The existence of Ni3MSb phases in ternary nickel-M-antimony systems (where “M” represents aluminum, gallium, or indium)

Published online by Cambridge University Press:  31 January 2011

C-H. Jan  and
Y.A. Chang
C-H. Jan
Affiliation:
Department of Materials Science and Engineering, University of Wisconsin, 1509 University Avenue, Madison, Wisconsin 53706
Y.A. Chang
Affiliation:
Department of Materials Science and Engineering, University of Wisconsin, 1509 University Avenue, Madison, Wisconsin 53706
Get access

Abstract

Phases of the nominal composition Ni3MSb (where “M” represents aluminum, gallium, or indium) were found to occur in their respective ternary systems. They were analyzed by x-ray diffraction and were found to exhibit the B81.5′ crystal structure, similar to that of Ni3GaAs. These phases were shown by differential thermal analysis (DTA) to be stable between room temperature and their melting points, which were determined to be >1150 °C, 1066 °C, and 1091 °C for Ni3AlSb, Ni3GaSb, and Ni3InSb, respectively. An analysis of their respective constituent binary systems suggested that these phases were not true ternary compounds, but rather represented specific compositions of extensive solid solutions of constituent binary phases. Speculations were made as to the solution behavior of these phases. The Ni3MSb phases were predicted to form initially in nickel/MSb diffusion couples, in an analogy to what is observed in nickel/GaAs diffusion couples.

Type
Articles
Information
Journal of Materials Research , Volume 6 , Issue 12 , December 1991 , pp. 2660 - 2665
Copyright
Copyright © Materials Research Society 1991

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1.Braslau, N., Thin Solid Films 104, 391 (1983).CrossRefGoogle Scholar
2.Grinolds, H. R. and Robinson, G. Y., Solid-State Electron. 23, 973 (1980).CrossRefGoogle Scholar
3.Marshall, E. D., Chen, W. X., Wu, C. S., Lau, S. S., and Kuech, T. F., Appl. Phys. Lett. 47, 298 (1985).CrossRefGoogle Scholar
4.Yu, L. S., Wang, L. C., Marshall, E. D., Lau, S. S., and Kuech, T. F., J. Appl. Phys. 65, 1621 (1989).CrossRefGoogle Scholar
5.Wang, L. C., Zhang, B., Fang, F., Marshall, E. D., Lau, S. S., Sands, T., and Kuech, T. F., J. Mater. Res. 3, 922 (1988).CrossRefGoogle Scholar
6.Sands, T., Marshall, E. D., and Wang, L. C., J. Mater. Res. 3, 914 (1988).CrossRefGoogle Scholar
7.Allen, L. H., Hung, L. S., Kavanagh, K. L., Phillips, J. R., Yu, A. J., and Mayer, J. W., Appl. Phys. Lett. 51, 326 (1987).CrossRefGoogle Scholar
8.Murakami, M. and Price, W. H., Appl. Phys. Lett. 51, 664 (1987).CrossRefGoogle Scholar
9.Lin, J-C., Schulz, K. J., Hsieh, K-C., and Chang, Y. A., in High-Temperature Materials Chemistry IV, edited by Munir, Z. A., Cubicciotti, D., and Tagawa, H. (Electrochem. Soc., Bennington, NJ, 1988), p. 476.Google Scholar
10.Lin, J-C., Schulz, K. J., Hsieh, K-C., and Chang, Y. A., J. Electrochem. Soc. 136, 3007 (1988).Google Scholar
11.Zheng, X-Y., Lin, J-C., Swenson, D., Hsieh, K-C., and Chang, Y. A., Mater. Sci. Eng. B5, 63 (1989).CrossRefGoogle Scholar
12.El-Boragy, M. and Schubert, K., Z. Metallkde. 72, 279 (1981).Google Scholar
13.Lin, J-C., Hsieh, K-C., Schulz, K. J., and Chang, Y. A., J. Mater. Res. 3, 148 (1988).CrossRefGoogle Scholar
14.Sands, T., Chang, C. C., Kaplan, A. S., Keramidas, V. G., Krishnan, K. M., and Washburn, J., Appl. Phys. Lett. 50, 1346 (1987).CrossRefGoogle Scholar
15.Caron-Popowich, R., Washburn, J., Sands, T., and Kaplan, A. S., J. Appl. Phys. 64, 4909 (1988).CrossRefGoogle Scholar
16.Sands, T., Keramidas, V. G., Washburn, J., and Gronsky, R., Appl. Phys. Lett. 48, 402 (1986).CrossRefGoogle Scholar
17.Sands, T., Keramidas, V. G., Yu, A. J., Yu, K-M., Gronsky, R., and Washburn, J., J. Mater. Res. 2, 262 (1987).CrossRefGoogle Scholar
18.Michel, W., Ann. Physik. 11, 321 (1963).CrossRefGoogle Scholar
19.Hewitt, D. F., Econ. Geol. 43, 408 (1948).CrossRefGoogle Scholar
20.Feschotte, D. and Eggiman, P., J. Less-Common Metals 63, 15 (1979).CrossRefGoogle Scholar
21.Ellner, M., Bhan, S., and Schubert, K., J. Less-Common Metals 19, 245 (1969).CrossRefGoogle Scholar
22.Kjekhus, A. and Pearson, W. B., in Progress in Solid State Chemistry (Pergamon Press, Inc., Oxford, U.K., 1964), p. 1.Google Scholar
23.Pauling, L., The Nature of the Chemical Bond (Cornell University Press, Ithaca, NY, 1960).Google Scholar