Microstructure and electrical properties of 0.5PZN-0.5PZT relaxor ferroelectrics close to the morphotropic phase boundary

Published online by Cambridge University Press:  31 January 2011

Lu-Yang Zhao ,
Yu-Dong Hou ,
Li-Min Chang ,
Man-Kang Zhu  and
Hui Yan
Yu-Dong Hou*
Affiliation:
Department of Materials Science and Engineering, Beijing University of Technology, Beijing 100124, China
Hui Yan
Affiliation:
Department of Materials Science and Engineering, Beijing University of Technology, Beijing 100124, China
*
a) Address all correspondence to this author. e-mail: [email protected]
Get access

Abstract

Relaxor ferroelectrics of Pb(Zn1/3Nb2/3)0.5(Zr0.47Ti0.53)0.5O3 (0.5PZN-0.5PZT) were prepared using the conventional oxide mixing method. Both x-ray diffraction analysis and Raman spectroscopy indicate that the amounts of rhombohedral phase are close to tetragonal phase, implying the presence of the morphotropic phase boundary (MPB) in the system of 0.5PZN-0.5PZT, and this result was further confirmed by transmission electron microscopy (TEM) micrographs. At MPB composition, the excellent piezoelectric properties, such as kp (0.66) and d33 (425pC/N), were obtained due to the more possible polarization directions of domains and high dc resistivity of 6.5 × 1010 Ω·cm. Meanwhile, the dielectric studies revealed that the indicator of the degree of diffuseness γ value is 1.73, implying that the relaxor nature of the 0.5PZN-0.5PZT is ceramic. The activation energy related to the dc conductivity was estimated from a linear fitting of the Arrhenius law. The value of 0.09 and 1.04 eV for low and high temperature range corresponds well to the activation energies of migration and first ionization of the oxygen vacancies.

Keywords

CeramicDielectric propertiesFerroelectric
Type
Articles
Information
Journal of Materials Research , Volume 24 , Issue 6 , June 2009 , pp. 2029 - 2034
Copyright
Copyright © Materials Research Society 2009

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1Cross, L.E.: Relaxor ferroelectrics. Ferroelectrics 76, 241 (1987).CrossRefGoogle Scholar
2Shrout, T.R. and Halliyal, A.: Preparation of lead-based ferroelectric relaxors for capacitors. Am. Ceram. Soc. Bull. 66, 704 (1987).Google Scholar
3Wakiya, N., Ishizawa, N., Shinozaki, K., and Mizutani, N.: Thermal stability of Pb(Zn1/3Nb2/3)O3 (PZN) and consideration of stabilization conditions of perovskite type compounds. Mater. Res. Bull. 30, 1121 (1995).CrossRefGoogle Scholar
4Yamashita, Y.: Large electromechanical-coupling factors in perovskite binary material system. Jpn. J. Appl. Phys. 33, 5328 (1994).CrossRefGoogle Scholar
5Fan, H.Q. and Kim, H.E.: Perovskite stabilization and electromechanical properties of polycrystalline lead zinc niobate-lead zirconate titanate. J. Appl. Phys. 91, 317 (2002).CrossRefGoogle Scholar
6Fan, H.Q., Jie, W.Q., Tian, C.S., Zhang, L.T., and Kim, H.E.: Domain morphology and field-induced phase transition in “two phase zone” of PZN-based ferroelectrics. Ferroelectrics 269, 33 (2002).CrossRefGoogle Scholar
7Fan, H.Q., Park, G.T., Choi, J.J., Ryu, J., and Kim, H.E.: Preparation and improvement in the electrical properties of lead-zinc-niobate–based ceramics by thermal treatments. J. Mater. Res. 17, 180 (2002).CrossRefGoogle Scholar
8Chang, L.M., Hou, Y.D., Zhu, M.K., and Yan, H.: Effect of sintering temperature on the phase transition and dielectrical response in the relaxor-ferroelectric-system 0.5PZN–0.5PZT. J. Appl. Phys. 101, 034101 (2007).CrossRefGoogle Scholar
9Hou, Y.D., Chang, L.M., Zhu, M.K., Song, X.M., and Yan, H.: Effect of Li2CO3 addition on the dielectric and piezoelectric responses in the low-temperature sintered 0.5PZN–0.5PZT systems. J. Appl. Phys. 102, 084507 (2007).CrossRefGoogle Scholar
10Dutta, S., Choudhary, R.N.P., and Sinha, P.K.: Synthesis and characterization of double-doped PZT piezoceramics. Proc. SPIE Int. Soc. Opt. Eng. 5062, 190 (2003).Google Scholar
11Souza, A.G. Filho, Lima, K.C.V., Ayala, A.P., Guedes, I., Freire, P.T.C., Melo, F.E.A.,Filho, J. Mendes, Araújo, E.B., and Eiras, J.A.: Raman scattering study of the PbZr1-xTixO3 system: Rhombohedralmonoclinic-tetragonal phase transitions. Phys. Rev. B: Condens. Matter 66, 132107 (2002).CrossRefGoogle Scholar
12Zhu, M.K., Lu, P.X., Hou, Y.D., Song, X.M., Wang, H., and Yan, H.: analysis of phase coexistence in Fe2O3-doped 0.2PZN–0.8PZT ferroelectric ceramics by Raman scattering spectra. J. Am. Ceram. Soc. 89, 3739 (2006).CrossRefGoogle Scholar
13Cohen, R.E.: Origin of ferroelectricity in perovskite oxides. Nature 358, 136 (1992).CrossRefGoogle Scholar
14Guo, R., Cross, L.E., Park, S.E., Noheda, B., Cox, D.E., and Shirane, G.: Origin of the high piezoelectric response in PbZr1-x TixO3. Phys. Rev. Lett. 84, 5423 (2000).CrossRefGoogle Scholar
15Noheda, B., Gonzalo, J.A., Cross, L.E., Guo, R., Park, S.E., Cox, D.E., and Shirane, G.: Tetragonal-to-monoclinic phase transition in a ferroelectric perovskite: The structure of PbZr0.52 Ti0.48O3. Phys. Rev. B: Condens. Matter 61, 8687 (2000).CrossRefGoogle Scholar
16Yoon, C.B., Lee, S.H., Lee, S.M., and Kim, Hyoun-Ee: Co-firing of PZN-PZT flextensional actuators. J. Am. Ceram. Soc. 87, 1663 (2004).CrossRefGoogle Scholar
17Yoon, C.B., Park, G.T., Kim, H.E., and Ryu, J.: Piezoelectric ultrasonic motor by co-extrusion process. Sens. Actuators, A 121, 515 (2005).CrossRefGoogle Scholar
18Uchino, K. and Nomura, S.: Critical exponents of the dielectric constants in diffused-phase transition crystals. Ferroelectr. Lett. 44, 55 (1982).CrossRefGoogle Scholar
19Ang, C., Yu, Z., and Cross, L.E.: Oxygen-vacancy-related low-frequency dielectric relaxation and electrical conduction in Bi: SrTiO3. Phys. Rev. B: Condens. Matter 62, 228 (2002).CrossRefGoogle Scholar
20Deng, G.C., Li, G.R., Ding, A.L., and Yin, Q.R.: Evidence for oxygen vacancy inducing spontaneous normal-relaxor transition in complex perovskite ferroelectrics. Appl. Phys. Lett. 87, 192505 (2005).CrossRefGoogle Scholar