Electrical properties of the La0.8Sr0.2MnO3 thin films on SrTiO3 substrate by an excimer laser metal organic deposition (ELMOD) process at low temperature
Published online by Cambridge University Press: 17 March 2011
Abstract
The electrical properties of epitaxial La0.8Sr0.2MnO3 films on a SrTiO3(STO) substrate prepared by changing the laser fluence, the irradiation time and the film thickness using excimer laser metal organic deposition(ELMOD) at 500/cm2, the film showed a 3.9 % maximum temperature coefficient of resistance (TCR: defined as 1/R•dR/dT) which was obtained by the ArF laser irradiation at 80mJ/cm2 for 10min. At a constant fluence of 80mJ/cm2, the Tm (temperature of the maximum TCR) of the La0.8Sr0.2MnO3 films increased from 225K to near 250K with an increase in the irradiation time to 90min at which the TCR was almost 3.9%. The La0.8Sr0.2MnO3 film that showed the maximum TCR of 4.0% at 275K was obtained by the ELMOD process at 500°C using the optimum conditions (Flence:80mJ/cm2, Irradiation time: 90min, Film thickness: 80nm).
- Type
- Research Article
- Information
- Copyright
- Copyright © Materials Research Society 2004
References
REFERENCES
- 6
- Cited by