GaN and AlN Layers Grown by Nano Epitaxial Lateral Overgrowth Technique on Porous Substrates
Published online by Cambridge University Press: 03 September 2012
Abstract
Defect density and stress reduction in heteroepitaxial GaN and AlN materials is one of the main issues in group III nitride technology. Recently, significant progress in defect density reduction in GaN layers has been achieved using lateral overgrowth technique. In this paper, we describe a novel technique based on nano-scale epitaxial lateral overgrowth.
GaN layers were overgrown by hydride vapour phase epitaxy (HVPE) on porous GaN. Porous GaN was formed by anodization of GaN layers grown previously on SiC ŝubstrates. Pore's size was in nano-scale range.
Thickness of overgrown layers ranged from 2 to 120 microns. It was shown that GaN layers overgrown on porous GaN have good surface morphology and high crystalline quality. The surface of overgrown GaN material was uniform and flat without any traces of porous structure. Raman spectroscopy measurements indicated that the stress in the layers grown on porous GaN was reduced down to 0.1 - 0.2 GPa, while the stress in the layers grown directly on 6H-SiC substrates remains at its usual level of about 1.3 GPa.
Preliminary experiments were done on HVPE growth of AlN layer on porous substrates. Improvement of surface morphology and crack density reduction has been observed.
- Type
- Research Article
- Information
- Copyright
- Copyright © Materials Research Society 1999
References
1
Fini, P., Marchand, H., Ibbetson, J.P., Moran, B., Zhao, L., DenBaars, S.P., Speck, J.s., Mishra, U.K., Mat. Res. Soc. Proc.
572, 315–320 (1999).Google Scholar
2
Zheleva, T.S., Smith, S.A., Thomson, D.B., Gehrke, T., Linthicum, K.J., Rajagopal, P., Carlson, E., Ashmawi, W.M., and Davis, R.F., Mat. Res. Soc. Proc.
537, G3.38 (1999).Google Scholar
3
Mynbaeva, M., Titkov, A., Kryzhanovski, A., Kotousova, I., Zubrilov, A.S., Ratnikov, V.V., Davydov, V.Yu., Kuznetsov, N.I., Mynbaev, K., Tsvetkov, D.V., Stepanov, S., Cherenkov, A., Dmitriev, V.A., Internet J. of Nitride Semicond. Research, 4, 14 (1999).Google Scholar
5
Purser, D., Jenkins, M., Lieu, D., Vaccaro, F., Faik, A., Hasan, M.A., Leamy, H.J., Carlin, C., Sardela, M.R. Jr., Zhao, Q., Willander, M., and Karlsteen, M., International Conference on Silicon Carbide and Related Materials 1999, Abstracts, 462 (1999).Google Scholar
7
Mynbaeva, M., Savkina, N., Tregubova, A., Scheglov, M., Lebedev, A., Zubrilov, A., Titkov, A., Kryganovski, A., Mynbaev, K., Seredova, N., Tsvetkov, D., Stepanov, S., Cherenkov, A., Kotousova, I., Dmitriev, V., to be published in the Proceedings of the Int. Conf. on Silicon Carbide and Related Materials, October 10-15, 1999, NC.Google Scholar
8
Kuznetsov, N.I., Nikolaev, A.E., Zubrilov, A.S., Melnik, Yu.V., Dmitriev, V.A., Appl. Phys. Lett.
75, 3138–3140 (1999).Google Scholar
10
Melnik, Yu.V., Nikolaev, A.E., Stepanov, S., Nikitina, I.P., Vassilevski, K., Ankudinov, A., Musikhin, Yu. and Dmitriev, V.A., Materials Science Forum, 264–268, 1121 (1998).Google Scholar