Transformation of an aluminosilicate gel into pre-kaolinitic and pre-zeolite structures: effects of the solution media

Published online by Cambridge University Press:  09 July 2018

C. R. De Kimpe  and
H. Kodama
C. R. De Kimpe
Affiliation:
Agriculture Canada, Station de Recherches, 2560 Hochelaga Blvd, Sainte-Foy, Québec G1V 2J3
H. Kodama
Affiliation:
Agriculture Canada, Chemistry and Biology Research Institute, Ottawa K1A OC6, Canada
Get access Rights & Permissions [Opens in a new window]

Extract

Rodrique et al. (1972) reported that kaolinite was formed at 200°C from gels with an A12O3/(A12O3 + SiO2) weight ratio ⩽0·315 and pH values ranging from 4·8 to 5·8. At this temperature and using a gel with an A12O3/(A12O3 + SiO2) weight ratio >0.315, boehmite and pseudoboehmite, were obtained at pH values of up to 5·8. The latter minerals were also observed in the products formed under similar conditions at 175°C.

Unlike the situation under acidic conditions, where gel composition is important, the gel/solution ratio becomes critical under alkaline conditions. When the gel/solution ratio is low, zeolites are produced from a gel with a weight ratio between 0·3 and 0·5 in the presence of NaOH at 130-170°C (De Kimpe, 1976). When the gel/solution ratio is high, kaolinite instead of zeolites is formed under similar conditions (De Kimpe, 1969, 1976). For an intermediate gel/solution ratio, smectite is produced from a gel with a weight ratio of 0.4 in the presence of NaOH at 175°C In the presence of KOH, however, kaolinite is the only crystalline product formed under similar pH and temperature conditions (De Kimpe et al., 1981).

Type
Notes
Information
Clay Minerals , Volume 19 , Issue 2 , April 1984 , pp. 237 - 242
Copyright
Copyright © The Mineralogical Society of Great Britain and Ireland 1984

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

Cloos, P., Leonard, A.J., Moreau, J.P., Herbillon, A. & Fripiat, J.J. (1969) Structural organization in amorphous silico-aluminas. Clays Clay Miner. 17, 279–287.Google Scholar
De Kimpe, C.R. (1969) Crystallization of kaolinite at low temperature from an alumino-silicic gel. Clays Clay Miner. 17, 37–38.CrossRefGoogle Scholar
De Kimpe, C.R. (1976) Formation of phyllosilicates and zeolites from pure silica-alumina gels. Clays Clay Miner. 24, 200–207.Google Scholar
De Kimpe, C.R., Gastuche, M.C. & Brindley, G.W. (1964) Low-temperature synthesis of kaolin minerals. Am. Miner. 49, 1–16.Google Scholar
De Kimpe, C.R., Kodama, H. & Rivard, R. (1981) Hydrothermal formation of a kaolinite-like product from non-crystalline aluminosilicate gels. Clays Clay Miner. 29, 446–450.Google Scholar
Klug, H.P. & Alexander, L.E. (1974) X-ray Diffraction Procedure for Polycrystalline and Amorphous Materials. 2nd edition, 791–859. John Wiley and Sons, New York.Google Scholar
Leonard, A., Suzuki, S., Fripiat, J.J. & De Kimpe, C.R. (1964) Structure and properties of amorphous silico-aluminas. I—Structure from X-ray fluorescence spectroscopy and IR spectroscopy. J. Phys. Chem. 68, 2608–2617.Google Scholar
Rodrique, L., Poncelet, G. & Herbillon, A. (1973) Importance of the silica subtraction process during the hydrothermal kaolinization of amorphous silico-aluminas. Proc. Int. Clay Conf. Madrid, 187–198.Google Scholar
White, E., McKinstry, H. & Bates, T.F. (1958) Crystal chemical studies by X-ray fluorescence. Proc. 7th Ann. Conf. X-ray Anal. Denver 2, 239–245.Google Scholar