner tip with a radius of 44 nm, was used for the experiments. It was found that the mechanical properties of sub-10 nm film thicknesses can be reliably measured using the sub-nm indentation system and a sharp indenting tip. As the thickness of the carbon overcoat increased, so too did the surface roughness. For all three film thickness samples, the trends of hardness and elastic modulus values with the contact depth are very similar. When the contact depth is smaller than the film thickness, the measured values of hardness and elastic modulus are higher than those of the glass substrate, and gradually decrease and then approach the values of glass substrate. When the contact depth is larger than the film thickness, the measured values approximate those of the glass substrate. The thinner film shows higher values of hardness and elastic modulus near the surface, which indicates that mechanical properties do change with film thickness and that measurements made on thicker films and extrapolated to thinner films may lead to incorrect conclusions.

Keywords

Elastic propertiesHardnessNanoscale
Type
Articles
Information
Journal of Materials Research , Volume 22 , Issue 1 , January 2007 , pp. 141 - 151
Copyright
Copyright © Materials Research Society 2007

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1Yamamoto, T., Kasamatsu, Y., and Hyodo, H.: Advanced stiction-free slider and DLC overcoat. FUJITSU Sci. Tech. J. 37(2), 201 (2001).Google Scholar
2Chaudhari, P.: Information technology: A play of materials. MRS Bull. 27(7), 55 (2000).Google Scholar
3Bhushan, B. and Li, X.: Nanomechanical characterization of solid surfaces and thin films. Int. Mater. Rev. 48(3), 125 (2003).Google Scholar
4Charitidis, C. and Logothetidis, S.: Nanomechanical and nanotribological properties of carbon based films. Thin Solid Films 482, 120 (2005).Google Scholar
5Lemoine, P., Zhao, J.F., Quinn, J.P., McLaughlin, J.A., and Maguire, P.: Hardness measurements at shallow depths on ultra-thin amorphous carbon films deposited onto silicon and Al2O3-TiC substrates. Thin Solid Films 379, 166 (2000).CrossRefGoogle Scholar
6Doerner, M.F. and Nix, W.D.: A method for interpreting the data from depth-sensing indentation instruments. J. Mater. Res. 1, 601 (1986).Google Scholar
7Oliver, W.C. and Pharr, G.M.: An improved technique for determining hardness and elastic modulus using load and displacement sensing indentation experiments. J. Mater. Res. 7, 1564 (1992).Google Scholar
8Cheng, Y. and Cheng, C.: Scaling approach to conical indentation in elastic-plastic solids with work hardening. J. Appl. Phys. 84, 1284 (1998).Google Scholar
9Kohzaki, M., Matsumuro, A., Hayashi, T., Muramatsu, M., and Yamaguchi, K.: Preparation of carbon nitride thin films by ion-beam-assisted deposition and their mechanical properties. Thin Solid Films 308–309, 239 (1997).Google Scholar
10Scharf, T.W., Deng, H., and Barnard, J.A.: Nanowear/nanomechanical testing and the role of stress in sputtered CNx overcoats. J. Appl. Phys. 81(8), 5393 (1997).Google Scholar
11Xu, Z. and Rowcliffe, D.: Finite element analysis of substrate effects on indentation behaviour of thin films. Thin Solid Films 447–448, 399 (2004).Google Scholar
12Buckle, H.: The Science of Hardness Testing and Its Research Applications (American Society for Metals, Metals Park, OH, 1973), pp. 453.Google Scholar
13Logothetidis, S.: Surface and interface properties of amorphous carbon layers on rigid and flexible substrates. Thin Solid Films 482, 9 (2005).Google Scholar
14Yu, N., Bonin, W.A., and Polycarpou, A.A.: High-resolution capacitive load-displacement transducer and its application in nanoindentation and adhesion force measurements. Rev. Sci. Instrum. 76, 045109 (2005).Google Scholar
15Anoikin, E.V., Yang, M.M., Chao, J.L., and Russak, M.A.: Magnetic hard disk overcoats in the 3–5 nm thickness range. J. Appl. Phys. 85(8), 5606 (1999).Google Scholar
16Grannen, K.J., Ma, X., and Thangaraj, R.: Ion beam deposition of carbon overcoats for magnetic thin film media. IEEE Trans. Magn. 36(1), 120 (2000).Google Scholar
17Chudoba, T. and Richter, F.: Investigation of creep behaviour under load during indentation experiments and its influence on hardness and modulus results. Surf. Coat. Technol. 148, 191 (2001).Google Scholar
18Oliver, W.C. and Pharr, G.M.: Measurement of hardness and elastic modulus by instrumented indentation: Advances in understanding and refinements to methodology. J. Mater. Res. 19(1), 3 (2004).Google Scholar
19Butterworth, S.: On the theory of filter amplifiers. Wireless Engineer. 7, 536 (1930).Google Scholar
20Stout, K.J., Sullivan, P.J., Dong, W.P., Mainsah, E., Lou, N., Mathia, T., and Zahouani, H.: The Development of Methods for the Characterization of Roughness in Three Dimension (Commission of the European Communities, Printed in Univ. of Birmingham, Report EUR 15178 EN, 1993).Google Scholar
21Suh, A.Y. and Polycarpou, A.A.: Effect of molecularly thin lubricant on roughness and adhesion of magnetic disks intended for extremely high-density recording. Tribol. Lett. 15(4), 365 (2003).CrossRefGoogle Scholar
22Mbise, G.W., Niklasson, G.A., and Granqvist, C.G.: Scaling of surface roughness in evaporated calcium fluoride films. Solid State Comm. 97(11), 965 (1996).Google Scholar
23Nanda, K.K., Sarangi, S.N., and Sahu, S.N.: Measurement of surface roughness by atomic force microscopy and Rutherford backscattering spectrometry of CdS nanocrystalline films. Appl. Surf. Sci. 133, 293 (1998).CrossRefGoogle Scholar
24Yang, H.N., Zhao, Y.P., Wang, G.C., and Lu, T.M.: Noise-induced roughening evolution of amorphous Si films grown by thermal evaporation. Phys. Rev. Lett. 76(20), 3774 (1996).Google Scholar
25Liu, Z.J., Jiang, N., Shen, Y.G., and Mai, Y.W.: Atomic force microscopy study of surface roughening of sputter-deposited TiN thin films. J. Appl. Phys. 92(7), 3559 (2002).Google Scholar
26Family, F. and Vicsek, T.: Scaling of the active zone in the Eden process on percolation networks and the ballistic deposition model. J. Phys. A 18, L75 (1985).Google Scholar
27Schwoebel, R.L. and Shipsey, E.J.: Step motion on crystal surfaces. Appl. Phys. 37, 3682 (1966).Google Scholar
28Schwoebel, R.L.: Step motion on crystal surfaces. II. J. Appl. Phys. 40, 614 (1968).Google Scholar
29Villain, J.: Continuum models of crystal growth from atomic beams with and without desorption. J. Phys. (France) I 1, 19 (1991).Google Scholar
30Siegert, M. and Plischke, M.: Slope selection and coarsening in molecular beam epitaxy. Phys. Rev. Lett. 73, 1517 (1994).Google Scholar
31Bull, S.J. and Korsunsky, A.M.: Mechanical properties of thin carbon overcoats. Tribol. Int. 31(9), 547 (1998).Google Scholar
32Lichinchi, M., Lenardi, C., Haugt, J., and Vitali, K.: Simulation of Berkovich nanoindentation experiments on thin films using finite element method. Thin Solid Films 312, 240 (1998).Google Scholar
33Xu, Z. and Rowcliffe, D.: Nanoindentation on diamond-like carbon and alumina coatings. Surf. Coat. Technol. 161, 44 (2002).Google Scholar
34Monteiro, O.R.: Thin film synthesis by energetic condensation. Annu. Rev. Mater. Res. 31, 111 (2001).Google Scholar
35Lifshitz, Y.: Diamondlike carbon—present status. Diamond Rel. Mater. 8, 1659 (1999).CrossRefGoogle Scholar
36Veprek, S. and Argon, A. S.: Mechanical properties of superhard nanocomposites. Surf. Coat. Technol. 146–147, 175 (2001).Google Scholar
37Montgomery, D.C.: Design and Analysis of Experiments, 5th ed. (John Wiley & Sons, New York, 2001), p. 96.Google Scholar