Carbonization and graphitization of polyimide Upilex

Published online by Cambridge University Press:  31 January 2011

Michio Inagaki ,
Kou-ichi Sakamoto  and
Yoshihiro Hishiyama
Michio Inagaki*
Affiliation:
Department of Materials Science, Toyohashi University of Technology, Tempaku-cho, Toyohashi, 440 Japan
Kou-ichi Sakamoto
Affiliation:
Department of Materials Science, Toyohashi University of Technology, Tempaku-cho, Toyohashi, 440 Japan
Yoshihiro Hishiyama
Affiliation:
Musashi Institute of Technology, 1–28–1, Tamazutsumi, Setagaya-ku, Tokyo, 158 Japan
*
a)Address correspondence to this author at Faculty of Engineering, Hokkaido University, Sapporo, 060 Japan.
Get access

Abstract

Two-step carbonization was found on a polyimide film, Upilex, similar to that observed on another polyimide, Kapton: large weight loss up to about 22 wt. % and linear shrinkage along the film surface to 30% in a narrow temperature range from 500 to 650 °C, and an additional small weight loss and shrinkage in a wide range between 700 and 1000 °C. The yield of carbonization agreed roughly with that calculated by assuming the release of non-carbon atoms as simple species of CO, O2, and N2. A 25 μm Upilex film yielded a relatively high degree of graphitization after heat treatment at 3000 °C: a layered structure under SEM, high magnetoresistance, and a sharp 002 x-ray diffraction peak at a d-spacing of 0.336 nm. The degree of graphitization was lower than for a similar Kapton film, which is attributed to the lack of flatness in the Upilex molecule. A very much lower degree of graphitization was observed for 50 μm Upilex films. This difference is tentatively attributed to constraints that must have influenced the orientation of the Upilex molecules near the surface of the films as they were formed.

Type
Articles
Information
Journal of Materials Research , Volume 6 , Issue 5 , May 1991 , pp. 1108 - 1113
Copyright
Copyright © Materials Research Society 1991

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1Hishiyama, Y., Yasuda, S., Yoshida, A., and Inagaki, M., J. Mater. Sci. 23, 3272 (1988).CrossRefGoogle Scholar
2Inagaki, M. and Hishiyama, Y., Colloq. Inter, sur les Composés Lamellaires, Pont-à-Mousson (March 1988), p. 1.Google Scholar
3Hishiyama, Y., Natsume, I., Ushijima, Y., Komada, O., and Inagaki, M., Materials Research Society Fall Meeting, Boston, MA (Dec. 1988), p. 231.Google Scholar
4Inagaki, M., Harada, S., Sato, T., Nakajima, T., Horino, Y., and Morita, K., Carbon 27, 253 (1989).CrossRefGoogle Scholar
5Buerger, A., Fitzer, E., Heym, M., and Terwisch, B., Carbon 13, 149 (1975).CrossRefGoogle Scholar
6Hishiyama, Y., Kaburagi, Y., and Inagaki, M., Chem. Phys. of Carbon, edited by Thrower, P. (in press).Google Scholar
7Yoshida, A. and Hishiyama, Y., Tanso, 1987 (No. 130), 110 (1987).CrossRefGoogle Scholar
8Murakami, M., Yasujima, H., Yumoto, Y., Mizogami, S., and Yoshimura, S., Solid State Commun. 45, 1085 (1983).CrossRefGoogle Scholar
9Watanabe, K., Murakami, M., and Yoshimura, S., Annual Meeting of Carbon Society of Japan, Sendai (Dec. 1988), p. 166.Google Scholar