Unidirectional solidification of Zn-rich Zn-Cu hypoperitectic alloy

Published online by Cambridge University Press:  31 January 2011

Hasan Kaya*
Affiliation:
Department of Science Education, Education Faculty, Erciyes University, Kayseri, Turkey
Sevda Engin
Affiliation:
Institute of Science and Technology, Department of Physics, Erciyes University, Kayseri, Turkey
U. Böyük
Affiliation:
Department of Science Education, Education Faculty, Erciyes University, Kayseri, Turkey
Emin Çadırlı
Affiliation:
Department of Physics, Faculty Arts and Sciences, Niğde University, Niğde, Turkey
Necmettin Maraşlı
Affiliation:
Department of Physics, Faculty Arts and Sciences, Erciyes University, Kayseri, Turkey
*
a) Address all correspondence to this author. e-mail: [email protected]
Get access

Abstract

Zn-0.7 wt.% Cu-hypoperitectic alloy was prepared in a graphite crucible under a vacuum atmosphere. Unidirectional solidification of the Zn-0.7 wt.% Cu-hypoperitectic alloy was carried out by using a Bridgman-type directional solidification apparatus under two different conditions: (i) with different temperature gradients (G = 3.85–9.95 K/mm) at a constant growth rate (41.63 μm/s) and (ii) with different growth rate ranges (G = 8.33–435.67 μm/s) at a constant temperature gradient (3.85 K/mm). The microstructures of the directionally solidified Zn-0.7 wt.% Cu-hypoperitectic samples were observed to be a cellular structure. From both transverse and longitudinal sections of the samples, cellular spacing (λ) and cell-tip radius (R) were measured. The effects of solidification-processing parameters (G and V) on the microstructure parameters (λ and R) were obtained by using a linear regression analysis. The present experimental results were also compared with the current theoretical and numerical models and similar previous experimental results.

Type
Articles
Copyright
Copyright © Materials Research Society 2009

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1.Hunziker, O., Vandyoussefi, M. and Kurz, W.: Phase and microstructure selection in peritectic alloys close to the limit of constitutional undercooling. Acta Mater. 46(18), 6325 (1998).CrossRefGoogle Scholar
2.Kerr, H.W. and Kurz, W.: Solidification of peritectic alloys. Int. Mater. Rev. 41, 129 (1996).CrossRefGoogle Scholar
3.Trivedi, R. and Park, J.S.: Dynamics of microstructure formation in the two-phase region of peritectic systems. J. Cryst. Growth 235, 572 (2002).CrossRefGoogle Scholar
4.John, D.H. St: The peritectic reaction. Acta Metall. 38(4), 631 (1990).Google Scholar
5.Yasuda, H., Notake, N., Tokeida, K., and Ohnaka, I.: Periodic structure during unidirectional solidification for peritectic CdSn alloys. J. Cryst. Growth 210, 637 (2000).CrossRefGoogle Scholar
6.Busse, P. and Meissen, F.: Coupled growth of the properitectic and the peritectic -phases in binary titanium aluminides. Scr. Metall. 36, 653 (1997).CrossRefGoogle Scholar
7.Flemings, M.C.: Solidification Processing (McGraw Hill, New York, 1974), p. 3153.Google Scholar
8.Kurz, W. and Sahm, P.R.: Solidification of Eutectic Materials (Springer Verlag, Berlin, 1975), p. 140.Google Scholar
9.Lo, T.S., Dobler, S., Plapp, M., Karma, A., and Kurz, W.: Twophase microstructure selection in peritectic solidification: From island banding to coupled growth. Acta Metall. 51, 599 (2003).Google Scholar
10.Hunt, J.D.: Solidification and Casting of Metals (The Metals Society, London, 1979), p. 3.Google Scholar
11.Kurz, W. and Fisher, D.J.: Dendritic growth and limit of stability tip radius and spacing. Acta Metall. 29, 11 (1981).CrossRefGoogle Scholar
12.Trivedi, R.: Interdendritic spacing: Part II. A. Comparison of theory and experiment. Metall. Trans. A 15, 977 (1984).CrossRefGoogle Scholar
13.Hunt, J.D. and Lu, S.Z.: Numerical modeling/dendritic array growth: Spacing and structure predictions. Metall. Trans. A 27, 611 (1996).CrossRefGoogle Scholar
14.Kurz, W., Giovanola, B., and Trivedi, R.: Theory of microstructural development during rapid solidification. Acta Metall. 34, 823 (1986).CrossRefGoogle Scholar
15.Kurz, W., Giovanola, B., and Trivedi, R.: Microsegregation in rapidly solidified Ag-15wt-percent-Cu. J. Cryst. Growth 91, 123 (1988).CrossRefGoogle Scholar
16.Li, Y., Ng, S.C., Ma, D., and Jones, H.: Observation of lamellar eutectic-like structure in A Zn-rich Zn-3.37wtCu peritectic alloy processed by bridgman solidification. Scr. Metall. 39, 7 (1998).CrossRefGoogle Scholar
17.Ma, D., Li, Y., Ng, S.C., and Jones, H.: Unidirectional solidification of Zn rich Zn-2.17 wt. Cu hypo-peritectic alloy. Sci. Technol. Adv. Mater. 2, 127 (2001).CrossRefGoogle Scholar
18.Cooksey, D.J., Monson, D., Wilkinson, M.P., and Hellawell, A.: The freezing of some continuous binary eutectic mixtures. Met. Trans. Soc. AIME 218, 745 (1964).Google Scholar
19.Tunca, H. and Smith, R.W.: Variation of dendrite arm spacing in Al-rich Zn-Al off-eutectic alloys. J. Mater. Sci. 23, 111 (1988).CrossRefGoogle Scholar
20.Young, K.P. and Kirkwood, D.H.: The dendrite arm spacings of aluminium-copper alloys solidified under steady-state conditions. Metall. Mater. Trans. A 6, 197 (1975).CrossRefGoogle Scholar
21.Sharp, R.M. and Hellawell, A.: Solute distributions at-non-planar solid-liquid growth fronts. I: Steady-state conditions. J. Cryst. Growth 6, 253 (1970).CrossRefGoogle Scholar
22.Pratt, R.A. and Grugel, R.N.: Microstructural response to controlled accelerations during the directional solidification of Al-6 wt Si alloys. Mater. Charact. 31, 225 (1993).CrossRefGoogle Scholar
23.Alberny, R., Serra, J., and Turpin, M.: Use of covariograms for dendrite arm spacings measurements. Trans. Metall. Soc. AIME 245, 55 (1969).Google Scholar
24.Lee, J.H., Kim, H.C., Jo, C.Y., Kim, S.K., Shin, J.H., Liu, S., and Trivedi, R.: Microstructure evolution in directionally solidified Fe-18Cr stainless steels. Mater. Sci. Eng., A 413414, 306 (2005).CrossRefGoogle Scholar
25.Tokieda, K., Yasuda, H., and Ohnaka, I.: Formation of banded structure in PbBi peritectic alloys. Mater. Sci. Eng., A 262, 238 (1999).CrossRefGoogle Scholar
26.Lee, J. and Verhoeven, J.D.: Peritectic formation in the Ni-Al system. J. Cryst. Growth 144, 353 (1994).CrossRefGoogle Scholar
27.Xu, W., Feng, Y.P., Li, Y., Zang, G.D., and Li, Z.Y.: Rapid solidification behavior of Zn-rich Zn-Ag peritectic alloys. Acta Mater. 50, 183 (2002).CrossRefGoogle Scholar
28.Gorbunov, A.V.: Parameters of melting dendrites in Na-Cl. Acta Metall. 40(3), 513 (1992).CrossRefGoogle Scholar
29.Trivedi, R. and Mason, J.T.: The effect of interface attachment kinetics on solidification interface morphologies. Metall. Mater. Trans. A 22, 235 (1991).CrossRefGoogle Scholar
30.Chou, K., Zhou, G., and Chen, W.: Fundamentals of Structural Chemistry (World Scientific Publishing Co., Singapore, 1993), p. 373.Google Scholar
31.Walker, D.J. and Mullis, A.M.: A mechanism for the equalisation of primary spacing during cellular and dendritic growth. J. Mater. Sci. 36, 865 (2001).CrossRefGoogle Scholar
32.Ganesan, S., Chan, C.L., and Poirier, D.R.: Permeability for flow parallel to primary arms. Mater. Sci. Eng., A 151, 97 (1992).CrossRefGoogle Scholar
33.Bhat, M.S., Poirier, D.R., and Heinrich, J.C.: Permeability for cross flow through columnar-dendritic alloys. Metall. Trans. B 26, 1049 (1995).CrossRefGoogle Scholar
34.Massalski, T.B.: Binary Alloy Phase Diagram (American Society for Metals, Metals Park, OH, 1986), p. 235.Google Scholar
35.Liu, H.Y. and Jones, H.: Solidification microstructure selection and characteristics in the zinc-based Zn-Mg system. Acta Metall. 40(2), 229 (1992).CrossRefGoogle Scholar