Grain growth and void formation in dielectric-encapsulated Cu thin films

Published online by Cambridge University Press:  31 January 2011

B. Yao ,
T. Sun ,
V. Kumar ,
K. Barmak  and
K.R. Coffey
B. Yao
Affiliation:
Advanced Materials Processing and Analysis Center, University of Central Florida, Orlando, Florida 32826
T. Sun*
Affiliation:
Advanced Materials Processing and Analysis Center, University of Central Florida, Orlando, Florida 32826
V. Kumar
Affiliation:
Department of Materials Science and Engineering, Carnegie Mellon University, Pittsburgh, Pennsylvania 15213
K. Barmak
Affiliation:
Department of Materials Science and Engineering, Carnegie Mellon University, Pittsburgh, Pennsylvania 15213
K.R. Coffey
Affiliation:
Advanced Materials Processing and Analysis Center, University of Central Florida, Orlando, Florida 32826
*
a)Address all correspondence to this author. e-mail: [email protected]
Get access

Abstract

Grain growth in 40-nm-thick Cu films encapsulated by over- and under-layers of SiO2, Al2O3, Si3N4, and MgO was investigated. The films were magnetron sputter deposited onto cooled SiO2/Si substrates in an ultrahigh vacuum purity environment. Ex situ annealing was performed at 400 and 800 °C in 1 atm reducing gas. Films deposited at −120 °C exhibited more extensive grain growth after annealing than films deposited at −40 °C. Films annealed at room temperature had grain sizes less than 35 nm. All films exhibited some void formation after annealing at 400 and 800 °C, but the films encapsulated in Al2O3 exhibited the lowest area fraction of voids. The mean grain sizes of the Al2O3-encapsulated films, as measured by the linear intercept method, were 86 and 134 nm after annealing at 400 and 800 °C, respectively.

Keywords

CuGrain sizeThin film
Type
Articles
Information
Journal of Materials Research , Volume 23 , Issue 7 , July 2008 , pp. 2033 - 2039
Copyright
Copyright © Materials Research Society 2008

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1Hu, C.K.Harper, J.M.E.: Copper interconnections and reliability. Mater. Chem. Phys. 52, 5 1998CrossRefGoogle Scholar
2Rossnagel, S.M.Kuan, T.S.: Alteration of Cu conductivity in the size effect regime. J. Vac. Sci. Technol., B 22, 240 2004CrossRefGoogle Scholar
3Rossnagel, S.M.Kuan, T.S.: Time development of microstructure and resistivity for very thin Cu films. J. Vac. Sci. Technol., A 20, 1911 2002CrossRefGoogle Scholar
4Detavernier, C., Deduytsche, D., Van Meirhaeghe, R.L., De Baerdemaeker, J.Dauwe, C.: Room-temperature grain growth in sputter-deposited Cu films. Appl. Phys. Lett. 82, 1863 2003CrossRefGoogle Scholar
5Barmak, K., Gungor, A., Cabral, C.Harper, J.M.E.: Annealing behavior of Cu and dilute Cu-alloy films: Precipitation, grain growth, and resistivity. J. Appl. Phys. 94, 1605 2003CrossRefGoogle Scholar
6Harper, J.M.E.Rodbell, K.P.: Microstructure control in semiconductor metallization. J. Vac. Technol., B 15, 763 1997CrossRefGoogle Scholar
7Gunther, B., Kumpmann, A.Kunze, H.D.: Secondary recrystallization effects in nanostructured elemental metals. Scr. Metall. Mater. 27, 833 1992CrossRefGoogle Scholar
8Moriyama, M., Matsunaga, K.Murakami, M.: Microstructure control in semiconductor metallization. J. Electron. Mater. 32, 261 2003CrossRefGoogle Scholar
9Alford, T.L., Chen, L.H.Gadre, K.S.: Stability of silver thin films on various underlying layers at elevated temperatures. Thin Solid Films 429, 248 2003CrossRefGoogle Scholar
10Palmer, J.E., Thompson, C.V.Smith, H.I.: Grain growth and grain size distributions in thin germanium films. J. Appl. Phys. 62, 2492 1987CrossRefGoogle Scholar
11Jiran, E.Thompson, C.V.: Capillary instabilities in thin-films. J. Electron. Mater. 19, 1153 1990CrossRefGoogle Scholar
12Dannenberg, R., Stach, E.A., Groza, J.R.Dresser, B.J.: In-situ TEM observations of abnormal grain growth, coarsening, and substrate de-wetting in nanocrystalline Ag thin films. Thin Solid Films 370, 54 2000CrossRefGoogle Scholar
13Srolovitz, D.J.Goldiner, M.G.: The thermodynamics and kinetics of film agglomeration. JOM 31, 47 1995Google Scholar
14Mullins, W.W.: Theory of thermal grooving. J. Appl. Phys. 28, 333 1957CrossRefGoogle Scholar
15Sieradzki, K., Bailey, K.Alford, T.L.: Agglomeration and percolation conductivity. Appl. Phys. Lett. 79, 3401 2001CrossRefGoogle Scholar
16Gadkari, P.R., Warren, A.P., Todi, R.M., Petrova, R.V.Coffey, K.R.: Comparison of the agglomeration behavior of thin metallic films on SiO2. J. Vac. Sci. Technol., A 23, 1152 2005CrossRefGoogle Scholar
17Yao, B., Petrova, R.V., Vanfleet, R.R.Coffey, K.R.: A modified back-etch method for preparation of plan-view high-resolution transmission electron microscopy samples. J. Electron Microsc. (Tokyo) 55, 209 2006CrossRefGoogle ScholarPubMed
18Yao, B.Coffey, K.R.: Back-etch method for plan view transmission electron microscopy sample preparation of optically opaque films. J. Electron Microsc. 57(2), 47 2008CrossRefGoogle ScholarPubMed
19Collins, T.J.: ImageJ for microscopy. Biotechniques 43(1 Suppl), 25 2007CrossRefGoogle ScholarPubMed
20Balluffi, R.W., Allen, S.A.Carter, W.C.: Kinetics of Materials 1st ed.John Wiley & Sons Hoboken,NJ 2005 368–376CrossRefGoogle Scholar