Transmission electron microscope samples of two types of metal matrix composites were prepared using both traditional thinning methods and the more novel focused ion beam miller. Electropolishing methods were able to produce, very rapidly, thin foils where the matrix was electron transparent, but the ceramic reinforcement particles remained unthinned. Thus, it was not possible in these foils to study either the matrix-reinforcement interface or the microstructure of the reinforcement particles themselves. In contrast, both phases in the composites prepared using the focused ion beam miller thinned uniformly. The interfaces in these materials were clearly visible and the ceramic reinforcement was electron transparent. However, microstructural artifacts associated with ion beam damage were also observed. The extent of these artifacts and methods of minimizing their effect were dependent on both the materials and the milling conditions used.

Reliability of thermal barrier coatings (TBC) hinges on the adhesion of a thermally grown oxide scale to an insulative ceramic topcoat and an underlying metallic bondcoat. The width of the scale and its interfaces makes transmission electron microscopy (TEM) an appropriate tool for its analysis. However, specimen preparation has proven to be a challenging obstacle leading to a dearth of TEM research on TBCs. A new approach to cross-section TBC TEM specimen preparation is described. The principal advantages of this technique are reproducibility, reduced specimen damage, and time savings resulting from decreased ion milling. This technique has been successfully applied to numerous TBC specimens with various thermal histories.