To apply hydrotalcites more effectively to the problem of dye wastewater, the effects of divalent metal ions on the structure and stability of hydrotalcites, especially on their photocatalytic activity, were compared. In the present study, M/Cr hydrotalcites (M3Cr-CO3-LDHs) (in which M = Mg, Co, Ni, Cu, Zn), where the M/Cr molar ratio was 3, were prepared by the co-precipitation method. The structures and properties were characterized using powder X-ray diffraction (XRD), Fourier-transform infrared spectroscopy (FTIR), thermogravimetric-differential thermal analysis (TG-DTA), and UV-Visible diffuse reflectance spectroscopy (UV-Vis DRS). The results showed that five kinds of M3Cr-CO3-LDHs were synthesized successfully, and the layered structure of the samples obtained was regular and the crystal phase was single. When methylene blue (MB) solution was exposed to ZnCr-CO3-LDHs, H2O2, and visible light irradiation, more than 90.67% of the methylene blue (MB) was removed after 140 min. The photocatalytic activity of the samples was in the order: Co3Cr-CO3-LDHs > Mg3Cr-CO3-LDHs > Cu3Cr-CO3-LDHs > Zn3Cr-CO3-LDHs > Ni3Cr-CO3-LDHs. The results of a catalytic mechanism study showed that photocatalytic degradation of MB involved a demethylation reaction, with the reactive species containing •O2-, •OH, and h+.

Composite materials include various components with different structures, which cooperatively increase their properties and extend their application. In this study, the graphitic carbon nitride (g-C3N4) guest material was assembled into the porous of the SiO2 aerogel, which was prepared during the gel process. By this way, the g-C3N4 could be absolutely encapsulated into the porous of the disordered porous SiO2 aerogel. The prepared g-C3N4/SiO2 composite had a loose porous structure and exhibited the much higher photocatalytic activity to the photodegradation of rhodamine B (RhB) under visible light. The disordered porous structure enhanced photocatalytic activity, and the degradation rate reached to 96.42% in 90 min under the irradiation of visible light, which could be attributed to its high surface area and effective electron–hole separation rate. The catalyst had the much higher stability and could be easily recycled utilization. The prepared composites could be applied to degrade organic pollutants in wastewater.

Dyeing wastewater has caused serious environmental problems nowadays. In this work, nickel–phosphorus plating–titanium dioxide (Ni-P-TiO2) electroless plating polyimide (PI) fabric was fabricated as an excellent visible light response composite. First, polyaniline (PANI) was in situ polymerized on the surface of the PI fabric. Second, PANI reduced palladium ions to be active seeds for initiating electroless plating of Ni-P-TiO2 layer. Finally, the Ni-P-TiO2/PANI/PI fabric with all-in-one structure was prepared, which can effectively overcome the drawbacks of poor loading fastness and insensitivity to visible light response. It was characterized by scanning electron microscopy, energy-dispersive spectroscopy, X-ray diffraction, X-ray photoelectron spectroscopy, thermogravimetric analysis, and ultraviolet–visible diffuse reflectance spectroscopy. The photocatalytic activity was evaluated by degrading reactive blue 19, methylene blue, and reactive red (M-3BE) under visible light irradiation. The results show that the degradation rates of the all three dyes were over 91% with robust cycle stability for repeated 5 cycles of use. The possible photocatalytic degradation mechanism of fabrics was also proposed based on free radical and hole removal experiments.

Ni2P/ZnS and Ni2P/CdS core/shell composites were synthesized using a simple two-step route at a low temperature. We used X-ray powder diffraction, scanning electron microscopy, energy dispersive spectroscopy, and so on to characterize their composition, structure, and morphology. The characterized results show that Ni2P/ZnS and Ni2P/CdS core/shell composites consist of Ni2P microsphere core and ZnS (or CdS) nanostructure shell, and CdS nanorods and ZnS nanoparticles are deposited on the surface of Ni2P microspheres, respectively. Then choosing methylene blue (MB) as a typical organic dye, the photocatalytic degradation activities of Ni2P/ZnS and Ni2P/CdS are investigated, which exhibit a good photocatalytic activity. When the concentration of MB solution is 1 × 10−5 mol/L and the mass of the added photocatalyst is 0.05 g, it is found that two composites have enhanced photocatalytic degradation ratios (89 and 78%) compared to that of Ni2P microsphere (65%), which might be due to the effective separation of photogenerated electron-hole pairs.

The uniform Ag@AgBr core–shell microspheres were synthesized by a very facile wet-chemical route in aqueous solution, including a reduction process to prepare sphere-like Ag core and a deposition process to synthesize AgBr shell. X-ray diffraction, x-ray photoelectron spectroscopy, field emission scanning electron microscopy, and high-resolution transmission electron microscopy results confirmed the formation of Ag@AgBr core–shell heterostructures which had been achieved by this simple method. Field emission scanning and high-resolution transmission electron microscopy results of the as-synthesized Ag@AgBr composite revealed that AgBr particles were deposited on the surface of sphere-like Ag core. Under visible-light (λ > 420 nm) and real sunlight irradiation, the as-synthesized Ag@AgBr samples exhibit high activity and good stability for the photodegradation of Rhodamine 6G (R6G) in water. The present work suggests that the as-synthesized Ag@AgBr core–shell microsphere can be applied as a visible light-activated photocatalyst in efficient utilization of solar energy for treating water polluted by some chemically stable azo dyes in environment. The enhanced photocatalytic performance of the as-synthesized Ag@AgBr composite might be attributed to accelerated separation efficiency of electron–hole pairs on the interface of the Ag@AgBr hybrids and improved visible-light absorption abilities when AgBr is coupled with Ag.

Zn3(VO4)2 nanorods with visible light-driven photocatalytic activity were prepared by hydrothermal reaction and characterized by x-ray diffraction, Fourier transform infrared, scanning electron microscopy, x-ray photoelectron spectroscopy, UV–vis diffuse reflectance spectra, and Brunauer–Emmett–Teller surface area and pore size analyzer. The Zn3(VO4)2 nanorods consisted of rods with a thickness of approximately 30 nm, length in the range 400–600 nm, and width in the range 150–250 nm. The photocatalytic degradation activities for methylene blue (MB) and 4-nitrophenol (4-NP) over the Zn3(VO4)2 nanorods were studied in detail. The photocatalytic activity of the as-prepared photocatalyst for MB and 4-NP in visible light under the same conditions was about 3.5 times and 2.5 times higher than that of N–TiO2, respectively. The main active species in the photodegradation come from •OH, and the photogenerated electrons also partly involved in the photocatalytic degradation process, in which the •OH radicals formed were in proportional to the light illumination time obeying zero-order reaction rate kinetics.

The ZrO2 and graphitic carbon nitride (g-C3N4) composite photocatalyst has been prepared by calcination process and hydrothermal treatment. The photocatalyst was characterized by x-ray diffraction, scanning electron microscopy, x-ray photoelectron spectroscopy, UV–vis diffuse reflection spectroscopy, Brunauer–Emmett–Teller and photoluminescence spectra. The photocatalytic activity of the photocatalysts was evaluated by degradation of methylene blue under visible light irradiation. The results showed that the activity of the composite photocatalyst ZrO2/g-C3N4 for photodegradation of MB is much higher than that of either pure g-C3N4 or ZrO2, which is ascribed to the effective electron–hole separation based on the photoluminescence spectra. The •O2− might be the main active species in MB photodegradation, and the •OH and photogenerated electrons are also partly involved in the process of photocatalytic degradation.

We report herein the crystal growth of ZnO nanoparticles by the foam fractionation method. In this study, the vertical column height of the foam was fixed and the velocity of the sparging air was varied, and the effect of foam flow rate on the synthesis of ZnO was investigated. The obtained ZnO consisted of aggregated platelets and had differing ultraviolet absorbances. The as-synthesized ZnO was hydrophobic because of the interaction between the anionic head groups of sodium dodecyl sulfate (SDS) and the ZnO under the precipitation conditions. The long chain of the SDS molecule was the cause of hydrophobicity. The contact angle of water was in the range of 95–105° for the obtained ZnO/SDS surface. The photocatalytic degradation efficiency of the as-synthesized (ZnO/SDS) and the calcined ZnO was investigated for methylene blue, and the calcined ZnO retained its activity even after three recycles.