Effect of binder composition on debinding and sintering processes of injection molded Fe–8Ni mixed powders

Published online by Cambridge University Press:  31 January 2011

Junjiro Takekawa
Junjiro Takekawa
Affiliation:
Department of Electron Materials, Faculty of Science & Technology, Ishinomaki Senshu University, 1 Shinmito Minamisakai, Ishinomaki 986–80, Japan
Get access

Abstract

The debinding process of injection-molded compacts of Fe–8Ni mixed powders, containing binders of different ratios of polymers to wax, was investigated. The effect of binder compositions and debinding conditions on the sinterability of the compacts were also studied. Distortions produced in the debinding processes of the compacts were minimized for the case where a ratio of polymer to the total binder contents was 0.35. In the case of the compacts debound in air, sintered densities increased by increasing the debinding temperature up to 350 °C, then decreased sharply for higher debinding temperatures. In the compacts debound in N2, sintered densities were almost independent of the debinding temperature. The sinterability of the compacts debound in N2 was inferior to that debound in air.

Type
Articles
Information
Journal of Materials Research , Volume 11 , Issue 5 , May 1996 , pp. 1127 - 1132
Copyright
Copyright © Materials Research Society 1996

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1.Pease, L. F. III, Int. J. Powder Met. 24, 123 (1988).Google Scholar
2.Gummeson, P., Int. J. Powder Met. 25, 207 (1989).Google Scholar
3.Pease, L. F. III, J. Metals 41, 15 (1989).Google Scholar
4.Gaspervich, J. R., Int. J. Powder Met. 27, 133 (1991).Google Scholar
5.Hens, K. F., Lee, D., and German, R. M., Int. J. Powder Met. 27, 141 (1991).Google Scholar
6.German, R. M. and Kubish, D., Powder Met. Int. 25, 165 (1993).Google Scholar
7.German, R. M., Int. J. Powder Met. 29, 47 (1993).Google Scholar
8.Shah, S. J. and German, R.E., Plastic Eng. 43, 33 (1987).Google Scholar
9.German, R. M., Int. J. Powder Met. 23, 273 (1987).Google Scholar
10.Lograsso, B. K. and German, R.M., Int. Powder Met. Int. 22, 17 (1990).Google Scholar
11.Moller, J. C. and Lee, D., Int. J. Powder Met. 30, 103 (1994).Google Scholar
12.Lin, S. T. and German, R. M., Powder Met. Int. 21, 9 (1989).Google Scholar
13.Miura, H., Honda, T., and Geramn, R.M., J. Jpn. Soc. Powder and Powder Metal. 38, 767 (1991).Google Scholar
14.Kankawa, Y., Akifusa, Y., Ono, K., and Kaneko, Y., J. Jpn. Soc. Powder and Powder Metal. 41, 232 (1994).Google Scholar
15.Zhang, H., German, R. M., and Bose, A., Int. J. Powder Met. 26, 217 (1990).Google Scholar
16.Vetler, R., Sanders, M.J., Majewska-Glabus, I., Zhuang, L.Z., and Duszczyk, J., Int. J. Powder Met. 30, 115 (1994).Google Scholar
17.Hens, K. F., Lee, D., Lin, S. T., and German, R. M., Powder Met. Int. 23, 15 (1991).Google Scholar
18.Kipphut, C. M. and German, R.M., Int. J. Powder Met. 27, 117 (1991).Google Scholar
19.Finn, C. W., Int. J. Powder Met. 27, 127 (1991).Google Scholar
20.Saitou, K., Basic and Application of Binders Used in Injection Molding of Fine Ceramics and Metal Powders (I.P.C., Tokyo, Japan, 1988), p. 385 (in Japanese).Google Scholar