Physical and mechanical characteristics of cement mortars and concretes with addition of clinoptilolite from Beli Plast deposit (Bulgaria), silica fume and fly ash

Published online by Cambridge University Press:  09 July 2018

V. Lilkov ,
I. Rostovsky  and
O. Petrov
V. Lilkov*
Affiliation:
University of Mining and Geology “St. Ivan Rilski”, Sofia, Bulgaria
I. Rostovsky
Affiliation:
Central Laboratory of Physico–Chemical Mechanics, Bulgarian Academy of Sciences, Sofia, Bulgaria
O. Petrov
Affiliation:
Institute of Mineralogy and Crystallography, Bulgarian Academy of Sciences; Sofia, Bulgaria
*
*E-mail: [email protected]
Get access Rights & Permissions [Opens in a new window]

Abstract

Cement mortars and concretes incorporating clinoptilolite, silica fume and fly ash were investigated for changes in their physical and mechanical properties. It was found that additions of 10% clinoptilolite and 10% Pozzolite (1:1 mixture of silica fume and fly ash) were optimal for improvement of the quality of the hardened products, giving 8% and 13% increases in flexural and compressive strength respectively. The specific pore volume of the mortars incorporating zeolite decreased between the 28th and 180th day to levels below the values for the control composition due to the fact that clinoptilolite exhibits its pozzolanic activity later in the hydration. In these later stages, pores with radii below 500 nm increased at the expense of larger pores. The change in the pore-size distribution between the first and sixth months of hydration occurs mostly in the mortars with added zeolite.

Keywords

cementpozzolanpozzolanic activitypozzolanic additivezeolitemortarconcretecement–zeolite mortarclinoptilolitesilica fumefly ashBeli Plast depositBulgaria
Type
Research Article
Information
Clay Minerals , Volume 46 , Issue 2 , June 2011 , pp. 213 - 223
Copyright
Copyright © The Mineralogical Society of Great Britain and Ireland 2011

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

Akira, N., Koichi, A. & Heizaburo, I. (2001) Effects of replacement ratio and grading of natural zeolite on compressive strength and freezing and thawing resistance of concrete. Japan Cement Association, Proceedings of Cement & Concrete, 55, 290–295.Google Scholar
Baldino, N., Gabriele, D., Frontera, P., Crea, F. & de Cindio, B. (2008) Rheological influence of synthetic zeolite on cement pastes. Pp. 758–760 in. The XV International Congress on Rheology — AIP Conference Proceeding, 1027 (Co, A., Leal, G.L., Colby, R.H. & Giacomin, J.A., editors). Monterey, California, USA.Google Scholar
Dimitrova, E. & Lilkov, V. (1996) Effect of active mineral admixtures on the rheological properties of cement pastes. XII International Congress on Rheology (Ait-Kadi, A., Dealy, J.M., James, D.F. & Williams, M.C., editors), August 18-23, Quebec City, Canada.Google Scholar
Janotka, I. & Krajči, V. (2000) Utilization of natural zeolite in Portland pozzolan cement of increased sulfate resistance. Journal of American Concrete Institute, 192, 23–238.Google Scholar
Janotka, I., Krajči, L. & Dzivak, M. (2003) Properties and utilization of zeolite-blended Portland cements. Clays and Clay Minerals, 51, 616–624.Google Scholar
Kontori, E., Perraki, T., Tsivilis, S. & Kakali, G. (2009) Zeolite blended cements: evaluation of their hydration rate by means of thermal analysis. Journal of Thermal Analysis and Calorimetry, 96, 993–998.Google Scholar
Langan, B.W., Weng, K. & Ward, M.A. (2002) Effect of silica fume and fly ash on heat of hydration of Portland cement. Cement and Concrete Research, 32, 1045–1051.CrossRefGoogle Scholar
Li, G-Z., Feng, N-Q. & Zang, X-W. (1990) High-strength and flowing concrete with a zeolitic mineral admixture. Journal of Cement, Concrete and Aggregates, 12, 61–69.Google Scholar
Lilkov, V. & Stoitchkov, V. (1996) Efect of the “Pozzolit” active mineral additive on the properties of cement mortars and concretes. Part 2: Pozzolanic activity. Cement and Concrete Research, 26, 1073–1081.Google Scholar
Lilkov, V., Dimitrova, E. & Petrov, O.E. (1997) Investigation on the hydration of cement containing fly ash and silica fume: the first 24 hours. Cement and Concrete Research, 27, 577–588.CrossRefGoogle Scholar
Marsh, B. & Day, R. (1988) Pozzolanic and cementitious reactions of fly ash in blended cement pastes. Cement and Concrete Research, 18, 301–310.Google Scholar
Mazloom, M., Ramezanianpour, A.A. & Brooks, J.J. (2004) Effect of silica fume on mechanical properties of high-strength concrete. Cement and Concrete Composites, 26, 347–357.CrossRefGoogle Scholar
Mertens, G., Snellings, R., Van Balen, K., Bicer-Simsir, B., Verlooy, P. & Elsen, J. (2009) Pozzolanic reactions of common natural zeolites with lime and parameters affecting their reactivity. Cement and Concrete Research, 39, 233–240.Google Scholar
Min-Hong, Z. & Odd, E.G. (1991) Effect of silica fume on pore structure and chloride diffusivity of low porosity cement pastes. Cement and Concrete Research, 21, 1006–1014.Google Scholar
Persson, B. (1998) Seven-year study on the effect of silica fume in concrete. Advanced Cement Based Materials, 7, 139–155.Google Scholar
Qing, Y., Zenan, Z., Deyu, K. & Rongshen, C. (2007) Influence of nano-SiO2 addition on properties of hardened cement paste as compared with silica fume. Construction and Building Materials, 21, 539–545.Google Scholar
Robins, P. & Austin, S. (1986) Bond of lightweight aggregate concrete containing condensed silica fume, fly ash silica fume, slag and natural pozzolanas in concrete. American Concrete Institute, Special Publication, SP-91, 941–951.Google Scholar
Şahmaran, M. (2008) The effect of replacement rate and fineness of natural zeolite on the rheological properties of cement-based grouts. Canadian Journal of Civil Engineering, 35, 796–806.Google Scholar
Şahmaran, M., Özkan, N., Keskin, S.B., Uzal, B., Yaman, I.Ö. & Erdem, T.K. (2008) Evaluation of natural zeolite as a viscosity-modifying agent for cementbased grouts. Cement and Concrete Research, 38, 930–937.Google Scholar
Sánchez de Rojas, M.I. & Frias, M. (1996) The pozzolanic activity of different materials, its influence on the hydration heat in mortars. Cement and Concrete Research, 26, 203–213.Google Scholar
Snellings, R., Mertens, G. & Elsen, J. (2010) Calorimetric evolution of the early pozzolanic reaction of natural zeolites. Journal of Thermal Analyses and Calorimetry, 101, 97–105.Google Scholar
Song, H-W., Pack, S-W., Nam, S.-H., Jang, J-C. & Saraswathy, V. (2010) Estimation of the permeability of silica fume cement concrete. Construction and Building Materials, 24, 315–321.Google Scholar
Stoitchkov, V., Abadjiev, P., Lilkov, V. & Vasileva, V. (1996) Effect of the “Pozzolit” active mineral admixture on the properties of cement mortars and concretes. Part 1: Physical and mechanical properties. Cement and Concrete Research, 26, 1066–1072.Google Scholar
Toutanji, H. & El-Korchi, T. (1995) The influence of silica fume on the compressive strength of cement paste and mortar. Cement and Concrete Research, 25, 1591–1602.Google Scholar
Wild, S., Sabir, B.B. & Khatib, M. (1995) Factors influencing strength development of concrete containing silica fume. Cement and Concrete Research, 27, 1567–1580.Google Scholar