Clay of apparent hydrothermal origin that fills amygdales in the Granby Basaltic Tuff (Lower Jurassic) of the Connecticut Valley was analyzed and found to consist of two exceptionally well-crystallized Fe-rich, trioctahedral 2:1 layer expandable phyllosilicates. Based on chemical and XRD analyses, the minerals were tentatively identified as saponite and vermiculite. The saponite exists predominately in the two-water hydration state, but also displays one- and three-water layer hydration states, which suggests heterogeneous layer charge distribution—a phenomenon not uncommon in smectites. The identity of the second clay remains equivocal, but XRD analyses, especially with regard to the swelling properties of the clay, indicate that it is a vermiculite. The well-crystallized nature of the Granby clay and the large size of the clay flakes (up to 1 mm) allowed us to use SEM/EDS X-ray imaging and spot analysis techniques in an attempt to detect chemical differences between the saponite and vermiculite. Results showed that the chemistry of individual crystals, within and among amygdales, was essentially uniform. This suggests that the saponite and vermiculite are chemically similar and that variations in their swelling properties result from other factors, such as crystal size, layer charge density, or charge localization within the unit layers. Crystal size differences in the Granby clay were observed with both the petrographic and scanning electron microscope. Changes in layer charge density or charge localization within unit layers could have been affected by the oxidation of Fe2+ to Fe3+, a transformation inferred from the green-to-brown color changes observed in the larger amygdales. The Granby clay is of special importance, because it is one of the few examples of a naturally occurring mixture of two well-crystallized, Fe-rich trioctahedral 2:1 layer expandable phyllosilicates with crystallochemical and swelling properties that appear to bridge the operational definitions for the smectite and vermiculite groups.

Batch reactor experiments were performed at 150°C, 175°C, and 200°C to determine the effect of high pH NaOH solutions on the mineralogy of the Opalinus shale. In these experiments, the change in solution quench pH at 25°C, solution composition, and mineralogy were monitored as a function of time for up to ≈40 days. Runs were performed in 50 ml titanium hydrothermal reactor vessels. Each reactor was charged with 0.5–5.0 g of the 80–200 mesh size fraction of Opalinus shale, and 25 ml of solution (0.1 and 0.01 M NaOH). The general sequence of reaction products observed under these high pH conditions include first the formation of analcime, followed by vermiculite, and finally Na-rectorite formation.

A series of reduced-charge (RC) hectorites were prepared by multiple heat (250°C) treatments of Mg-saturated hectorites (SHCa-1 ). Cation exchange capacity (CEC) measurements and alkylammonium exchange indicated that a decrease in layer charge occurred with each Mg-250 treatment. Chemical analyses showed that decreases in structural Li and increases in structural Mg contents coincided with charge reduction. Fluorescence measurements of adsorbed quinoline indicated that the hectorite surface was acidified during charge reduction; hydroxyl group deprotonation is a possible source for the acidity. Fourier transform infrared spectra (FTIR) indicated that the Mg-250 treatment induced the loss of structural Li and shifted the SiO stretch band to a position similar to that in talc. The relative intensities of the OH and SiO stretch bands in FTIR spectra suggest that some of the hydroxyl groups in hectorite were lost, possibly by deprotonation. However, thermogravimetric data (TG) reveal no significant difference in the hydroxyl contents of the hectorites.

The FTIR spectra, CEC, layer charge, chemical, and TG data all supported the view that Mg substitution for octahedral Li occurred which resulted in a more “talc-like” structure. Charge reduction in smectites is evidently a general phenomenon and can be induced by heat treatment with the proper exchangeable cation. The ability to reduce the charge of hectorites makes it possible to prepare a series of clays which vary in charge but lack structural Fe. Such RC smectites should be suitable for expandable clay mineral studies which utilize spectroscopic techniques that are sensitive to Fe content.

Thin section, XRD, SEM, and isotopic techniques have been used to study authigenic kaolinite occurring in reservoir sandstones of the Lower Permian Aldebaran Sandstone. Where the unit is no longer an active aquifer, kaolinite is an intermediate-stage phase, and is highly depleted in deuterium (δDSMOW = −115 to −99‰) and 18O (δ18OSMOW = +7.8 to +8.9‰), indicating that precipitation must have been from meteoric water. Deep penetration of this water is linked to Late Triassic deformation and uplift of the Denison Trough sequence, an event which led to exposure of the Aldebaran Sandstone by the Early Jurassic prior to its re-burial beneath Jurassic and Cretaceous sedimentary rocks. The same water was probably involved in the creation of secondary porosity in the interval.

Where the Aldebaran Sandstone is presently undergoing meteoric flushing, kaolinite is relatively enriched in deuterium (δDSMOW = −104 to −93‰) and 18O (δ18OSMOW = +11.7 to +14.6‰), reflecting precipitation largely from post-Mesozoic meteoric water which was isotopically heavier than the Mesozoic water involved in intermediate-stage kaolinite precipitation. This temporal shift in meteoric water isotopic composition is related to the northward drift of the Australian continent to lower latitudes since the Mesozoic Era.

Bentonite- and sepiolite-supported copper catalysts have been prepared either by adsorption of Cu(II) from aqueous solutions of copper nitrate at pH ~4.5 or by adsorption of a [Cu(NH3)4]2+ complex from an ammonia solution of CuSO4 at pH ~9.5. The structure and composition of the calcined preparations have been studied by X-ray diffraction, chemical analysis, and energy dispersive X-rays. Textural characteristics have derived from the analysis of the adsorption-desorption isotherms of N2. All catalysts have been tested for the dehydrogenation of methanol to methyl formate. For this reaction, bentonite-based catalysts were found to have very little activity, which indicates that copper located in the inter-lamellar spaces is inaccessible to methanol molecules. On the contrary, copper-sepiolite catalysts showed a very high specific activity even for those catalysts with a very low copper content. The chemical state of copper in the catalysts on-stream has been revealed by X-ray photoelectron spectroscopy and X-ray-induced Auger techniques. In most of the catalysts Cu+ is the dominant copper species.

Calcite crystals exposed to clay volatiles react with some components of these volatiles, giving rise to a variety of surface morphologies. F, Cl, and S in different proportions were detected by electron microprobe analysis of the calcite surfaces. Under identical experimental conditions, volatiles from every clay mineral examined caused a specific morphology and chemical composition of the calcite surfaces, but these varied with temperature of the calcite. Changes in pH values and mass spectra of the volatiles after passage through calcite demonstrate that even on rapid heating some clay volatile-calcite reactions occur at temperatures as low as 150°C. Species other than those detectable by electron microprobe analysis also participate in the reactions in which CO2 is liberated.

Hydroxy-interlayered vermiculite (HIV) is a ubiquitous phyllosilicate in the <0.05-mm fraction of sandy soils on the U.S. southeastern coastal plain. Extensive areas of soils with abundant HIV (i.e., peninsular Florida) have no detectable mica; yet the coarseness, platy habit, and nonexchangeable K associated with HIV grains suggest a mica precursor. The objectives of this study were: (1) to probe for mica zones (1.0-nm) within HIV grains, using high-resolution transmission electron microscopy (HRTEM), and (2) to determine intragrain elemental distributions via electron microprobe analysis (EMA). HIV grains from a Quartzipsamment medium-silt fraction, which contained no detectable mica by X-ray diffraction (XRD), were concentrated via high-density liquid separation. EMA transects and X-ray dot maps showed zonation or trends of K depletion near edges of some grains, with K2O contents ranging from trace levels to >40 g kg-1. Elemental oxide data indicated a dioctahedral phyllosilicate structure, with some octahedral substitution of Fe and Mg for Al. Intermittent 1.0-nm lattice-fringe images obtained by HRTEM supported the presence of mica zones within grains. There were no detectable 1.4-nm fringes, despite the dominance of a 1.4-nm XRD peak, indicating the instability of the HIV specimen under the electron beam. Results support a transformational link between mica and HIV in these soils. Rapid incursion and polymerization of Al following loss of K from mica may limit the extent of the vermiculite intermediate. The latter idea is consistent with the paucity of vermiculite in Florida soils. Traces of occluded mica may be the last remnants of the precursor grain. A sand-sized mica precursor would likely have weathered in place during the period when colloidal components such as kaolinite illuviated to deeper zones. Thus, the transformation product (HIV) would comprise a significant proportion of the <0.05-mm fraction persisting in sandy eluvial horizons.

The surface excesses of Na and Cl on synthetic imogolite and allophanes with varying Al/Si molar ratios in 0.10 M and 0.01 M NaCl solutions were determined using 22Na and 36Cl as ion probes. The point of zero net charge (PZNC) values ranged from 4.1 to 8.4, increasing with the Al/Si molar ratio for the allophanes, and was highest for imogolite (Al/Si = 2.01). The PZNC values were significantly lower than the point of zero charge (PZC) values previously determined by microelectrophoresis for the same material, indicating that Na resided within the shear plane to a greater extent than Cl. The PZNC values of allophanes were lower than their PZSE values, indicating that permanent charge existed in allophanes, and increased as Al/Si decreased. Conversely, the PZNC of imogolite was higher than its point of zero salt effect (PZSE) determined by potentiometric titration. Adsorption of Cl on imogolite from 0.1 and 0.01 M NaCl solutions below pH 8.4 and of Na from 0.1 M NaCl solutions between pH 5 and 8.4 exceeded the proton charge determined by potentiometric titration. There was no direct evidence of permanent charge in imogolite and excess Cl adsorption could not be entirely explained by simultaneous intercalation of Na and Cl. Isomorphic substitution of Al in tetrahedral sites was shown to increase with decreasing Al/Si by 27Al high-resolution solid-state nuclear magnetic resonance (NMR) spectra of allophanes, and was absent in imogolite. The chemical shifts of Al(4) and Al(6) were similar in allophanes (63.0–64.7 ppm and 6.1–7.8 ppm, respectively) and the chemical shift of Al(6) was 9.4 in imogolite.

The oxidation state of structural iron greatly influences the physical-chemical properties of clay minerals, a phenomenon that may have significant implications for pollutant fate in the environment, for agricultural productivity, and for industrial uses of clays. Knowledge of redox mechanisms is fundamental to understanding the underlying basis for iron's effects on clays. Past studies revealed that the extent of Fe reduction varied depending on the reducing agent used, but this variation may not have been a simple function of the reduction potential of the reducing agent. The objective of this study was to identify the relationship between the Fe reduction mechanism and free radical activity in the reducing agent. Several reducing agents and their mixtures with the Na-saturated, 0.5 to 2 μm size fraction of ferruginous smectite (SWa-1) were analyzed by electron spin resonance (ESR) spectroscopy to determine the presence of unpaired electrons or free radicals. Only Na2S2O4 exhibited paramagnetic free-radical behavior with a signal at about g = 2.011, which was attributed to the sulphoxylate (S02− ·) free radical. The free radical was labile in aqueous solution, and the ability of Na2S2O4 solution to reduce structural Fe in the smectite decreased with age of the solution and paralleled the disappearance of the free radical signal in the ESR spectrum. The paramagnetic species was preserved and enhanced if Na2S2O4 was added to the clay suspension, indicating that either the clay surface stabilized the SO2− · radical or the additional unpaired electrons were produced in the clay structure.

Hydrothermal tobelitic phyllosilicates modeled as ISII (R3) ordering with a minimum of 2–3% and a maximum of 6–8% interstratified smectite occur in veins and as replacement of fossils in hydrothermally altered black shale. These heavy metal-rich phyllosilicate veins formed during a Mesozoic-aged, regional-scale hydrothermal event that affected an area which encompasses the Mercur Au district (Wilson and Parry, 1990a, 1990b). Associated minerals include kaolinite, quartz, chlorite, Fe-oxides, I/S (R1, 45% smectite), and pyrite. N and O contents of NH4 phyllosilicates determined by microprobe analysis range from 0.19 to 1.78 and 48.6 to 52.9 elemental wt. %, respectively. Infrared absorption analysis indicates N occurs as NH4+. Very high O analyses are probably caused by contamination with kaolinite. A representative structural formula for the tobelitic material is [(NH4)0.36K0.36Na0.03]-(Al1.91Mg0.13Fe0.03)(Si3.21Al0.79)O10(OH1.88F0.12).

Correlation plots of data from microprobe analyses indicate an atypically high correlation between interlayer charge and octahedral layer charge and no correlation between (K+Na) and N. More typical correlations between N and (K+Na) and between interlayer charge and tetrahedral layer charge are obtained if 2–8% of a beidellitic smectite are factored out of the analyses. This amount of smectite is consistent with modeling of X-ray diffraction data using the computer program NEWMOD (Reynolds, 1985).

Possible sources of NH4 are from introduction by hydrothermal fluids or from thermal degradation of organic matter prevalent within the host rocks during low-grade metamorphism. The occurrence of NH4 phyllosilicate veins in unoxidized shale and the limited occurrence of NH4 phyllosilicates within the host shales suggests a hydrothermal source for the NH4.

Fe(II) and Fe(III) in various proportions were coprecipitated by NH3 at pH ≈ 11. The Fe(II)/Fe(III) ratio (x) was varied from 0.10 to 0.50. After stabilization by aging at pH ≃ 8 in anaerobic conditions, hydrous precipitates were characterized by electron microscopy, Mössbauer spectroscopy, and kinetics of dissolution in acidic medium. At any x value, all stable products exhibited the structure of (oxidized) magnetite. For x ≤ 0.30, two distinct species were coexisting: the one (“m”) was made up of ca. 4nm-sized particles with a low Fe(II) content (Fe(II)/Fe(III) ≈ 0.07), and the other (“M”) consisted of particles of larger, more or less distributed sizes, and composition Fe(II)/Fe(III) ≈ 0.33; “M” increased relative amount with increasing x. For x ≥ 0.35, “M” was the only constituent and its Fe(II)/Fe(III) ratio was equal to x. “M” is identified with (nonstoichiometric) magnetite, whereas “m” is likely to be an oxyhydroxide. Mechanisms of formation are discussed, and a phase diagram is proposed which schematizes the evolution of the coprecipitation products with x and with time. Addition of Fe(II) after the precipitation of Fe(III), instead of coprecipitation, yielded very similar results.

Selected Brazilian Oxisols were sampled and submitted to high-gradient magnetic separation (HGMS) to study the iron oxide-clay mineral associations. The soils, derived from four different parent materials, have mineralogy dominated mostly by hematite, goethite, and kaolinite. Gibbsite appears in most soil samples. The high-gradient magnetic separation showed good separation for some soils, as indicated by color differentiation and iron oxide segregation between magnetic and nonmagnetic fractions. Soils that showed a somewhat low surface area for the iron oxides associated with high phosphate adsorption were poorly separated by HGMS. This suggests a strong interaction between kaolinite and iron oxides, which would indicate a low estimation of their surface areas obtained by the difference method using BET-N2 data. A relative concentration of anatase and rutile in the magnetic portion of some of the samples was attributed to the presence of Fe, either as coatings on the crystals or within the structure of these two minerals.

Experimental alteration of volcanic glass has been carried out in distilled water at 200°C and 150°C. The formation and transformation processes of alteration products have been examined by scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray powder diffraction (XRD), infrared absorption analysis, and X-ray photoelectron spectroscopy. SEM and TEM clearly show that amorphous aluminum-silicate coatings with allophane particles precipitate on the surface of volcanic glass during the earliest alteration stage. Noncrystalline flaky and/or fibrous materials are formed from the allophane aggregates and from the amorphous coatings as new reaction products. The flaky and/or fibrous materials curl inward and transform into 100–500 nm circular smectite. The Al/Si atomic ratio of 1.09 for allophane decreases progressively to 0.65 for smectite through 0.86 for noncrystalline transitional material. The smectite has d(06) spacing of 1.497 Å and consists mainly of Si, Al, and small amounts of Fe, Ca, and Na.

Adsorption of cetylpyridinium chloride (CPC) onto kaolinite can be followed using the electroacoustic effect. The dynamic mobility, measured at a frequency of 1 MHz, varies from about −2 to +1 × 10−8 m2 V−1 s−1 in a number of steps, reflecting the adsorption of two separate layers, with the bilayer being more obvious, especially at pH 5–8. The behaviour at different pHs reflects the different charge characteristics of the basal cleavage planes and the crystal edges. When the amount of added CPC is equal to the cation exchange capacity of the clay, the kinetic charge changes from negative to positive and there is a pronounced break in the conductivity curve. It is also possible to estimate the edge to face area from such measurements and so obtain a measure of the aspect ratio of the clay crystallites. The (minimum) value for this clay is about 5:1.

Complex X-ray diffraction (XRD) profiles are described crystallographically by simulating XRD peaks for each phase, and adding the various elementary patterns to fit the experimental X-ray pattern. X-ray patterns of a ground muscovite and three polyphasic diagenetic I/S samples are fitted with this powerful, but time-consuming, technique. In the 6°–10°2θ CuKα range, the asymmetry of the muscovite peak is related to a very broad coherent scattering domain size (CSDS) distribution; for the I/S samples the even greater asymmetry is due to the presence of several phases with close, but distinct crystallographic characteristics (I/S, illite, and detrital mica).

A simulation-decomposition approach for modelling XRD patterns is introduced to describe quickly and accurately the various clay minerals (essentially mixed-layer illite/smectite and illite) present in a sedimentary series, and to follow their individual evolution during diagenesis. The theory for these simulations is described briefly. The influence of mixed-layer heterogeneity (the distribution of CSDS, and the distribution of smectite content) on the shape of X-ray peaks is shown theoretically to be minimal. Indeed, for both CSDS and smectite content, the important parameter for peak shape appears to be the mean value of the distribution and not its width and/or its shape. The theoretical limitations of the decomposition method are presented. Minor experimental limitations (reproducibility, experimental peak shape, discrimination) make this method a powerful and reliable tool to describe X-ray patterns. The method is used to show the simultaneous occurrence of three “illitic” phases in a sedimentary series from the Paris Basin. The respective evolution of the three phases is clearly evidenced by using this decomposition method. However, the precise identification of these different phases remains difficult to determine because of the difference in peak width between simulated and experimental X-ray patterns.

The rehydration and rehydroxylation properties of homoionic rectorites (saturated with Ca2+, Mg2+, Na+, or K+) were further investigated. The rehydration properties of the rectorite were characterized as follows: (1) basal spacings of rehydrated materials after heating above 500°C changed to 22.5 Å for H2O-complexes, 26.85 Å for ethylene glycol-complexes, and 27.65 Å for glycerol-complexes; (2) rehydrated Ca- and Mg-materials exhibited single layer hydrates at <50% RH, and rehydrated K-material showed double layer hydrates at 80% RH; (3) IR absorption spectra due to rehydrated H2O and OH exhibited the same or very close absorption intensities and frequencies to each other; (4) DTA-TGA curves of rehydrated materials indicated that the amount of rehydrated H2O approached about 4.2 wt. %, and about one-half of OH was rehydroxylated after heating at 800°C; and (5) interlayer cations of expandable layer components became non-exchangeable after heating above 500°C. These results suggest the following rehydration mechanism of rectorite: the interlayer cations migrate into the hexagonal holes of the SiO4 network by thermal dehydration. The cations migrated below 400°C easily return to the interlayer space and their original hydrated configurations have been recovered completely on rehydration. However, those migrated above 500°C are fixed to the hexagonal holes but water molecules are regained in the interlayer space. Consequently, electrostatic effects of interlayer cations on formation of water molecule layers are considerably reduced.

The <0.5-μm fraction of 120 samples from a lithologically complex Permian sedimentary sequence, underlying dolerite intrusive sheets, has been characterized by means of X-ray diffraction to establish I/S compositions as a function of temperature, lithology and time duration. Illitization has been active over the entire 210 m depth range and the clay data reflect both the local pattern of contact metamorphism and the more regional trend of heat flow during burial. A continuum exists in the illite proportions of the illite/smectite interstratifications with increasing distance from the intrusive sheet ranging from R = 3 with less than 5% smectite via R = 2 and R = 1 to R = 0 with up to 70% smectite. In the mixed-lithology section, individual component layers in the I/S within similar distance levels, but between contrasting lithologies, appear to vary only within a very restricted compositional range. In the massive mudstone strata, however, more silty parts contain I/S of a higher degree of ordering and lower expandability. Calcite contents are reflected in a higher rate of chlorite formation, but not in the I/S composition. A satisfactory inverse correlation was found between percent smectite in I/S and vitrinite reflectance in the lithologically complex section. R = 1 interstratifications are associated with a maximum vitrinite reflectance of 1.07–1.29 and R > 1 phases with 1.93–2.7, indicating that time duration is not a controlling factor in the illitization process in this facies. R = 0 interstratifications are present in a massive mudstone/siltstone sequence situated furthest from the igneous intrusives, and display vitrinite reflectance values of 1.42–1.52. No satisfactory explanations for this finding can be offered.

Products resulting from the reaction of toluene with Cu(II)-montmorillonite were analyzed using GC/MS, HPLC/MS, GPC, and FTIR methods. Numerous oligomers of toluene were observed, extending at least as high as the resolution limit (1500 g/mol) of the GPC column. The FTIR spectrum of the nonvolatile components of the extract was very similar to that of liquid toluene. GC/MS data on the volatile components revealed dimers, trimers, and a multitude of transmethylated products. Oligomerization proceeded via both ring-ring (i.e., polyphenyl) and ring-methyl linkages. The primary trans-methylated products were tert-butylbenzene and isopropylxylene, indicating a competition between ringand side-chain methylations. The side-chain substitutions cannot be explained in terms of the aromatic radical cation intermediate which typically forms in arene/clay reactions. A consideration of alkylbenzene reactions observed in various other media suggests that the present transmethylation reactions occur via a benzyl cation intermediate.

According to Lippmann (1977, 1982) wide compositional variations and excess enthalpies of mixing calculated with electrostatic models imply that clay minerals of variable composition are dis-equilibrium solids. However, recent ATEM analyses of illite samples indicate compositional homogeneity of single illite grains and limited compositional variations in sedimentary basins. Moreover, Lippmann's electrostatic model may be inadequate inasmuch as it neglects polarization energy which is known to be a significant component of lattice energy even in dominantly ionic structures. Contrary to the assumptions of Lippmann, I/S minerals have also been shown to undergo Ostwald ripening.

May et al. (1986) reported that smectites do not reversibly control equilibria and further argued that conceptual and experimental deficiencies inherent in the solubility method prevent the attainment and demonstration of equilibrium in experiments with complex aluminosilicates of variable composition. However, equilibrium may be assumed if: (1) steady states are approached from both under- and over-saturation, (2) the slopes of univariant lines representing mineral-solution equilibria are rational over a wide range of solution compositions and temperature, and (3) results are reproducible in experiments of long duration. Recent solubility studies of smectites, chlorites, and illites meet these criteria indicating that clay minerals of variable composition are true phases capable of attaining equilibrium.

Expandable fluorine micas were synthesized using talc and Na2SiF6 at 800°C for 2 hours in air, nitrogen, argon, and under vacuum. Gaseous SiF4, generated from Na2SiF6, and the resultant amorphous sodium silicofluoride formed during the reaction between talc and Na2SiF6 below 900°C are taking active part in the formation of expandable micas because the intensity of the 12.5 Å reflection of expandable micas decreases as the gas flow increases in the furnace. Expandable micas seem to be formed by the transformation from talc taking place without the entire disruption of the original atomic arrangement. This takes place with the loss of one Mg2+ from an octahedral site and by the intercalation of every two Na+ into the interlayer site of talc. Infrared absorption and thermal analyses show that expandable micas include a small amount of OH− in their structures.