The infrared transmission spectra of four silicate glasses before and after exposure to water

Published online by Cambridge University Press:  31 January 2011

Roy D. Husung  and
Robert H. Doremus
Roy D. Husung
Affiliation:
Rensselaer Polytechnic Institute, Troy, New York 12180-3590
Robert H. Doremus
Affiliation:
Rensselaer Polytechnic Institute, Troy, New York 12180-3590
Get access

Abstract

The infrared transmission spectra of four silicate glasses were investigated. By using blown glass films, 1–2 μm thick, detailed infrared transmission spectra were generated over the 4000–180 cm−1 range, both before and after the films were exposed to water. The water had little effect on the spectra of the 70SiO2–20Na2O–10Al2O3 (mol %) and Pyrex compositions, but had a large effect on the spectra of the 70SiO2–30Na2O (mol %) and Corning 015 compositions. The Si–O nonbridged stretching band at ∼950 cm−1 and a largely overlooked bending band at ∼600 cm−1 were the bands most sensitive to hydration in the 70/30 and 015 compositions. Changes were also seen in the Si–O–Si bridged stretching bands at ∼1050 cm−1 and ∼770 cm−1. The water, however, had no effect on the dominant Si–O–Si bending band at 460 cm−1. It was also discovered that the 70/30 and 015 films reacted with the atmosphere to form a carbonate layer on their surface. This carbonate accounted for the 1450 cm−1 and 230 cm−1 bands seen in their infrared transmission spectra.

Type
Articles
Information
Journal of Materials Research , Volume 5 , Issue 10 , October 1990 , pp. 2209 - 2217
Copyright
Copyright © Materials Research Society 1990

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1Tomozawa, H. and Tomozawa, M., J. Non-Cryst. Solids 109, 311 (1989).CrossRefGoogle Scholar
2Olbert, B. H. and Doremus, R. H., J. Am. Ceram. Soc. 66 (3), 163 (1983).CrossRefGoogle Scholar
3Dunken, H. and Doremus, R. H., J. Non-Cryst. Solids 92, 61 (1987).CrossRefGoogle Scholar
4Bartholomew, R. F., Butler, B. L., Hoover, H. L., and Wu, C. K., J. Am. Ceram. Soc. 63 (9–10), 481 (1980).CrossRefGoogle Scholar
5Hench, L. L., J. Non-Cryst. Solids 19, 27 (1975).CrossRefGoogle Scholar
6Clark, D. E., Dilmore, M. F., Ethridge, E. C., and Hench, L. L., J. Am. Ceram. Soc. 59 (1–2), 62 (1976).CrossRefGoogle Scholar
7Clark, D. E., Dilmore, M. F., Ethridge, E. C., and Hench, L. L., Glass Technol. 18 (4), 121 (1977).Google Scholar
8Dilmore, M. F., Clark, D. E., and Hench, L. L., J. Am. Ceram. Soc. 61 (9–10), 439 (1978).CrossRefGoogle Scholar
9Zellmer, L. A. and White, W. B., in Scientific Basis for Nuclear Waste Management VIII, edited by Jantzen, C. M., Stone, J. A., and Ewing, R. C. (Mater. Res. Soc. Symp. Proc. 44, Pittsburgh, PA, 1985, p. 73.Google Scholar
10Sweet, J. R. and White, W. B., Phys. Chem. Glasses 10 (6), 246 (1969).Google Scholar
11Hanna, R. and Su, G-J., J. Am. Ceram. Soc. 47 (12), 597 (1964).CrossRefGoogle Scholar
12Florinskaya, V. A., in The Structure of Glass (Consultants Bureau, New York, 1960), Vol. 2, p. 154.Google Scholar
13Heaton, H. M. and Moore, H., J. Soc. Glass Technol. 411, 28T (1957).Google Scholar
14Jellyman, P. E. and Procter, J. P., J. Soc. Glass Technol. 39, 173T (1955).Google Scholar
15Park, J. W. and Chen, H., J. Non-Cryst. Solids 40, 515 (1980).CrossRefGoogle Scholar
16Ferraro, J. R. and Manghnani, M. H., J. Appl. Phys. 43 (11), 4595 (1972).CrossRefGoogle Scholar
17Ferraro, J. R., Manghnani, M. H., and Quattrochi, A., Phys. Chem. Glasses 13 (4), 116 (1972).Google Scholar
18Day, D. E. and Rindone, G. E., J. Am. Ceram. Soc. 45 (10), 489 (1962).CrossRefGoogle Scholar
19Kolesova, V. A., in The Structure of Glass (Consultants Bureau, New York, 1960), Vol. 2, p. 177.Google Scholar
20Harrick, N. J., Appl. Optics 10 (10), 2344 (1971).CrossRefGoogle Scholar
21Bansal, N. P. and Doremus, R. H., Handbook of Glass Properties (Academic Press, New York, 1986).Google Scholar
22Prassas, M., Phalippou, J., Hench, L. L., and Zarzycki, J., J. Non- Cryst. Solids 48, 79 (1982).CrossRefGoogle Scholar
23 Sadtler Research Laboratories, Sadtler High Resolution Spectra Inorganic and Related Compounds (Sadtler Research Laboratori Inc., Philadelphia, PA, 1965)Google Scholar
24Hanna, R., J. Phys. Chem. 69 (11), 3846 (1965).CrossRefGoogle Scholar
25 Joint Committee on Powder Diffraction Standards, Powder Diffraction File (JC on PDS, Philadelphia, PA, 1974).Google Scholar
26Doremus, R. H., in Materials Stability and Environmental Degretion, edited by Barkatt, A., Verink, E. D. Jr., and Smith, L. R. (Mater. Res. Soc. Symp. Proc. 125, Pittsburgh, PA, 1988), p. 177.Google Scholar
27Doremus, R. H., J. Non-Cryst. Solids 41, 145 (1980).CrossRefGoogle Scholar