Laser Transformed SiC Thin Films

Published online by Cambridge University Press:  21 February 2011

K. G. Kreider
Affiliation:
National Institute of Standards and Technology Gaithersburg, MD 20899
D. R. F. Burgess Jr
Affiliation:
National Institute of Standards and Technology Gaithersburg, MD 20899
M. J. Tarlov
Affiliation:
National Institute of Standards and Technology Gaithersburg, MD 20899
G. Gillen
Affiliation:
National Institute of Standards and Technology Gaithersburg, MD 20899
S. Wight
Affiliation:
National Institute of Standards and Technology Gaithersburg, MD 20899
R. Lareau
Affiliation:
EPS-Army Research Laboratory Ft. Monmouth, NJ 07703
L. M. Casas
Affiliation:
EPS-Army Research Laboratory Ft. Monmouth, NJ 07703
Get access

Abstract

Silicon carbide has excellent physical and electronic properties for use in devices when higher temperatures or higher power densities are required. We have investigated a direct laser conversion technique to create electrical conductors on the high band-gap silicon carbide. Thin films of silicon carbide (SiC) were sputter deposited on AI2O3, SiO2, and Si substrates using a SiC target with an RF planar magnetron. These films were irradiated at 308 nm with multiple 15 ns excimer laser pulses creating 0.5 to 2 mm wide electrically conducting paths. Both the irradiated and unirradiated films were evaluated as a function of substrate type, deposition temperature, finish, stoichiomelry, annealing temperature, sputter gas, film thickness, and laser processing conditions. The lowest resistivity films, originally 10 ohm-m, were calculated to be 160 μohm-m obtained after irradiation, which compares to a value of 50 μohm-m obtained after irradiating bulk SiC. The films were characterized using XPS, SIMS, AES, SEM, and Raman spectroscopy. We were able to characterize the composition of the films and conducting traces, the surface oxide, the critical binding energies, the lattice structure, and the morphology of the microstructure. Models for the phase transformations and conductivity have been formulated.

Type
Research Article
Copyright
Copyright © Materials Research Society 1994

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Wasa, K., Nagai, T., and Hayakawa, S., Thin Solid Films 31, 235 (1976)Google Scholar
2. Wasa, K., Tohda, T., and Hayakawa, S., Rev. Sci. Inst. 50, 10834 (1979)Google Scholar
3. Tohda, T., Wasa, K., and Hayakawa, S., J. Electrochem Soc. 127, 44 (1980).Google Scholar
4. Seeward, K.L., Barbee, T.W., and Tiller, W.A., J. Vac. Sci. Tech. A4, 31 (1986)Google Scholar
5. Suzaki, Y., Inoue, S., Hasegawa, I., Yoshii, K., and Kawabe, H., Thin Solid Films 173, 235 (1989).Google Scholar
6. Quick, N.R. and Matson, R.J. in Proceedings of the International Symposium on Microelectronics '91, Duarte, F.J. and Harris, D.G. (ed), STS Press, McLean, 1992, p 545.Google Scholar
7. Quick, N.R., U.S. Patent No. 5,145,741, 8 Sep. 1992 Google Scholar
8. Binary Allo Phase Diagrams, ed. Massalski, T.B., American Society from Metals, Cleveland, OH, 1986, p. 589.Google Scholar
9. Adar, F., Microchem. J. 38, 50 (1988).Google Scholar
10. Tuinstra, F. and Koenig, J.L., J. Chem. Phys. 53, 1126 (1970)Google Scholar
11. Gerault, J., Morancho, R., Constant, G. and Alnot, M., Thin Solid Films 101, (1983)Google Scholar