Effect of fiber coating on creep behavior of SiC fiber-reinforced titanium aluminide matrix composites

Published online by Cambridge University Press:  03 March 2011

Hsing-Pang Chiu ,
J-M. Yang  and
J.A. Graves
Hsing-Pang Chiu
Affiliation:
Department of Materials Science and Engineering, University of California, Los Angeles, California 90024-1595
J-M. Yang
Affiliation:
Department of Materials Science and Engineering, University of California, Los Angeles, California 90024-1595
J.A. Graves
Affiliation:
Rockwell International Science Center, Thousand Oaks, California 91358
Get access

Abstract

The effect of fiber coating on the creep behavior and damage mechanisms of unnotched SCS-6 fiber-reinforced Ti3Al matrix composites under longitudinal and transverse loading was investigated at 700 °C. Stresses ranging from 700 to 900 MPa and 200 to 400 MPa were used for longitudinal and transverse loading, respectively. An Ag/Ta duplex layer was coated onto the SCS-6 fiber prior to consolidation via physical vapor deposition. The microstructure of the crept composites was examined to determine the creep deformation mechanisms. The creep cracking behavior of the notched composites was also studied at initial stress intensity factors, Ki, ranging from 15 to 20 MPa-m1/2. Microstructural observation revealed that multiple fiber fracture (at low to medium stress levels), microcracking along the reaction zone/matrix interface (at medium stress levels), and matrix cracking extending from the broken fiber ends (at high stress levels) were the major damage mechanisms during quasi-steady state creep under longitudinal loading. The results show that the Ag/Ta duplex coating significantly improved the creep resistance and flexural strength of the composite under transverse loading. The Ag/Ta duplex coating was also shown to significantly prolong the creep rupture life of SiC fiber-reinforced Ti3Al composites.

Type
Articles
Information
Journal of Materials Research , Volume 9 , Issue 1 , January 1994 , pp. 198 - 206
Copyright
Copyright © Materials Research Society 1994

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1Yang, J-M. and Jeng, S.M., JOM 44 (6), 52 (1992).CrossRefGoogle Scholar
2Brindley, P. K., Draper, S. L., Eldridge, J. I., Nathal, M. V., and Arnold, S. M., Metall. Trans. A 23A, 2527 (1992).CrossRefGoogle Scholar
3Kieschke, R. R., Somekh, R. E., and Clyne, T. W., Acta Metall. Mater. 39 (4), 427 (1991).CrossRefGoogle Scholar
4Jeng, S. M., Yang, J-M., and Graves, J. A., J. Mater. Res. 8, 905 (1993).CrossRefGoogle Scholar
5Chiu, H-P., Jeng, S. M., and Yang, J-M., J. Mater. Res. 8, 2040 (1993).CrossRefGoogle Scholar
6Fett, T. and Munz, D., in Mechanical Testing of Engineering Ceramics at High Temperature, edited by Dyson, B. F., Lohr, R. D., and Morrell, R. (Elsevier Applied Science, London, 1988), p. 189.Google Scholar
7Goto, S. and McLean, M., Acta Metall. Mater. 39 (2), 153 (1991).CrossRefGoogle Scholar
8Jeng, S. M. and Yang, J-M., Mater. Sci. Eng. (1993, in press).Google Scholar
9Thayer, R. B. and Yang, J-M., Mater. Sci. Eng. A 160, 169 (1993).CrossRefGoogle Scholar
10Cho, W., Thompson, A. W., and Williams, J. C., Metall. Trans. A 21A, 641 (1990).CrossRefGoogle Scholar