Testing shows that many of the present commercially available bentonite products used for clay liner/soil sealant applications may be susceptible to chemical degradation by certain contaminants. Testing also confirms that a recently developed contaminant resistant clay (CRC) is resistant to various contaminants that would otherwise attack and degrade the present commercially available products. The tests that were used to determine its effectiveness were American Petroleum Institute (API) fluid loss, rigid wall hydraulic conductivity, flexible wall hydraulic conductivity and a newly developed top loading filter press (TLFP) test (LSK method).

Sets of replicate hydraulic conductivity tests were conducted using 100 mM KCl and 20 and 40 mM CaCl2 solutions to evaluate how changes in hydraulic conductivity are related to changes in the exchange complex and physical properties (water content and free swell) of prehydrated and non-prehydrated bentonite used for geosynthetic clay liners (GCLs). Essentially no change in hydraulic conductivity and water content (or void ratio) occurred during tests with the 100 mM KCl solution even though K+ was replacing Na+ on the exchange complex. In contrast, for the CaCl2 solutions (20 mM and 40 mM), the hydraulic conductivity increased and the free swell and water content decreased as exchange of Ca2+ for Na+ occurred. Faster changes in hydraulic conductivity and the exchange complex occurred in the tests with the 40 mM CaCl2 solution and the non-prehydrated bentonite (i.e. the hydraulic conductivity changed more rapidly when exchange occurred more rapidly). Even though exchange of Ca2+ for Na+ was essentially complete at the end of testing, the hydraulic conductivity obtained with the 20 mM CaCl2 solution was less and the water content greater than obtained with the 40 mM CaCl2 solution (2.6 × 10−8 cm/s vs. 6.7 × 10−8 cm/s, 122% vs. 111%, and 3.2 vs. 2.9). Similarly, the prehydrated bentonite had lower hydraulic conductivity (1.9 × 10−8 cm/s vs. 6.7 × 10−8 cm/s) and greater water content (167% vs. 111%) than the non-prehydrated bentonite at the end of testing, even though Ca-for-Na exchange was essentially complete.