Limit of superconductivity in silver/superconductor metal-matrix composites prepared with Bi–Pb–Sr–Ca–Cu–O ceramic powders

Published online by Cambridge University Press:  31 January 2011

Asok K. Sarkar ,
I. Maartense  and
T.L. Peterson
Asok K. Sarkar
Affiliation:
University of Dayton Research Institute, Metals and Ceramics, 300 College Park Avenue, Dayton, Ohio 45469-0170
I. Maartense
Affiliation:
Wright Laboratory, Materials Directorate, WL/MLPO, Wright-Patterson Air Force Base, Ohio 45433-6533
T.L. Peterson
Affiliation:
Wright Laboratory, Materials Directorate, WL/MLPO, Wright-Patterson Air Force Base, Ohio 45433-6533
Get access

Abstract

Superconducting composite samples were prepared by sintering a mixture of metallic silver and Bi(Pb)–Sr–Ca–Cu–O powder in air. For Ag contents between 0 and ∼15 vol. %, the bulk critical temperature was depressed as much as 40 K, and the relative proportion of the 2223 phase with respect to the 2212 phase was decreased, compared to the pure sample. However, as the Ag content was increased to between 19 and 70 vol. %, critical temperatures above 100 K were measured by transport and ac susceptibility techniques, and the relative proportions of the phases were restored to that of the pure sample. The limit of bulk superconductivity was reached at 73 vol. % Ag where the bulk critical temperature was ∼85 K. For higher Ag contents bulk superconductivity was not observed. Our results also show that sintering in air of silver-clad tapes containing Bi(Pb)–Sr–Ca–Cu–O powder, either by itself or with silver powder, need not be detrimental to the final superconductive properties.

Type
Articles
Information
Journal of Materials Research , Volume 7 , Issue 7 , July 1992 , pp. 1672 - 1678
Copyright
Copyright © Materials Research Society 1992

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1.Dou, S. X., Song, K. H., Liu, H. K., Sorrel, C. C., Apperley, M. H., Gouch, A. J., Savvides, N., and Hensley, D. W., Physica C 160, 533 (1989).CrossRefGoogle Scholar
2.Jin, S., Sherwood, R. C., Tiefel, T. H., Kammlott, G. W., Fastnacht, R. A., Davis, M. E., and Zahurak, S. M., Appl. Phys. Lett. 52, 1628 (1988).CrossRefGoogle Scholar
3.Tsudo, H., Miura, Y., Tsuchida, K., and Kato, A., Ceram. Int. 17, 5 (1991).CrossRefGoogle Scholar
4.Selim, R., Caton, R., Buoncristiani, A. M., Byvik, C. E., Edahl, R. A., Jr., and Wise, S., J. Appl. Phys. 67, 376 (1990).CrossRefGoogle Scholar
5.Matsumoto, Y., Hombo, J., Yamaguchi, Y., and Mitsunaga, T., Mater. Res. Bull. XXIV, 1469 (1989).CrossRefGoogle Scholar
6.Tripathi, R. B., Johnson, D. W., Jr., and Fleming, D. A., J. Mater. Res. 6, 455 (1991).CrossRefGoogle Scholar
7.Song, K-H., Liu, H. K., Dou, S. X., Sorrel, C. C., Savvides, N., and Bowden, G. J., J. Mater. Sci. Mater. Electron. 1, 30 (1990).CrossRefGoogle Scholar
8.Sarkar, A. K., Maartense, I., Peterson, T. L., and Kumar, B., J. Appl. Phys. 66, 3717 (1989).CrossRefGoogle Scholar
9.Morgan, P. E. D., Housley, R. M., Porter, J. R., and Ratio, J. J., Physica C 176, 279 (1991).CrossRefGoogle Scholar
10.Kase, J., Togano, K., Kumakura, H., Dietderich, D. R., Irisawa, N., Morimoto, T., and Maeda, H., Jpn. J. Appl. Phys. 29, L1096 (1990).CrossRefGoogle Scholar
11.Jin, S., van Dover, R. B., Tiefel, T. H., Graebner, J. E., and Spencer, N. D., Appl. Phys. Lett. 58, 868 (1991).CrossRefGoogle Scholar
12.Sarkar, A. K. and Maartense, I., Solid State Commun. 77, 121 (1991).CrossRefGoogle Scholar
13.Newnham, R. E., Skinner, D. P., and Cross, L. E., Mater. Res. Bull. XIII, 525 (1978).CrossRefGoogle Scholar
14.Gao, W., Li, S., Parrella, R., Rudman, D. A., and Vander Sande, J. B., J. Mater. Res. 5, 2633 (1990).CrossRefGoogle Scholar
15.Morgan, P. E. D., Piche, J. D., and Housley, R. M., Physica C 191, 179 (1992).CrossRefGoogle Scholar
16.Sarkar, A. K. and Maartense, I., unpublished results.Google Scholar
17.Sarkar, A. K., Maartense, I., Kumar, B., and Peterson, T. L., Supercond. Sci. Technol. 3, 199 (1990).CrossRefGoogle Scholar
18.Kozlowski, G., Maartense, I., Spyker, R., Leese, R., and Oberly, C. E., Physica C 173, 195 (1991).CrossRefGoogle Scholar
19.Yamada, Y., Obst, B., and Flukiger, R., Supercond. Sci. Technol. 4, 165 (1991).CrossRefGoogle Scholar