Mechanism of electromigration-induced failure in flip-chip solder joints with a 10-μm-thick Cu under-bump metallization

Published online by Cambridge University Press:  03 March 2011

Jae-Woong Nah ,
Kai Chen ,
K.N. Tu ,
Bor-Rung Su  and
Chih Chen
Jae-Woong Nah*
Affiliation:
Department of Materials Science and Engineering, University California at Los Angeles, Los Angeles, California 90095-1595
Kai Chen
Affiliation:
Department of Materials Science and Engineering, University California at Los Angeles, Los Angeles, California 90095-1595
K.N. Tu
Affiliation:
Department of Materials Science and Engineering, University California at Los Angeles, Los Angeles, California 90095-1595
Bor-Rung Su
Affiliation:
Department of Materials Science and Engineering, National Chiao Tung University, Taiwan 30050, People’s Republic of China
Chih Chen
Affiliation:
Department of Materials Science and Engineering, National Chiao Tung University, Taiwan 30050, People’s Republic of China
*
a)Address all correspondence to this author. e-mail: [email protected]
Get access

Abstract

The electromigration-induced failure in flip-chip eutectic SnPb solder joints with a 10-μm-thick Cu under-bump metallization (UBM) was studied without the effect of current crowding in the solder region. The current crowding occurred inside the UBM instead of in the solder joint at the current density of 3.0 × 104 A/cm2 because of the spreading of current in the very thick Cu UBM. In these joints, the failure occurred through a two-stage consumption of the thick Cu UBM in the joint where electrons flowed from the chip to the substrate. In the first stage, the Cu UBM dissolved layer by layer rather uniformly across the entire Cu UBM–solder interface. In the second stage, after half of the Cu UBM was dissolved, an asymmetrical dissolution of Cu UBM took place at the corner where electrons entered from the Al interconnect to the Cu UBM. Experimental observation of dissolution steps of the 10-μm-thick Cu UBM is presented. The transition from the first stage to the second stage has been found to depend on the location of current crowding in the flip-chip joints as the UBM thickness changes during the electromigration test. The current distribution in the flip-chip solder joints as a function of UBM thickness was simulated by three-dimensional finite element analysis. The dissolution rate of Cu UBM in the second stage was faster than that in the first stage. The mechanism of electromigration-induced failure in the flip-chip solder joints with a 10-μm-thick Cu UBM is discussed.

Keywords

ElectromigrationPackagingSoldering
Type
Articles
Information
Journal of Materials Research , Volume 22 , Issue 3 , March 2007 , pp. 763 - 769
Copyright
Copyright © Materials Research Society 2007

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

Article purchase

Temporarily unavailable

References

REFERENCES

1John, H.: Lau, Flip Chip Technology (McGraw-Hill, New York, 1996), p. 123.Google Scholar
2Kim, H.K., Tu, K.N., and Totta, P.A.: Ripening-assisted asymmetric spalling of Cu–Sn compound spheroids in solder joints on Si wafers. Appl. Phys. Lett. 68, 2204 (1996).CrossRefGoogle Scholar
3Liu, A.A., Kim, H.K., Tu, K.N., and Totta, P.A.: Spalling of Cu6Sn5 spheroids in the soldering reaction of eutectic SnPb on Cr/Cu/Au thin films. J. Appl. Phys. 80, 2774 (1996).CrossRefGoogle Scholar
4Liu, C.Y., Kim, H.K., Tu, K.N., and Totta, P.A.: Dewetting of molten Sn on Au/Cu/Cr thin-film metallization. Appl. Phys. Lett. 69, 4014 (1996).CrossRefGoogle Scholar
5Lee, T.Y., Choi, W.J., Tu, K.N., Jang, J.W., Kuo, S.M., Lin, J.K., Frear, D.R., Zeng, K., and Kivilahti, J.K.: Morphology, kinetics, and thermodynamics of solid-state aging of eutectic SnPb and Pb-free solders (Sn-3.5Ag, Sn-3.8Ag-0.7Cu and Sn-0.7Cu) on Cu. J. Mater. Res. 17, 291 (2002).CrossRefGoogle Scholar
6Nah, J.W., Paik, K.W., Suh, J.O., and Tu, K.N.: Mechanism of electromigration-induced failure in the 97Pb-3Sn and 37Pb-63Sn composite solder joints. J. Appl. Phys. 94, 7560 (2003).CrossRefGoogle Scholar
7Tu, K.N.: Recent advances on electromigration in very-large-scale-integration of interconnects. J. Appl. Phys. 94, 5451 (2003).CrossRefGoogle Scholar
8 Assembly Edition Packaging Section. International Technology Roadmap for Semiconductors (2005) ITRS, San Jose, CA), p. 2 Table 93a (http://www.itrs.net/Links/2005ITRS/Home2005.htm).Google Scholar
9Hu, Y.C., Lin, Y.H., Kao, C.R., and Tu, K.N.: Electromigration failure in flip chip solder joints due to rapid dissolution of copper. J. Mater. Res. 18, 2544 (2003).CrossRefGoogle Scholar
10Lin, Y.H., Tsai, C.M., Hu, Y.C., Lin, Y.L., and Kao, C.R.: Electromigration-induced failure in flip-chip solder joints. J. Electron. Mater. 34, 27 (2005).CrossRefGoogle Scholar
11Lin, Y.H., Hu, Y.C., Tsai, C.M., Kao, C.R., and Tu, K.N.: In situ observation of the void formation-and-propagation mechanism in solder joints under current-stressing. Acta Mater. 53, 2029 (2005).CrossRefGoogle Scholar
12Shao, T.L., Liang, S.W., Lin, T.C., and Chen, C.: Three-dimensional simulation on current-density distribution in flip-chip solder joints under electric current stressing. J. Appl. Phys. 98, 044509 (2005).CrossRefGoogle Scholar
13Choi, W.J., Yeh, E.C.C., and Tu, K.N.: Mean-time-to-failure study of flip-chip solder joints on Cu/Ni(V)/Al thin-film under-bump-metallization. J. Appl. Phys. 94, 5665 (2003).CrossRefGoogle Scholar