Scanning electron microscopy operated at cryogenic temperature (cryo-SEM) is a powerful tool for investigating surface and cross-sectional nanostructures of water-containing samples. Typically, cryo-SEM samples are frozen just before observation in specific metal carriers. However, pre-frozen samples are also of interest, such as frozen food and freeze-stored animal samples. In such cases, sample mounting with a defined orientation is required, but there has been a lack of ideal conductive adhesives that can be used without increasing the sample temperature. Here, we developed a mixture of graphite oxide and 1,3-butanediol as an adhesive, capable of gluing samples at dry-ice temperature and is frozen below that temperature. Dispersion of graphite oxide increased the conductivity and reduced the charge-up contrast. Acquisition of energy-dispersive X-ray spectrum, cross-sectional ion milling, and high-resolution imaging were successfully achieved using the adhesive. We tested and confirmed the usefulness of this new adhesive by applying it to cryo-SEM surface imaging of diatomite, freeze-fractured cross-sectional imaging of chicken liver, and ion milling cross-sectional imaging of a deep-sea snail. The new adhesive is not only useful for food science and field-preserved biological samples but also potentially applicable to wider fields such as archaeological and biological samples preserved under permafrost.

Graphite oxide (GO) is generated by treating graphite with strong oxidizers. GO retains the structure of graphite, but does so with a larger and irregular basal plane spacing. The oxidation of graphite results in the formation of epoxide groups, as well as C–OH and COOH groups. It is the presence of some of these moieties that allows GO to be dispersed in water, allowing for its use in waterborne formulations. Although GO does not possess the electrical properties of single-sheet graphene, it can be swelled in water, which allows for intercalation of hydrophilic polymer between GO sheets, resulting in a composite that can be coated to produce a continuous film. After coating it may be possible to chemically convert GO to a reduced graphite oxide (r-GO) with improved electrical conductivity. X-ray diffraction (XRD) is ideally suited to evaluate GO–polymer composite samples for evidence of intercalation or exfoliation of GO. Examples of GO–polymer analysis by XRD are presented, along with results that demonstrate the effect of relative humidity (RH) on neat GO. Knowing the ambient RH during XRD data collection was found to be important to correctly assess the extent of polymer intercalation within the GO lattice.