Synthesis and sintering of Ca0.5Sr0.5Zr4P6O24 powders by the decomposition/combustion of Ca-, Sr-, nitrate-ammonium dihydrogen phosphate-urea mixtures

Published online by Cambridge University Press:  03 March 2011

Chang S. Hong ,
P. Ravindranathan ,
Dinesh K. Agrawal  and
Rustum Roy
Chang S. Hong
Affiliation:
Research Center of Ssangyong Cement Industrial Co., Ltd., Daejeon, Korea
P. Ravindranathan
Affiliation:
Materials Research Laboratory, The Pennsylvania State University, University Park, Pennsylvania 16802
Dinesh K. Agrawal
Affiliation:
Materials Research Laboratory, The Pennsylvania State University, University Park, Pennsylvania 16802
Rustum Roy
Affiliation:
Materials Research Laboratory, The Pennsylvania State University, University Park, Pennsylvania 16802
Get access

Abstract

Ca0.5Sr0.5Zr4P6O24 (CSZP) powders were prepared by the decomposition/combustion method using Ca(NO3)2 · 4H2O, Sr(NO3)2, ZrO(NO3)2 · xH2O, NH4H2PO4, urea, and NH4NO3 as starting materials. The homogenized slurries of the mixture were heated at 500 °C for 5 min to obtain CSZP powders. The as-synthesized powders were amorphous and crystallized after heating 800 °C for 2 h. The specific surface area of the powder was varied with the batch weight of starting materials or the amount of urea and ammonium nitrate. Powders with high specific surface area (150 m2/g) could be produced by this method. The sinterability of the powders was comparable to that of sol-gel derived powders. The sintered density of the compacts was 99% of theoretical after firing in air at 1350 °C for 6 h.

Type
Articles
Information
Journal of Materials Research , Volume 9 , Issue 9 , September 1994 , pp. 2398 - 2403
Copyright
Copyright © Materials Research Society 1994

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1Limaye, S. Y., Agrawal, D. K., Roy, R., and Mehrotra, Y., J. Mater. Sci. 26, 93–98 (1991).CrossRefGoogle Scholar
2Roy, R., Agrawal, D. K., Alamo, J., and Roy, R. A., Mater. Res. Bull. XIX, 471–477 (1984).CrossRefGoogle Scholar
3Lenain, G. E., McKinstry, H. A., Limaye, S. Y., and Woodward, A., Mater. Res. Bull. XIX, 1451–1456 (1984).CrossRefGoogle Scholar
4Agrawal, D. K. and Stubican, V. S., Mater. Res. Bull. XX, 99–106 (1985).CrossRefGoogle Scholar
5Oota, T. and Yamai, I., J. Am. Ceram. Soc. 69, 1–6 (1986).CrossRefGoogle Scholar
6Limaye, S. Y., Agrawal, D. K., and McKinstry, H. A., J. Am. Ceram. Soc. 70, C232–C236 (1987).CrossRefGoogle Scholar
7Agrawal, D. K. and Adair, J. H., J. Am. Ceram. Soc. 73, 2153–2155 (1990).CrossRefGoogle Scholar
8Ibrahim, D. M. and Hennicke, H. W., Trans. J. Ceram. Soc. 80, 8–12 (1981).Google Scholar
9Siracusa, G., Seminara, A., Cucinotta, V., and Gurrieri, S., Thermochim. Acta 23, 109–115 (1978).CrossRefGoogle Scholar
10Lupin, M. S. and Peters, G. E., Thermochim. Acta 73, 79–87 (1984).CrossRefGoogle Scholar
11Sonder, E., Quinby, T. C., and Kinser, D. L., Am. Ceram. Soc. Bull. 65, 665–668 (1986).Google Scholar
12Kingsley, J. J. and Patil, K. C., Mater. Lett. 6, 427–432 (1988).CrossRefGoogle Scholar
13Zdaniewski, W. A., J. Am. Ceram. Soc. 61, 199–204 (1978).CrossRefGoogle Scholar
14Matusita, K. and Sakka, S., J. Non-Cryst. Solids 38 & 39, 741–746 (1980).CrossRefGoogle Scholar