X-Ray Fractography On Fatigue Fracture Surfaces of Aisi 4340 Steel*

Published online by Cambridge University Press:  06 March 2019

Yukio Hirose
Affiliation:
On leave from Kanazawa University, Japan Department of Civil Engineering and Material Research Center, Northwestern University, EvanstonILL., 60201, U.S.A.
Zenjlro Yajima
Affiliation:
On leave from Kanazawa University, Japan Department of Civil Engineering and Material Research Center, Northwestern University, EvanstonILL., 60201, U.S.A. On leave from Kanazawa Institute of Technology, Japan
Toshio Mura
Affiliation:
On leave from Kanazawa University, Japan Department of Civil Engineering and Material Research Center, Northwestern University, EvanstonILL., 60201, U.S.A.
Get access

Extract

The X-ray fractographic technique was applied to fatigue fracture surfaces of tempered AISI 4340 steel. Residual stresses and half-value breadths were measured by the X-ray diffraction.

In the present paper, the residual stresses and plastic strains on fatigue fracture surfaces and some parameters in the fracture mechanics were investigated. A simple model of mechanics was proposed to explain these experimental results.

Type
Research Article
Copyright
Copyright © International Centre for Diffraction Data 1985

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

Footnotes

*

This work was supported by NSF-MRL Grant DMR-8216972 and partly by U.S. Army Research Grant DAAG-29-85-K-0134.

References

1. Bilby, B.A., Cottrel, A.H. and Swinden, K.H., “The Spread of Plastic Yield from a Notch)” Proc. Roy. Soc., A272: 304 (1963).Google Scholar
2. Committee on Mechanical Behavior of Materials, “Standard Method of X-Ray Stress Measurement”, J. Soci. Mat. Sci. Jap., 13 (1973).Google Scholar
3. Hirose, Y., Yajima, Z., and Tanaka, K., “X-Ray Fractography on Stress Corrosion Cracking of High Strength Steel”, Advances in X-ray Analysis, 27: 213 (1984).Google Scholar
4. Hirose, Y., Yajima, Z., and Tanaka, K., “X-Ray Fractographic Approach to Fracture Toughness of AISI. 340 Steel”, Advances in X-ray Analysis, 28: 289 (1985).Google Scholar
5. Yajima, Z., Hirose, Y., and Tanaka, K., “X-Ray Diffraction Observation of Fracture Surfaces of Ductile Cast Iron”, Advances in X-ray Analysis, 26: 291 (1983).Google Scholar
6. Sekita, Y., Kodama, S., and Misawa, H., “X-Ray Fractography on Fatigue Fractured Surface”, J. Soci. Mat. Sci. Jap., 32: 258 (1983).Google Scholar
7. Tanaka, K., and Hatanaka, H., “Residual Stress Near Fatigue Fracture Surfaces of High Strength and Mild Steels Measured by X-Ray Method”, J. Soci. Mat. Sci. Jap., 31: 215 (1982).Google Scholar
8. Yajima, Z., Hirose, Y., and Tanaka, K., “X-Ray Diffraction Observation of Fractured Surface of Fracture Toughness Specimen of High Strength Steel”, J. Jap. Soc. Strength and Fracture of Materials, 16: 59 (1981).Google Scholar
9. Levy, N., Marcal, P. v., Ostergren, W.J., and Rice, J.R., “Small Seal Yielding Near a Crack in Plane Strain: A Finite Element Analysis”, .Int. J. Frac. Mech., 7: 143 (1971).Google Scholar