A self-propagating high-temperature synthesis method for synthesis of AlN powder

Published online by Cambridge University Press:  31 January 2011

Shyan-Lung Chung ,
Wen-Liang Yu  and
Chun-Nan Lin
Shyan-Lung Chung*
Affiliation:
Department of Chemical Engineering, National Cheng Kung University, Tainan, Taiwan, 70101, Republic of China
Wen-Liang Yu
Affiliation:
Department of Chemical Engineering, National Cheng Kung University, Tainan, Taiwan, 70101, Republic of China
Chun-Nan Lin
Affiliation:
Department of Chemical Engineering, National Cheng Kung University, Tainan, Taiwan, 70101, Republic of China
*
a)Address all correspondence to this author. e-mail: [email protected]
Get access

Abstract

A new self-propagating high-temperature synthesis (SHS) process has been developed for synthesis of AlN powder under low nitrogen pressures. Al and NH4X (X = F, Cl, Br, or I) powders were mixed and pressed into a compact, which was placed in a reaction chamber filled with nitrogen. The combustion synthesis reaction was ignited by heating directly the compact, and high product yields (∼90%) were obtained under nitrogen pressures of around 0.5 MPa. The product yield was affected by the reactant composition, the nitrogen pressure, and the compact-forming pressure. The powder as synthesized consists mainly of fibers, coarse granules, and agglomerated fine particles, which become mostly smaller than 10 μm after grinding. A reaction process was also proposed that explains the effects of the experimental parameters on the product yield.

Type
Articles
Information
Journal of Materials Research , Volume 14 , Issue 5 , May 1999 , pp. 1928 - 1933
Copyright
Copyright © Materials Research Society 1999

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1.Sheppard, L. M., Ceram. Bull. 69 (11), 1801 (1990).Google Scholar
2.Mroz, T. J. Jr, Ceram. Bull. 71 (5), 782 (1992).Google Scholar
3.Mroz, T. J. Jr, Ceram. Bull. 72 (6), 78 (1993).Google Scholar
4.Selvaduray, G. and Sheet, L., Mater. Sci. Technol. 9, 463 (1993).CrossRefGoogle Scholar
5.Haussonne, F. J-M., Mater. Manufacturing Processes 10 (4), 717 (1995).CrossRefGoogle Scholar
6.Merzhanov, A. G. and Borovinskaya, I. P., Combust. Sci. Technol. 10, 195 (1975).CrossRefGoogle Scholar
7.Crider, J. F., Ceram. Eng. Sci. Proc. 3 (9–10), 519 (1982).CrossRefGoogle Scholar
8.Lee, W.C., Tu, C. L., Weng, C. Y., and Chung, S. L., J. Mater. Res. 10, 774 (1995).CrossRefGoogle Scholar
9.CRC Handbook of Chemistry and Physics: A Ready-Reference Book of Chemical and Physical Data, 77th ed. (CRC, Boca Raton, FL, 1996–1997).Google Scholar