Growth and properties of KBe2BO3F2 crystal

Published online by Cambridge University Press:  03 March 2011

Jiyang Wang ,
Chenqian Zhang ,
Yaogang Liu ,
Jianxiu Zhang ,
Xiaobo Hu ,
Minhua Jiang ,
Chuangtian Chen ,
Yicheng Wu  and
Zuyan Xu
Jiyang Wang*
Affiliation:
The State Key Lab of Crystal Materials, Shandong University, Jinan 250100, People's Republic of China
Chenqian Zhang
Affiliation:
The State Key Lab of Crystal Materials, Shandong University, Jinan 250100, People's Republic of China
Yaogang Liu
Affiliation:
The State Key Lab of Crystal Materials, Shandong University, Jinan 250100, People's Republic of China
Jianxiu Zhang
Affiliation:
The State Key Lab of Crystal Materials, Shandong University, Jinan 250100, People's Republic of China
Xiaobo Hu
Affiliation:
The State Key Lab of Crystal Materials, Shandong University, Jinan 250100, People's Republic of China
Minhua Jiang
Affiliation:
The State Key Lab of Crystal Materials, Shandong University, Jinan 250100, People's Republic of China
Chuangtian Chen
Affiliation:
Beijing Center for Crystal R&D, Academy of Sciences, Beijing 100080, People's Republic of China
Yicheng Wu
Affiliation:
Beijing Center for Crystal R&D, Academy of Sciences, Beijing 100080, People's Republic of China
Zuyan Xu
Affiliation:
Beijing Center for Crystal R&D, Academy of Sciences, Beijing 100080, People's Republic of China
*
a)Address all correspondence to this author. e-mail: [email protected]
Get access

Abstract

Single crystals of KBeBO3F (KBBF) up to 2 mm in thickness were grown by using a spontaneous nucleation method. The flux was composed of KF and B2O3, and the optimal ratio for growing KBBF single crystal thicker than 1 mm is suggested to be (1.0–1.5):(5.0):(0.7–1.2) (KBBF:KF:B2O3) in molar ratio. The ideal morphology of.KBBF is two sets of tabular facets and a set of rhombic facets. Surface morphology.was characterized both by optical microscopy and atomic force microscopy. Transmission spectra showed that high transmission was maintained up to 170 nm. Based on refractive index measurements, phase matching curves for types I and II were determined. Using a prism coupling method, the effective fourth harmonic generation for an Nd:YAB laser was realized in an 0.6-mm-thick KBBF sample. The output energy of the 266-nm beam was 0.282 mJ, and the conversion efficiency was 11.8%. A 183.6-nm laser over 1 mW was obtained from a Ti:sapphire second harmonic generation beam in an 0.8-mm KBBF sample. The conversion efficiency reached 2.3%. A 179.4-nm laser was also observed from a 358.7-nm laser by directly frequency doubling. This is the shortest wavelength obtained through nonlinear optical processes in a solid-state laser.

Type
Articles
Information
Journal of Materials Research , Volume 18 , Issue 10 , October 2003 , pp. 2478 - 2485
Copyright
Copyright © Materials Research Society 2003

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1.Deway, C.F., Jr., Cook, W.R., Jr., Hodgson, R.T., and Wynne, J.J., Appl. Phys. Lett. 26, 714 (1975).CrossRefGoogle Scholar
2.Chen, C., Wu, B., Jiang, A., and You, G., Sci. Sin. B 7, 598 (1984).Google Scholar
3.Chen, C., Wu, Y., Jiang, A., You, G., Li, R., and Lin, S., J. Opt. Soc. Am. B. 6(4), 611 (1989).Google Scholar
4.Mei, L., Wang, Y., Chen, C., and Wu, B., J. Appl. Phys. 74, 7014 (1993).CrossRefGoogle Scholar
5.Chen, C., Wang, Y., Wu, B., Wu, K., Zeng, W., and Yu, L., Nature 332, 373 (1995).Google Scholar
6.Botsanova, L.R., Egorov, V.A., and Nikolaev, A.V., Dokl. Akad. Nauk. SSSR 178, 1317 (1968).Google Scholar
7.Solv, L.P. A'eva and Bakakin, V.V., Kristallografiya 15, 922 (1970).Google Scholar
8.Mei, L., He, C., and Chen, C., J. Cryst. Growth 132, 609 (1993).CrossRefGoogle Scholar
9.Mei, L., Huang, X., Wang, Y., Wu, Q., Wu, B., and Chen, C., Kristallografiya 210, 93 (1995).Google Scholar
10.Sosaki, T., Mori, Y., Yoshimura, M., Yap, Y.K., and Kamimura, T., Mater. Sci. Eng. 30, 1 (2000).CrossRefGoogle Scholar
11.Tang, D., Xia, Y., Wu, B., and Chen, C., J. Cryst. Growth 222, 125 (2001).CrossRefGoogle Scholar
12.Chen, C., Xu, Z., Deng, D., Zhang, J., Wong, G., Wu, B., Ye, N., and Tang, D., Appl. Phys. Lett. 68, 2930 (1996).CrossRefGoogle Scholar
13.Chen, C., Ye, N., Lin, J., Jiang, J., Zeng, W., and Wu, B., Adv. Mater. 11, 1071 (1999).3.0.CO;2-G>CrossRefGoogle Scholar
14.Chen, C., Lu, J., Wang, G., Xu, Z., Wang, J., Zhang, C., and Liu, Y., Chin. Phys. Lett. 18, 1081 (2001).CrossRefGoogle Scholar
15.Chen, C. and Xu, Z., J. Synth. Crystals 31, 224 (2002) (in Chinese).Google Scholar