The mechanical behavior of ceramic–metal laminate under thermal shock

Published online by Cambridge University Press:  31 January 2011

Dov Sherman  and
Doron Schlumm
Dov Sherman
Affiliation:
Department of Materials Engineering, Technion-Israel Institute of Technology, Haifa 32000, Israel
Doron Schlumm
Affiliation:
Department of Materials Engineering, Technion-Israel Institute of Technology, Haifa 32000, Israel
Get access

Abstract

A new material system for applications involving thermal shock is proposed. The system consists of thin layers of ceramics and thinner metallic interlayers. In this study, a ceramic/metal laminate was constructed from Coor's ADS96R thin plates alternating with thinner Wesgo Cusil Active Braze Alloy interlayer foils and joined in active brazing. The maximum brazing temperature was 845 °C. Square laminated plates were quenched in room-temperature distilled water, where a very large heat transfer coefficient exists, and therefore, severe conditions of thermal shock occur. The laminated plates, initially at temperatures of 600 and 800 °C, were quenched at their bottom surface only in a specially designed apparatus. The temperatures at the top and the bottom surfaces of the specimens were measured by means of two thermocouples during quenching. The basic features of this architecture are described. The dominant behavior was the absence of interaction between the biaxial cracking mechanisms in a ceramic layer with those in an adjacent ceramic layer, and localization of the damage to those layers that experienced sufficient tensile stresses. The result was a dramatic increase of the residual strength after thermal shock. In addition, R-curve behavior upon mechanical loading caused by plastic deformation of the metallic interlayer was observed.

Type
Articles
Information
Journal of Materials Research , Volume 14 , Issue 9 , September 1999 , pp. 3544 - 3551
Copyright
Copyright © Materials Research Society 1999

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1.Hasselman, D.P.H, J. Am. Ceram. Soc. 52, 600 (1955).CrossRefGoogle Scholar
2.Jin, Z-H and Mai, Y-W., J. Am. Ceram. Soc. 78, 1873 (1995).CrossRefGoogle Scholar
3.Claussen, N. and Hasselman, D.P.H, in Thermal Stresses in Severe Environments, edited by Hasselman, D.P.H and Heller, R.A. (Plenum, New York, 1980), p. 381.CrossRefGoogle Scholar
4.Becher, P.F. and Warwick, W.H., NATO ASI Series, Series E: Applied Science, edited by Schneider, G.A. and Petzow, G. (Kluwer Academic Publishers, 1993), Vol. 241, p 37.Google Scholar
5.Kingery, W.D., J. Am. Ceram. Soc. 38, 3 (1955).CrossRefGoogle Scholar
6.Wang, H. and Singh, R.N., Int. Mater. Rev. 39, 6 (1994).CrossRefGoogle Scholar
7.Becher, P.F., Comm. Am. Ceram. Soc. 1, C–17 (1981).Google Scholar
8.Upadhya, K., Yang, J.M., and Hoffman, W.P., J. Am. Ceram. Soc. Bull. 75(12), 51 (1997).Google Scholar
9.Bøggild, O.B., Kong. Dansk. Vidensk. Selskabs Skrifter, 9, 235 (1930).Google Scholar
10.Currey, J.D., Proc. Roy. Soc. B196, 443 (1997).Google Scholar
11.Sherman, D., Lemaitre, J., and Leckie, F.A., Acta Metall. 43, 3261 (1995).CrossRefGoogle Scholar
12.Sherman, D., Lamaitre, J., and Leckie, F.A., Acta. Metall. 43, 4483 (1995).CrossRefGoogle Scholar
13.Cutler, W.A., Zok, F.W., and Lange, F.F., J. Am. Ceram. Soc. 79, 1825 (1996).CrossRefGoogle Scholar
14.Clegg, W.J., Kendall, K., Alford, N.M., Birchall, D., and Button, T.W., Nature 347, 455 (1990).CrossRefGoogle Scholar
15.Clegg, W.J., Acta. Metall. Mater. 40, 3093 (1992).CrossRefGoogle Scholar
16.Zhang, L. and Krstic, V.D., Theo. App. Frac. Mech. 24, 13 (1995).CrossRefGoogle Scholar
17.Marshall, D.B., Ratto, J.J., and Lange, F.F., J. Am. Ceram. Soc. 74, 2979 (1991).CrossRefGoogle Scholar
18.Evans, A.G., Bartlett, A., Davis, J.B., Flinn, B.D., Turner, M., and Reimanis, I.E., Scripta Metall. Mater. 25, 1003 (1991).CrossRefGoogle Scholar
19.Oh, T.S., Rodel, J., Cannon, R.M., and Ritchie, R.O., Acta Metall. 36, 2083 (1988).CrossRefGoogle Scholar
20.Reimanis, I.E., Dalgleish, B.J., and Evans, A.G., Acta Metall. 39, 3133 (1991).CrossRefGoogle Scholar
21.Schussler, A. and Gahr, K-H.Z, J. de Physique IV 1, C7–121 (1991).Google Scholar
22.Cho, C-H. and Yu, Jin, Scripta Metall. 26, 1737 (1990).Google Scholar
23.Naka, M., Sahpath, K., Okamoto, I., and Arata, Y., Mater. Sci. Eng. 98, 407 (1988).CrossRefGoogle Scholar
24.Naka, M., Kim, K., Okamoto, I., Trans. of JWRI 13, 157 (1984).Google Scholar
25.Sherman, D., Mater. Lett. 33, 255 (1998).CrossRefGoogle Scholar
26.Sherman, D. and Schlumm, D. (unpublished).Google Scholar
27.Evans, A.G. and Hutchinson, J.W., Acta Metall. Mater. 43, 2507 (1995).CrossRefGoogle Scholar