Highly conductive group VI transition metal dichalcogenide films by solution-processed deposition

Published online by Cambridge University Press:  18 July 2011

Wooseok Ki
Affiliation:
Department of Chemistry and Chemical Biology, Rutgers University, Piscataway, New Jersey 08854
Xiaoying Huang
Affiliation:
Department of Chemistry and Chemical Biology, Rutgers University, Piscataway, New Jersey 08854
Jing Li*
Affiliation:
Department of Chemistry and Chemical Biology, Rutgers University, Piscataway, New Jersey 08854
David L. Young
Affiliation:
National Renewable Energy Laboratory, Golden, Colorado 80401
Yong Zhang
Affiliation:
National Renewable Energy Laboratory, Golden, Colorado 80401
*
a) Address all correspondence to this author. e-mail: [email protected]
Get access

Abstract

A new soluble synthetic route was developed to fabricate thin films of layered structure transition metal dichalcogendies, MoS2 and WS2. High-quality thin films of the dichalcogenides were prepared using new soluble precursors, (CH3NH3)2MS4 (M = Mo, W). The precursors were dissolved in organic solvents and spun onto substrates via both single- and multistep spin coating procedures. The thin films were formed by the thermal decomposition of the coatings under inert atmosphere. Structural, electrical, optical absorption, thermal, and transport properties of the thin films were characterized. Surface morphology of the films was analyzed by atomic force microscopy and scanning electron microscopy. Highly conductive and textured n-type MoS2 films were obtained. The measured room temperature conductivity ∼50 Ω−1 cm−1 is substantially higher than the previously reported values. The n-type WS2 films were prepared for the first time using solution-processed deposition. WS2 displays a conductivity of ∼6.7 Ω−1 cm−1 at room temperature.

Type
Articles
Copyright
Copyright © Materials Research Society 2007

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1Ridley, B.A., Nivi, B., and Jacobson, J.M.: All-inorganic field effect transistors fabricated by printing. Science 286, 746 (1999).CrossRefGoogle ScholarPubMed
2Mitzi, D.B., Copel, M., and Chey, S.J.: Low-voltage transistor employing a high-mobility spin-coated chalcogenide semiconductor. Adv. Mater. 17, 1285 (2005).CrossRefGoogle Scholar
3Kagan, C.R., Mitzi, D.B., and Dimitrakopoulos, C.D.: Organic-inorganic hybrid materials as semiconducting channels in thin-film field-effect transistors. Science 286, 945 (1999).CrossRefGoogle ScholarPubMed
4Mitzi, D.B., Kosbar, L.L., Murray, C.E., Copel, M., and Afzall, A.: High-mobility ultrathin semiconducting films prepared by spin coating. Nature 428, 299 (2004).CrossRefGoogle ScholarPubMed
5Rapoport, L., Bilik, Y., Feldman, Y., Homyonfer, M., Cohen, S.R., and Tenne, R.: Hollow nanoparticles of WS2 as potential solid-state lubricants. Nature 387, 791 (1997).CrossRefGoogle Scholar
6Hinnemann, B., Moses, P.G., Bonde, J., Jørgensen, K.P., Nielsen, J.H., Horch, S., Chorkendorff, I., and Nørskov, J.K.: Biomimetic hydrogen evolution: MoS2 nanoparticles as catalyst for hydrogen evolution. J. Am. Chem. Soc. 127, 5308 (2005).CrossRefGoogle ScholarPubMed
7Simon, R.A., Ricco, A.J., Harrison, J., and Wrighton, M.S.: Improvement of the photoelectrochemical oxidation of halides by platinization of metal dichalcogenide photoanodes. J. Phys. Chem. 87, 4446 (1983).CrossRefGoogle Scholar
8Chen, J., Li, S.L., Gao, F., and Tao, Z.L.: Synthesis and characterization of WS2 nanotubes. Chem. Mater. 15, 1012 (2003).CrossRefGoogle Scholar
9Afanasiev, P. and Bezverkhy, I.: Synthesis of MoS x (5 >x > 6) amorphous sulfides and their use for preparation of MoS2 monodispersed microspheres. Chem. Mater. 14, 2826 (2002).CrossRefGoogle Scholar
10Zelenski, C.M. and Dorhout, P.K.: Template synthesis of near-monodisperse microscale nanofibers and nanotubules of MoS2. J. Am. Chem. Soc. 120, 734 (1998).CrossRefGoogle Scholar
11Jäger-Waldau, A., Lux-Steiner, M.Ch., Jäger-Waldau, G., and Bucher, E.: WS2 thin films prepared by sulphurization. Appl. Surf. Sci. 71, 731 (1993).CrossRefGoogle Scholar
12Devadasan, J. Jebarj, Sanjeeviraja, C., and Jayachandran, M.: Electrodeposition of p -WS2 thin film and characterization. J. Cryst. Growth 226, 67 (2001).CrossRefGoogle Scholar
13Ballif, C., Regula, M., Lévy, F., Burmeister, F., Schäfle, C., Matthes, T., Leiderer, P., Niedermann, P., Gutmannsbauer, W., and Bucher, R.: Submicron contacts for electrical characterization of semiconducting WS2 thin films. J. Vac. Sci. Technol., A 16, 1239 (1998).CrossRefGoogle Scholar
14Li, S.J., Bernède, J.C., Pouzet, J., and Jamali, M.: WS2 thin films prepared by solid state reaction (induced by annealing) between the constituents in thin film form. J. Phys. Condens. Matter 8, 2291 (1996).CrossRefGoogle Scholar
15Mandal, K.C. and Mondal, A.: Chemically deposited semiconducting molybdenum sulfide thin films. J. Solid State Chem. 85, 176 (1990).CrossRefGoogle Scholar
16Tonti, D., Varsano, F., Decker, F., Ballif, C., Regula, M., and Remškar, M.: Preparation and photoelectrochemistry of semiconducting WS2 thin films. J. Phys. Chem. B 101, 2485 (1997).CrossRefGoogle Scholar
17Pütz, J. and Aegerter, M.A.: Spin deposition of MoS x thin films. Thin Solid Films 351, 119 (1999).CrossRefGoogle Scholar
18Wendlandt, W.M. and Hecht, H.G.: Reflectance Spectroscopy (Wiley Interscience, New York, 1966).Google Scholar
19 ICDD Card Nos. 37-1492 and 08-0237 International Center for Diffraction Data: Newton Square, PA, 1996.Google Scholar
20Bucher, E. and Aruchamy, A., Photoelectrochemistry and Photovoltaics of Layered Semiconductors (Kluwer Academic Publishers, Dordrecht, NL, 1992), p. 36.Google Scholar
21Bernède, J.C., Pouzet, J., Gourmelon, E., and Hadouda, H.: Recent studies on photoconductive thin films of binary compounds. Synth. Met. 99, 45 (1999).CrossRefGoogle Scholar
22Cheon, J., Gozum, J.E., and Girolami, G.S.: Chemical vapor deposition of MoS2 and TiS2 films from the metal-organic precursors Mo(S-t-Bu)4 and Ti(S-t-Bu)4. Chem. Mater. 9, 1847 (1997).CrossRefGoogle Scholar
23Barreau, N. and Bernède, J.C.: MoS2 textured films grown on glass substrates through sodium sulfide based compounds. J. Phys. D Appl. Phys. 35, 1197 (2002).CrossRefGoogle Scholar
24Wilson, J.A. and Yoffe, A.D.: The transition metal dichalcogenides discussion and interpretation of the observed optical, electrical and structural properties. Adv. Phys. 18, 193 (1969).CrossRefGoogle Scholar
25Alonso, G., Petranovskii, V., Valle, M. Del, Cruz-Reyes, J., Licea-Claverie, A., and Fuentes, S.: Preparation of WS2 catalysts by in situ decomposition of tetraalkylammonium thiotungstates. Appl. Catal. G E N 197, 87 (2000).CrossRefGoogle Scholar
26Sze, S.M.: Semiconductor Devices: Physics and Technology 2nd ed. (John Wiley & Sons, New York, 1985).Google Scholar
27Mergel, D. and Qiao, Z.: Correlation of lattice distortion with optical and electrical properties of In2O3:Sn films. J. Appl. Phys. 95, 5608 (2004).CrossRefGoogle Scholar
28Ouerfelli, J., Bernède, J.C., Khelil, A., and Pouzet, J.: Photoconductive WS2 thin films obtained from multilayer Ni/W/S . . . W/S structure. Appl. Surf. Sci. 120, 1 (1997).CrossRefGoogle Scholar
29Walton, R.I. and Hibble, S.J.: A combined in situ x-ray absorption spectroscopy and x-ray diffraction study of the thermal decomposition of ammonium tetrathiotungstate. J. Mater. Chem. 9, 1347 (1999).CrossRefGoogle Scholar
30Ellmer, K., Stock, C., Diesner, K., and Sieber, I.: Deposition of c⫠-oriented tungsten disulfide (WS2) films by reactive DC magnetron sputtering from a W-target in Ar/H2S. J. Cryst. Growth 182, 389 (1997).CrossRefGoogle Scholar