In order to improve the removal efficiency of clays in oil refining, to explore the related factors and to clarify the removal mechanism of alkaline nitride, a series of modified clays was prepared to test removal of alkaline nitride from lubricating oil. After the addition of 1 wt.% FeCl3, the removal rate of alkaline nitride increased from 33.6% to 43.3%. Furthermore, the acidity and chlorine content did not exceed acceptable levels. The testing methods of N2 adsorption–desorption, particle-size distribution, Fourier-transform infrared spectroscopy and X-ray diffraction were conducted to verify the removal mechanism. The removal rate of alkaline nitride is mainly related to the density of Lewis acid sites. The Fourier-transform infrared spectra confirmed the existence of the complexation reaction. The basic nitrides were removed by chemical adsorption via Fe3+-complexation.

The surface coating of a gas reaction electrode with layered double hydroxides (LDHs) featuring various electrode catalyst activities was prepared via electrodeposition and the subsequent crystal growth of LDHs. LDH formation was confirmed by X-ray diffraction and Raman scattering measurements after subsequent crystal growth on respective electrodeposited precursor films in Ni-Fe and Zn-Al LDH systems. However, the crystal growth of LDHs in Ni-Mn and Cu-Mn systems was observed on the Mg-Al LDH-electrodeposited films. LDH films were also deposited on the surface of a carbon paper electrode with a rugged surface via electrodeposition and subsequent crystal growth. Using the prepared LDH-coated carbon paper electrodes, the electrode catalytic activity for the oxygen reduction reaction (ORR) was examined. For Ni-Mn, Ni-Al and Ni-Fe LDH-coated carbon paper electrodes, the threshold voltages of the ORR decreased. Hence, the LDHs electrodeposited on a gas reaction electrode have high electrochemical catalytic activity for the ORR.

Clays are used in the general production of earthen tiles. In this study, the production and characterization of earthen tiles from schist, a clayey rock formed by metamorphism of mudstone or shale, was investigated. The impact of tiles on atmospheric temperature through their absorption of the visible, near-infrared and far-infrared wavelength regions is evaluated. In particular, the absorption of ultraviolet and infrared radiation by the tiles was evaluated, as this could have beneficial applications for human health and the environment. UV-A radiation (320–400 nm) is not absorbed by the atmosphere, but schist materials absorb UV-A, which can contribute to melanoma formation (i.e. cancer). Field-emission scanning electron microscopy, X-ray fluorescence spectrometry and X-ray diffraction were used for the analysis of the schist materials. The tile-production stages of schist materials (drying, firing, water absorption rate, etc.) were tested at Hatipoglu Gunes Tile and Brick Industry, Inc. (Turkey). The tiles fired at 950°C and 1000°C comply with the industry standard compressive strength values for fired tiles (when converted to industry production conditions) and were 156.15 and 123.20 kg cm–2, respectively.

Clays are raw materials with properties that are necessary for the manufacture of ceramic tiles. The characteristics of clay ceramic raw materials may vary within the same mineral deposit. Clay blending promotes better use of clay reserves, thereby increasing the applicability and life cycle of raw materials. Therefore, it is important to understand the mechanisms controlling the firing of ceramic tiles. In this study, three different clays from a clay deposit were assessed and ten formulations were prepared using the mixture design method. The formulations were analysed using differential thermal and thermogravimetric analyses and dilatometric analysis. Subsequently, the most refractory and fluxing formulations were subjected to thermal tests under various heating rates, similar to the process used for the calculation of apparent sintering activation energy for the densification of clays and for pyroplasticity tests. It is suggested that a mineral deposit can be assessed based on activation energy and thermal kinetics, expanding the alternatives available to the miner through the planning of mixtures with various clays and thus reducing the energy costs of the industrial process.