Solidification of CaCO3 containing SrCO3 by hydrothermal hot-pressing

Published online by Cambridge University Press:  31 January 2011

Nakamichi Yamasaki ,
Tang Weiping  and
Kazumichi Yanagisawa
Nakamichi Yamasaki
Affiliation:
Research Laboratory of Hydrothermal Chemistry, Faculty of Science, Kochi University, Kochi 780, Japan
Tang Weiping
Affiliation:
Research Laboratory of Hydrothermal Chemistry, Faculty of Science, Kochi University, Kochi 780, Japan
Kazumichi Yanagisawa
Affiliation:
Research Laboratory of Hydrothermal Chemistry, Faculty of Science, Kochi University, Kochi 780, Japan
Get access

Abstract

Powders of calcium carbonate with strontium carbonate were solidified by mechanical compression under hydrothermal conditions. The effects of hydrothermal conditions such as temperature, pressure, and ratio of Ca/Sr on the reaction process and microstructure of the solidified bodies were examined. Solidification of every powder easily proceeded with shrinkage above 200 °C to 300 °C. The compacts of strontium carbonate were more easily solidified, and compressive strength was 190 MPa and its density was 93.5%. The solidification with shrinkage of compacts consisting of mixed powders of calcium and strontium carbonates was accelerated with an increase in strontium carbonate content. It was revealed that the small amount of strontium carbonate powder acts as a bonding material among large calcium carbonate particles.

Type
Articles
Information
Journal of Materials Research , Volume 8 , Issue 8 , August 1993 , pp. 1972 - 1976
Copyright
Copyright © Materials Research Society 1993

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1Roy, D. M., Goude, G. R., and Bobrowsky, A., Cement and Concrete Research 1, 349–366 (1972).CrossRefGoogle Scholar
2Hirano, S. and Somiya, S., Am. Ceram. Soc. Bull. 55, 534 (1976).CrossRefGoogle Scholar
3Yoshimura, M. and Somiya, S., Am. Ceram. Soc. Bull. 59, 246 (1980).Google Scholar
4Yamasaki, N., Yanagisawa, K., Nishioka, M., and Kanahara, S., J. Mater. Sci. Lett. 5, 355 (1986).CrossRefGoogle Scholar
5Yanagisawa, K., Kanahara, S., Nishioka, M., and Yamasaki, N., J. Nucl. Sci. Technol. 21, 558 (1984).CrossRefGoogle Scholar
6Yamasaki, N., Yanagisawa, K., and Kakiuchi, N., J. Mater. Res. 5, 647 (1990).CrossRefGoogle Scholar
7Matsuoka, K., Kuwabara, K., Yamasaki, N., and Mitsushio, H., Rep. Res. Lab. Hydrotherm. Chem., Kochi University 3, 8 (1978).Google Scholar
8Yamasaki, N., Tang, W., and Ke, J., J. Mater. Sci. Lett. 11, 934 (1992).CrossRefGoogle Scholar