Creation of locally selective mirror surface on 40BaO–40TiO2–20B2O3 glass by XeCl pulse laser irradiation

Published online by Cambridge University Press:  03 March 2011

Hirokazu Masai ,
Shintaro Mizuno ,
Takumi Fujiwara ,
Yasuhiko Benino ,
Takayuki Komatsu  and
Hiroshi Mori
Hirokazu Masai*
Affiliation:
Department of Applied Physics, Tohoku University, Aoba-ku, Sendai 980-8579, Japan
Shintaro Mizuno
Affiliation:
Department of Applied Physics, Tohoku University, Aoba-ku, Sendai 980-8579, Japan
Takumi Fujiwara
Affiliation:
Department of Applied Physics, Tohoku University, Aoba-ku, Sendai 980-8579, Japan
Yasuhiko Benino
Affiliation:
Department of Materials Science and Technology, Nagaoka University of Technology, Nagaoka, Niigata 940-2188, Japan
Takayuki Komatsu
Affiliation:
Department of Materials Science and Technology, Nagaoka University of Technology, Nagaoka, Niigata 940-2188, Japan
Hiroshi Mori
Affiliation:
Department of Applied Physics, Tohoku University, Aoba-ku, Sendai 980-8579, Japan
*
a) Address all correspondence to this author. e-mail: [email protected]
Get access

Abstract

Creation of mirror dots, localized areas of smooth surface with a shape of laser beam on a glass material, using a XeCl laser irradiation is reported. Laser irradiation of a 40BaO–40TiO2–20B2O3 sample heated to 300 °C induced a smooth and flat surface, where no scratches caused by a mechanical polishing were observed. The present finding indicates that the melting of the surface occurred by the combined effect of the heat-assistance and the increased absorption coefficient of TiO2. In the present system, the absorption coefficient in the ultraviolet region, which originates from TiO2, was found to increase with increasing temperature. The presented technique will open new possibilities in integrated optics; the surface of a small protruded or hollow area can be made smooth, which cannot be achieved by conventional mechanical polishing.

Keywords

AmorphousLaserOxide
Type
Articles
Information
Journal of Materials Research , Volume 22 , Issue 5 , May 2007 , pp. 1270 - 1274
Copyright
Copyright © Materials Research Society 2007

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1Takahashi, Y., Kitamura, K., Benino, Y., Fujiwara, T., and Komatsu, T.: Second-order optical nonlinear and luminescent properties of Ba2TiSi2O8 nanocrystallized glass. Appl. Phys. Lett. 86, 091110 (2005).CrossRefGoogle Scholar
2Honma, T., Benino, Y., Fujiwara, T., Komatsu, T., and Sato, R.: Technique for writing of nonlinear optical single-crystal lines in glass. Appl. Phys. Lett. 83, 2796 (2003).CrossRefGoogle Scholar
3Masai, H., Fujiwara, T., Benino, Y., and Komatsu, T.: Large second-order optical nonlinearity in 30BaO-15TiO2-55GeO2 surface crystallized glass with strong orientation. J. Appl. Phys. 100(2), 023526/1 (2006).CrossRefGoogle Scholar
4Kosaka, S., Benino, Y., Fujiwara, T., Dimitrov, V., and Komatsu, T.: Synthesis and nonlinear optical properties of BaTi(BO3)2 and Ba3Ti3O6(BO3)2 crystals in glasses with high TiO2 contents. J. Solid State Chem. 178, 2067 (2005).CrossRefGoogle Scholar
5Denton, E.P., Rawson, H., and Stanworth, J.E.: Vanadate glasses. Nature 173, 1030 (1954).CrossRefGoogle Scholar
6Mercier, R., Malugani, J.P., Fahys, B., and Robert, G.: Synthesis, crystal structure, and vibrational analysis of lithium hexathiohypodiphosphate (Li4P2S6). J. Solid State Chem. 43, 151 (1981).CrossRefGoogle Scholar
7Tatsumisago, M., Shinkuma, Y., and Minami, T.: Stabilization of superionic a-silver iodide at room temperature in a glass matrix. Nature 354, 217 (1991).CrossRefGoogle Scholar
8Pilkington, L.A.B.: The float glass process, in Proceedings of the Royal Society of London, Series A, Mathematical and Physical Science, Vol. 314, 1969, pp. 1–25.CrossRefGoogle Scholar
9Fujiwara, T., Ogawa, R., Takahashi, Y., Benino, Y., Komatsu, T., and Nishii, J.: Formation of gratings and two-dimensional photonic structures by laser-induced nanocrystallization. Phys. Chem. Glasses 43C, 213 (2002).Google Scholar
10Davis, K.M., Miura, K., Sugimoto, N., and Hirao, K.: Writing waveguides in glass with a femtosecond laser. Opt. Lett. 21, 1729 (1996).CrossRefGoogle ScholarPubMed
11Mizuno, S., Fujiwara, T., Benino, Y., and Komatsu, T.: Novel technique for fabrication of nanoparticle structures in KNbO3-TeO2 glass for photonic integrated circuits. Jpn. J. Appl. Phys. 45, 6121 (2006).CrossRefGoogle Scholar
12Tachiwana, K.: Colored glasses, in Glass Kogaku Handbook edited by Yamane, M., Yasui, I., Wada, M., Kokubu, Y., Terai, R., Kondo, K., Ogawa, S. (Asakura Syoten, Tokyo, Japan, 1999), p. 561.Google Scholar
13Park, H., Bakhtiiarov, A., Zhang, W., Baca, I.V., and Barbier, J.: Non-centrosymmetric Ba3Ti3O6(BO3)2. J. Solid State Chem. 177, 159 (2004).CrossRefGoogle Scholar
14Higazy, A.A., Hussein, A., Ewaida, M.A., and El-Hofy, M.: The effect of temperature on the optical absorption edge of the titanium oxide-doped soda-lime silica glasses. J. Mater. Sci. Lett. 7, 453 (1988).CrossRefGoogle Scholar
15Nakano, H. and Nakayama, T.: Mechanism associated with ArF and KrF excimer laser ablation of human tooth enamel. Reza Kenkyu 26, 37 (1998).Google Scholar