The low temperature hexagonal to orthorhombic transformation in Si3N4 reinforced BAS matrix composites

Published online by Cambridge University Press:  03 March 2011

A. Bandyopadhyay ,
P.B. Aswath ,
W.D. Porter  and
O.B. Cavin
A. Bandyopadhyay
Affiliation:
Department of Mechanical and Aerospace Engineering and Materials Science and Engineering Program. University of Texas at Arlington, Arlington, Texas 76019-0031
P.B. Aswath
Affiliation:
Department of Mechanical and Aerospace Engineering and Materials Science and Engineering Program. University of Texas at Arlington, Arlington, Texas 76019-0031
W.D. Porter
Affiliation:
High Temperature Materials Laboratory, Oak Ridge National Laboratory, Oak Ridge, Tennessee 37831-6064
O.B. Cavin
Affiliation:
High Temperature Materials Laboratory, Oak Ridge National Laboratory, Oak Ridge, Tennessee 37831-6064
Get access

Abstract

The amount of Si3N4 in a Si3N4-BaO · Al2O3 · 2SiO2 (BAS) composite and the time of sintering was examined in the context of the low temperature hexagonal to orthorhombic transformation in BAS. It was found that with increasing amounts of Si3N4 in the composite, the temperature of the hexagonal to orthorhombic transformation was decreased. As the sintering time was increased for a given composite composition, a drop in the temperature of the hexagonal to orthorhombic transformation was observed. which was linked to an increase in the β-Si3N4 content in the composite. In addition, as the Si3N4 content in the composite was increased, a resultant drop in the coefficient of thermal expansion of the composite occurred. The extent of the linear dimensional change of the composite during the BAS hexagonal to orthorhombic transformation is reported.

Type
Articles
Information
Journal of Materials Research , Volume 10 , Issue 5 , May 1995 , pp. 1256 - 1263
Copyright
Copyright © Materials Research Society 1995

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1Sjögern, H., Geol. Foren. 17, 578–582 (1895).CrossRefGoogle Scholar
2Strandmark, J. E., Geol. Fören. Forh. 25, 289–318 (1903).CrossRefGoogle Scholar
3Lin, H. C. and Foster, W. R., Am. Min. 53, 134 (1968).Google Scholar
4Bansal, N. P. and Hyatt, M.J., J. Mater. Res. 4, 1257–1265 (1989).CrossRefGoogle Scholar
5Yoshiki, B. and Matsumoto, K., J. Am. Ceram. Soc. 34, 283 (1951).CrossRefGoogle Scholar
6Takéuchi, Y., Mineralogical J. 2, 311–332 (1958).Google Scholar
7Ito, T., X-Ray Studies on Polymorphism (Maruzen Co. Ltd, Tokyo, 1950), pp. 19–29.Google Scholar
8Drew, P. and Lewis, M. H., J. Mater. Sci. 9, 261 (1974).CrossRefGoogle Scholar
9Bandyopadhyay, A., Quander, S. W., Aswath, P. B., Freitag, D. W., Richardson, K K, and Hunn, D.L., Scripta Metall. et Mater. (1995)Google Scholar
10Hardi, D. and Jack, K. H., Nature 180, 332 (1957).CrossRefGoogle Scholar