MnOx –CeO2/t-ZrO2 catalyst was prepared by impregnation of nanotetragonal zirconia. The NO conversion of 5 wt% MnOx –CeO2/t-ZrO2 catalyst was 68.1% at 100 °C while that of 30 wt% MnOx –CeO2/t-ZrO2 catalyst was 97.4%. The x-ray diffraction, Brunner–Emmet–Teller measurements (BET), and H2-TPR showed surface properties of the prepared catalysts were good for selective catalytic reduction reactions. X-ray photoelectron spectroscopy analysis indicated that Mn4+ and Ce4+ oxidation states were predominant on the surface of the catalyst and so was lattice oxygen which was conducive to Lewis acid sites. NH3-TPD test results demonstrated that Lewis acid sites are predominant on the surface of catalyst. The presence of SO2 reduced the catalyst activity. The realized conversion dramatically decreased to 47% from nearly 100% after 8 h. Characterization of fresh and spent catalysts indicated the deterioration of active component and deposition of NH4HSO4 or (NH4)2SO4 contribute to SO2 poisoning.

A stable mesoporous multilamellar silica vesicle (MSV) was developed with a gallery pore size of about 14.0 nm. A simulative enzyme, hemoglobin (Hb), was immobilized on this newly developed MSV and a conventional mesoporous silica material SBA-15. The structures and the immobilization of Hb on the mesoporous supports were characterized with x-ray diffraction, transmission electron microscopy, N2 adsorption-desorption isotherms, Fourier transform infrared, ultraviolet-visible spectroscopy, and so forth. MSV is a promising support for immobilizing Hb due to its large pore size and high Hb immobilization capacity (up to 522 mg/g) compared to SBA-15 (236 mg/g). Less than 5% Hb was leached from Hb/MSV at pH 6.0. The activity study indicated that the immobilized Hb retained most peroxidase activity compared to free Hb. Thermal stability of the immobilized Hb was improved by the proctetive environment of MSV and SBA-15. Such an Hb-mesoporous support with high Hb immobilization capacity, high activity, and enhanced thermal stability will be attractive for practical applications.