Well developed mullite whiskers were obtained by heating compacts of kaolin and 2 wt.% sodium pyrophosphate powder at 1350ºC for 10 h, with or without a small addition of aluminium sulphate. Without aluminium sulphate, mullite whiskers were obtained with an aspect ratio of >8 and reasonably uniform diameter (~0.05–0.3 μm). When aluminium sulphate additions were employed a mass of relatively well developed and interlocked whisker-shaped crystals were produced, with an aspect ratio of >10 (~0.05–0.3 μm in diameter). Larger whiskers were also observed, with aspect ratio of >25 (~0.2–0.5 μm in diameter).

Unusual irregular galena crystals and whiskers were found in close proximity in some druse cavities from the Gradishtc hydrothcrmal lead-zinc deposit in the Madan ore district, Bulgaria. The following crystal forms were observed: (1) straight thin [110] whiskers and thicker needles; (2) kinked whiskers; (3) curvilinear whiskers; (4) complex tortuous whiskers composed of segments with varying directions—[110], [100], [211], (5) thicker irregular elongated crystals. Combinations of these forms occur also. The detailed SEM study shows that all these formations are single crystals of extreme anisometricity, bounded by octahedral and cubic faces as well as by stepped surfaces of these forms. Surface structures such as longitudinal grooves, jagged edges, striations, pits, etc., are abundant.

It is assumed that these highly non-equilibrium crystals with large surface areas were formed through rapid directed growth from highly supersaturated solutions under a diffusional regime. Such special environments arose in the ore veins as a result of tectonic shocks leading locally to a drastic volume increase and P and T decrease in the solutions.

Remarkable single crystal galena formations in the unique form of cylindrical or steep conical ‘pillars’ with ‘capitals’ of small rhombododecahedral single crystals of sphalerite, are described. It is suggested that the pillars result from a highly specific process of anisotropic mineral dissolution controlled by a system of internal channels in the original skeletal crystals and represent a kind of dissolution whiskers.

We report here the fabrication and characterization of ultra-long AlN whiskers by physical vapor transport method. The obtained whiskers are 1–3 µm in diameter and up to millimeters in length. The whiskers grow along the [0001] crystallographic direction and are well crystallized. They exhibit a strong ultraviolet emission at 345 nm, the shortest wavelength reported in AlN whiskers or nanowires. Our results indicate that these large scales of AlN whiskers are less contaminated by oxygen and other impurities compared with the previously reported ones, which may find wide applications in fabricating ultraviolet optoelectronic devices.

Understanding the growth of whiskers or high aspect ratio features on substrates can be aided when the crystallography of the feature is known. This study has evaluated three methods that utilize electron backscatter diffraction (EBSD) for the determination of the crystallographic growth direction of an individual whisker. EBSD has traditionally been a technique applied to planar, polished samples, and thus the use of EBSD for out-of-surface features is somewhat more difficult and requires additional steps. One of the methods requires the whiskers to be removed from the substrate resulting in the loss of valuable physical growth relationships between the whisker and the substrate. The other two techniques do not suffer this disadvantage and provide the physical growth information as well as the crystallographic growth directions. The final choice of method depends on the information required. The accuracy and the advantages and disadvantages of each method are discussed.

The whiskers spontaneously grown in Cd–Mg–Yb alloy containing icosahedral quasicrystal as dominant phase have been investigated by electron microscopy. It is found that: (i) the whiskers are mainly composed of Cd with growth direction along . CdO particles are frequently observed on surfaces of whiskers and the alloy, indicating the importance of the oxidation process during the whisker growth; (ii) there exist four types of orientation relationship between Cd and CdO. The interfaces between them are shown to accommodate large lattice misfit, which is well explained by near coincidence site lattice model; (iii) nanosized Cd particles are observed to aggregate around the whisker root, providing a convincing experimental evidence for the long-range atomic diffusion. Our study offers a unique opportunity to unveil the relationship between unstability of quasicrystal structure and whisker formation and may have some implications for oxidation process of metals.

Complementary to our first paper on the origin of threefold contrast on SiC high resolution transmission electron microscopy (HRTEM) images, we now provide an example of threefold contrast produced by a stacking layer sequence which corresponds to one unit cell of the 9R polytype.